Table 3 ATRP of styrene at 100 °C
Time (h) | M n × 103(g/mol) | PDI | % Weight lossa | Grafting densityb | Initiator efficiency |
---|---|---|---|---|---|
2 | 18 | 2.96 | 64 | 0.48 | 0.18 |
4 | 32 | 2.37 | 73 | 0.41 | 0.16 |
6 | 41 | 2.54 | 82 | 0.55 | 0.21 |
8 | 52 | 2.47 | 91 | 1.01 | 0.39 |
10 | 64 | 1.84 | 94 | 1.26 | 0.49 |