Tailoring magnetic properties of electrodeposited thin films of the molecule-based magnet Cr5.5(CN)12 11.5H2O

  • Helena Prima-Garcia1Email author,

    Affiliated with

    • Eugenio Coronado1,

      Affiliated with

      • Juan P Prieto-Ruiz1 and

        Affiliated with

        • Francisco M Romero1

          Affiliated with

          Nanoscale Research Letters20127:232

          DOI: 10.1186/1556-276X-7-232

          Received: 9 January 2012

          Accepted: 24 April 2012

          Published: 24 April 2012


          This paper reports on molecular-based magnetic thin films of Prussian blue analogues (PBA) with high critical temperatures composed of mixed-valence chromium cyanides. The thin films of PBA were synthesized by means of electrodeposition technique. Morphology and magnetic study are presented in a function of electrochemical deposition conditions. We present the electrochemical methods as a promising and effective tool for preparing molecular-based magnetic thin films of Prussian blue analogue.


          Magnetic materials Thin films Molecule-based magnet Prussian blue MOKE


          The family of Prussian blue analogues (PBA) of general formula CcAa[B(CN)6]b·nH2O (C, alkali cation; A and B, transition metal ions) are molecule-based materials with interesting magnetic properties.

          Electrochemical methods have been extensively used to fabricate high-quality films of molecule-based materials with interest in molecular spintronics such as PBAs [13].

          Electrodeposition is considered as a real alternative to physical deposition techniques, such as evaporation, sputtering, and molecular beam epitaxy, in order to provide a simple and cost-effective technology for the preparation of high-quality films and multilayers [4, 5]. Electrochemical methods are intrinsically fast and compatible with patterning and large-scale production [6] with the possibility of working in wet non-vacuum conditions.

          In this way, electrodeposition is presented as one of the simplest and cheapest processes available for the fabrication of thin films [7] being of great interest in possible industrial applications.

          In this work, we report on the fabrication and characterization of Prussian blue analogue thin films obtained by electrodeposition, showing this technique as a promising and effective tool for preparing high-quality thin films of this molecule-based magnet with great perspectives in the field of molecular spintronics.


          Preparation of the films

          All reagents were purchased from Sigma-Aldrich (St. Louis, MO, USA) and used without further purification. The electrochemical synthesis of the PBA Cr3.5II[CrIII(CN)6[CrII(CN)6·11.5H2O has been described in previous works [8]. An aqueous solution containing K3[Cr(CN)6 (5 mmol) and CrCl3 (7.5 mmol) was reduced at a fixed potential (E = −0.88 V vs Ag/AgCl reference electrode) on a substrate of Mylar or glass (dimension 5 × 10 mm) coated with an evaporated Au layer of 100-nm thickness. This substrate was used as the working electrode. A Metrohm Autolab potentiostat (Kanaalweg, Utrecht, The Netherlands) in coulometry mode was employed for depositing the transparent films with a Pt wire as a counter electrode. After preparation, films were rinsed with deionized water and dried at room temperature. Films of different thicknesses were obtained by varying the time of deposition. The thicknesses were determined using an Ambios Technology XP-1 profilometer (Milpitas, CA, USA) placed on a vibration isolation table.

          AFM -study

          A Nanoscope Multimode (Veeco Instruments Inc., Plainview, NY, USA) atomic force microscopy in tapping mode operation was used in the morphological study of the electrodeposited films. Root mean square (RMS) roughness and average particle size were determined using WSx4.0 Develop 13.0 software [9], developed by Nanotec Electronics S.L. (Tres Cantos, Madrid, Spain).

          MOKE measurements

          The magneto-optical characterization was performed with a self-made Kerr magnetometer. A He-Ne laser with a wavelength of 633 nm and an output power of 12 mW was used as the light source producing a nearly linearly-polarized light beam. This beam was passed through a Glan-Laser calcite polarizer (Karl Lambrecht Corporation, Chicago, IL, USA) with an extinction coefficient of 10−5, which allows working with both s-polarized (electric field perpendicular to the plane of incidence) and p-polarized (electric field parallel to the plane of incidence) configurations. The design of the electromagnets and the cryostat allows the use of longitudinal, polar, and transverse geometries. The external magnetic field range in the polar configuration is ±150 mT.

