Table 1 Characteristics of different samples used for investigation during milling
From: High-yield Synthesis of Multiwalled Carbon Nanotube by Mechanothermal Method
Milling time (h) | Sample (Id) | SA (m2/g) | Crystalline size = D(nm) |
---|---|---|---|
0 | C0 | 5.5 | 31.1 |
5 | C5 | 21.2 | 30.1 |
10 | C10 | 25.8 | 29.8 |
20 | C20 | 31.5 | 29.1 |
30 | C30 | 35.1 | 27.4 |
40 | C40 | 39.9 | 26.2 |
50 | C50 | 45.6 | 25.4 |
60 | C60 | 50.1 | 24.6 |
70 | C70 | 56.1 | 23.9 |
80 | C80 | 62.5 | 22.1 |
90 | C90 | 70.2 | 20.1 |
100 | C100 | 78.9 | 18.5 |
110 | C110 | 91.1 | 17.1 |
120 | C120 | 115.2 | 13.9 |
130 | C130 | 145.2 | 11.2 |
140 | C140 | 175.5 | 8.5 |
150 | C150 | 200.5 | 5.2 |
160 | C160 | 205.5 | 4.9 |
170 | C170 | 207.4 | 4.8 |
180 | C180 | 209.1 | 4.7 |
190 | C190 | 209.5 | 4.8 |
200 | C200 | 211.2 | 4.8 |
210 | C210 | 211.2 | 4.8 |
220 | C220 | 211.2 | 4.8 |