From: Self-organised synthesis of Rh nanostructures with tunable chemical reactivity

Figure 6

Out-of-phase diffraction maps (S z = 1.88) after ion irradiation of Cu(110). (a), (b), (c) Temperature dependence after dosing at ɛ = 400 eV, f = 1.5 ML/min for a total fluence of 21 ML. (d), (e), (f) Flux dependence after dosing at ɛ = 400 eV and T = 230 K for a total fluence of 21 ML. (g), (h), (i) Energy dependence for irradiation at the flux f = 1 ML/min and at T = 230 K for a total fluence of 45 ML. The figure is reproduced from Ref. [17]