          Results and discussion

          By reducing [Cr(H2O)63+ at a fixed potential of E = −0.88 V in an aqueous solution containing [Cr(CN)63− anions, it was possible to obtain thin films of Crx(CN)6·zH2O [10] (1). Thus, an electroactive transparent film is formed in situ by a reaction of the [Cr(H2O)62+ species with the hexacyanometalate anion on the surface electrode resulting in the formation of the insoluble PBA. By changing the electrodeposition time in coulometry, it was possible to tune the thickness of the electrodeposited films. The relationship between the time of deposition and the film thickness was found to be nearly linear (Table 1). The use of this electrochemical method allowed us to fabricate films with thicknesses ranging from 1,500 nm for 100 s deposition time to 40 nm for films with a deposition time of 1 s.
          Table 1

          Morphological parameters of different thin films of 1

          Time of deposition (s)

          Thickness (nm)

          Average particle size (nm)

          RMS roughness (nm)

          Coercive fielda(mT)


          1,500 ± 100

          600 ± 100


          32 ± 5


          450 ± 30

          320 ± 80


          49 ± 5


          250 ± 10

          180 ± 30


          76 ± 5


          80 ± 10

          170 ± 40


          85 ± 5


          50 ± 10

          120 ± 20


          33 ± 5


          40 ± 10

          90 ± 20


          10 ± 5

          a At 190 K.

          Optical absorption spectra of the electrodeposited films of 1 [11] and attenuated total reflectance infrared spectra (ATR-IR) have been studied somewhere else. The ATR-IR spectra showed for all the different thicknesses a principal band located at 2,186 cm−1 corresponding to the cyanide stretching vibration of the [CrIII(CN)63− anion in concordance with the previous results [10]. The IR frequency associated with this specie is independent of the film thickness [11], indicating that the composition of the film is unaltered as the thickness is decreased.

          In order to characterize the morphology of the films of 1, an atomic force microscopy (AFM) study was performed (Figure 1). In this case, only the images corresponding to the thinner films obtained so far are showed. The images were acquired in tapping mode, with a 5 × 5-μm scan sizes for films with different deposition times. For the thicker films, it is possible to distinguish a polycrystalline structure composed of pyramidal particles of different sizes [11]. This type of morphology has been observed in the epitaxial electrodeposition of Prussian blue on Au(110) surface [12]. For the thinner films, the average particle size (Table 1) increases from a value of 90 nm (lateral size) for the film prepared after 1-s electrodeposition (40-nm thickness) to a value of 170 nm for the film of 80 nm. During the initial (nucleation) stages of the electrodeposition process, the reaction takes place at the naked surface of the electrode, and its kinetics is only limited by diffusion of the species, resulting in very small particles that cover homogenously the electrode surface. At longer deposition times, the intensity of the electrochemical current decreases, indicating a slower kinetics that results in the growth of the particles as pyramidal microcrystals as has been studied at thicker films of sample (1) [11]. The roughness of the film surface shows a slight increase with the deposition time, passing from a value of 8 nm for the 40-nm thickness film to a value of 10 nm for the 80-nm thickness film.
          Figure 1

          AFM topography images. Surface of thin films of 1 obtained after different times of electrodeposition: (a) 10 s (80-nm thickness), (b) 2 s (50-nm thickness), and (c) 1 s (40-nm thickness).

          The magnetic properties of the films at different thickness have been studied somewhere else [11] exhibiting negligible changes on the magnetic properties when changing the film thickness.

