Table 1 Deflection angle between the major diameter of the fitting ellipse and the field direction
From: Transverse electric field–induced deformation of armchair single-walled carbon nanotube
SWCNT samples | EA (V/Å) | Deflection angle (degree) | EB (V/Å) | Deflection angle (degree) |
|---|---|---|---|---|
(5,5)C100H20 | 0.4 | 86.6 | 0.4 | 0.4 |
0.7 | 0.1 | 0.7 | 0.1 | |
1.0 | 0.4 | 1.0 | 0.1 | |
1.4 | 0.2 | 1.4 | 0.3 | |
1.8 | 1.5 | 1.8 | 0.0 | |
(5,5)C150H20 | 0.5 | 8.3 | 0.5 | 4.6 |
1.0 | 2.1 | 1.0 | 7.8 | |
1.4 | 0.6 | 1.4 | 4.8 | |
1.8 | 0.4 | 1.8 | 2.5 | |
2.2 | 1.2 | 2.0 | 1.6 | |
2.6 | 2.3 | |||
2.8 | 2.3 | |||
(5,5)C200H20 | 1.0 | 2.8 | ||
1.5 | 1.5 | |||
2.0 | 7.1 | |||
2.3 | 11.7 | |||
2.6 | 12.0 | |||
(6,6)C120H24 | 0.5 | 0.0 | 0.5 | 0.2 |
0.8 | 0.0 | 0.8 | 0.5 | |
0.9 | 0.1 | 0.9 | 0.5 | |
1.2 | 0.0 | 1.2 | 0.0 | |
1.4 | 0.0 | 1.4 | 0.0 | |
(7,7)C140H28 | 0.3 | 4.9 | 0.4 | 6.9 |
0.5 | 6.1 | 0.7 | 3.2 | |
0.7 | 2.5 | 0.9 | 2.8 | |
0.9 | 2.5 | 1.0 | 2.3 | |
1.0 | 0.6 | |||
(8,8)C160H32 | 0.2 | 0.5 | 0.2 | 0.1 |
0.5 | 1.7 | 0.5 | 0.3 | |
0.6 | 2.7 | 0.6 | 0.7 | |
0.7 | 0.5 | 0.7 | 1.0 | |
0.8 | 0.5 | 0.8 | 0.2 |