Table 2 Tensile properties of EVA grades and their nanocomposites at 4 wt% filler loading

From: Influence of Matrix Polarity on the Properties of Ethylene Vinyl Acetate–Carbon Nanofiller Nanocomposites

Sample Tensile strength (MPa) Elongation at break (%) Modulus at 100% elongation (MPa)
EVA40 8.36 ± 0.19 495 ± 15 1.31 ± 0.12
EVA50 5.35 ± 0.12 440 ± 10 0.74 ± 0.11
EVA60 5.24 ± 0.20 430 ± 10 0.57 ± 0.05
EVA70 5.04 ± 0.17 410 ± 14 0.48 ± 0.07
EVA40-4EG 9.32 ± 0.18 525 ± 12 2.39 ± 0.15
EVA50-4EG 7.21 ± 0.14 435 ± 16 1.94 ± 0.08
EVA60-4EG 7.51 ± 0.10 420 ± 10 2.05 ± 0.06
EVA70-4EG 7.98 ± 0.15 410 ± 15 2.29 ± 0.12
EVA40-4T 8.95 ± 0.18 470 ± 15 2.56 ± 0.13
EVA50-4T 6.60 ± 0.12 370 ± 15 2.40 ± 0.09
EVA60-4T 6.68 ± 0.18 370 ± 16 2.42 ± 0.10
EVA70-4T 6.75 ± 0.20 375 ± 15 2.46 ± 0.10
EVA40-4F 11.10 ± 0.21 565 ± 20 3.13 ± 0.14
EVA50-4F 11.34 ± 0.12 400 ± 15 3.38 ± 0.11
EVA60-4F 11.45 ± 0.15 375 ± 13 3.65 ± 0.10
EVA70-4F 12.30 ± 0.16 380 ± 15 4.13 ± 0.15