          Magneto-optical Kerr effect (MOKE) measurements were performed in order to probe directly the magnetic properties of the different thin films described in Table 1. A source of linearly polarized light of high wavelength (λ = 633 nm) and low power (12 mW) was used in order to prevent any photomagnetic effect. The Kerr rotation (θk) of the films, directly proportional in a first approximation to the magnetization of the samples, was recorded as a function of the applied magnetic field for different temperatures. The first striking result from the MOKE study is that a relatively large hysteresis loops appeared just below Tc for all the films measured in polar configuration (magnetic field perpendicular to the surface sample). The difference between MOKE and other magnetometer like superconducting quantum interference device (SQUID) is probably due to the local surface character of the MOKE technique, which is more sensitive to subtle variations in the morphology of the sample. Also, it has to be considered that the MOKE signal at a given energy of the incident light depends on the joint magneto-optical density of states.

          The magneto-optical response at 190 K of the thinner films of 1 with thicknesses ranging from 80 to 40 nm is depicted in Figure 2. In contrast with the SQUID measurements, where it was found to be independent of the film thickness, here, the coercive field suffers an important change in value when decreasing the film thickness (Table 1). This tendency has been studied [11]. In Figure 3, the coercive field is showed as a function of the mean grain size. When the particle size is reduced, the coercive field increases, passing through a maximum and then decreasing again. The magnetization reversal process for the particles composing the film is different in each region of the curve in Figure 3. The thicker films with a bigger grain size consist of relatively large multi-domain magnetic particles, whereas in the thinner films, the particles approach the single-domain limit, resulting in an increase in coercivity. Such a particle-size effect has been previously described in other molecule-based materials [1315].
          Figure 2

          Normalized MOKE hysteresis loops. Obtained in polar configuration for three thin films of 1 of various thicknesses.

          Figure 3

          Coercive field. As a function of the average grain size of thin films of 1 shown in Table 1.

          In consequence, there is an increase in coercive field with the reduction of the grain size until this value reaches a maximum, in our case 85 mT for a grain size of 170 nm; underneath this value, the physical processes associated to the magnetization reversal in smaller grains produce a reduction in coercive field.


          In summary, it has been demonstrated in this work that it is possible to tune the thickness of electrodeposited films of Prussian blue analogues by changing the electrodeposition time. Therefore, it is possible to reach the nanometer scale in thin films of PBA by reducing the electrodeposition time to few seconds. Thus, the morphology of the films of PBA is also modified varying the thickness of the film by a change in the average grain size. These thinner films possess a smoother surface consisting in homogeneous particles of smaller size. Interestingly, as the thickness of the film is reduced, its magnetic properties are considerably improved (higher coercivity and squareness of the hysteresis loops) until a limit is reached beneath this limit; the coercivity is reduced surely until the superparamagnetic limit.

          Consequently, the utility of electrochemical methods has been also demonstrated in order to obtain in a simple, fast, and reproducible way high-quality thin films of PBA which are molecule-based magnets with very interesting magnetic properties and possible applications in molecular spintronic.

          In view of the versatility of these materials, which include the easy tuning of the magnetic (nature of the magnetic ordering, anisotropy, coercivity, and critical temperature) and electronic (redox potential, energy gap) properties by simply varying the nature of the metal centers, future work will focus on the fabrication and MOKE characterization of PBA-based magnetic multilayers to study proximity effects as well as on the use of these films as spin injector of all-molecular spin valves.



          Financial support from the European Union (Projects HINTS FP7-263104-2 and SpinMol Advanced Grant ERC-2009-AdG-20090325), the Secretaria de Estado de Investigación, Desarrollo e Innovación (Projects with FEDER cofinancing MAT2007-61584, Consolider-Ingenio in Molecular Nanoscience CSD2007-00010, and MATMOLSPIN, MAT201122785), and Generalitat Valenciana (PROMETEO program) is gratefully acknowledged.

