Figure 6From: Effects of Crystalline Anisotropy and Indenter Size on Nanoindentation by Multiscale SimulationVon Mises strain distribution at the indentation depth of a 0.56 nm (at point B in Fig. 5), b 0.86 nm (at point D in Fig. 5), c 1.2 nm (at point F in Fig. 5) and d 1.80 nm (at point H in Fig. 5) for single crystal Ag thin film on (001) surface, where the indenter width is 8dBack to article page