          Authors’ Affiliations

          Instituto de Ciencia Molecular, Universidad de Valencia


          1. Ohkoshi S, Fujishima A, Hashimoto K: Transparent and colored magnetic thin films: (FeIIxCrII1-x)1.5[CrIII(CN)6]. J Am Chem Soc 1998, 120: 5349. 10.1021/ja980732fView Article
          2. Sato O, Iyoda T, Fujishima A, Hashimoto K: Electrochemically tunable magnetic phase transition in a high-Tc chromium cyanide thin film. Science 1996, 271: 49. 10.1126/science.271.5245.49View Article
          3. Ohkoshi S, Einaga Y, Fujishima A, Hashimoto K: Magnetic properties and optical control of electrochemically prepared iron–chromium polycyanides. J of Electroanalytical Chemistry 1999, 473: 245–249. 10.1016/S0022-0728(99)00173-4View Article
          4. Bakonyi I, Péter L: Electrodeposited multilayer films with giant magnetoresistance (GMR): progress and problems. Prog Mater Sci 2010, 55: 107. 10.1016/j.pmatsci.2009.07.001View Article
          5. Ross CA: Electrodeposited multilayered thin films. Ann Rev Mater Science 1994, 24: 159. 10.1146/annurev.ms.24.080194.001111View Article
          6. Yang FY, Liu K, Hong K, Reich DH, Searson PC, Chien CL: Large magnetoresistance of electrodeposited single crystal bismuth thin films. Science 1999, 284: 1335. 10.1126/science.284.5418.1335View Article
          7. Shwarzer W, Lashmore DS: Giant magnetoresistance in electrodeposited films. IEEE Transactions On Magnetics 1996, 32(Is 4):3133.
          8. Sato O, Iyoda T, Fujishima A, Hashimoto K: Photoinduced magnetization of a cobalt-iron cyanide. Science 1996, 271: 49. 10.1126/science.271.5245.49View Article
          9. Horcas I, Fernández R, Gómez-Rodríguez JM, Colchero J, Gómez-Herrero J, Baró AM: WSXM: a software for scanning probe microscopy and a tool for nanotechnology. Rev Sci Instrum 2007, 78: 013705. 10.1063/1.2432410View Article
          10. Buschmann WE, Paulson SC, Wynn CM, Girtu MA, Epstein AJ, White HS, Miller JS: Reversed (negative) magnetization for electrochemically deposited high-Tc thin films of chromium hexacyanide magnets. Chem Mater 1998, 10: 1386–1395. 10.1021/cm970773vView Article
          11. Coronado E, Makarewicz M, Prieto-Ruiz JP, Prima-Garcia H, Romero FM: Magneto-optical properties of electrodeposited thin films of the molecule-based magnet Cr5.5(CN)12·11.5 H2O. Adv Mater 2011, 23: 4323–4326. 10.1002/adma.201101513View Article
          12. Nakanishi S, Lu G, Kothari HM, Bohannan EW, Switzer JA: Epitaxial electrodeposition of prussian blue thin films on single-crystal Au(110). J Am Chem Soc 2003, 125: 14998. 10.1021/ja0381151View Article
          13. Kurmoo M, Kepert CJ: Magnetic materials containing the dicyanamide anion, {N(Cn)2}−. Mol Cryst Liq Cryst 1999, 334: 693–702. 10.1080/10587259908023362View Article
          14. Vopsauroiu M, Georgieva M, Vallejo Fernandez G, Manzoor S, Thwaites MJ, OGrady K: Preparation of high moment CoFe films with controlled grain size and coercivity. J Applied Phys 2005, 97: 10N303. 10.1063/1.1855276
          15. Prado Y, Lisnard L, Heurtaux D, Rogez G, Stephan O, Dia N, Riviere E, Catala L, Mallah T: Tailored coordination nanoparticles: assessing the magnetic single-domain critical size. Chem Commun 2011, 47: 1051–1053. 10.1039/c0cc03382kView Article


          © Prima-Garcia et al.; licensee Springer. 2012

          This article is published under license to BioMed Central Ltd. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://​creativecommons.​org/​licenses/​by/​2.​0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.