Table 2 Comparison of Ω t (t = 2, 4, 6)(×10−20cm2) of Er3+ in some host materials
From: Highly Efficient Near-IR Photoluminescence of Er3+ Immobilized in Mesoporous SBA-15
Host material | Ω 2 | Ω 4 | Ω 6 |
---|---|---|---|
Germanate glass [29] | 5.81 | 0.85 | 0.28 |
Fluorophosphate glass [29] | 2.91 | 1.63 | 1.26 |
Silicate glass [29] | 4.23 | 1.04 | 0.61 |
Aluminate glass [29] | 5.60 | 1.60 | 0.61 |
Fluoride glass [29] | 2.91 | 1.27 | 1.11 |
Phosphate glass [30] | 3.89 | 1.01 | 0.55 |
Tellurite glass [31] | 5.05 | 1.45 | 1.22 |
Bismuth-based glass [32] | 3.86 | 1.52 | 1.17 |
Er(PMS)x-SBA-15 | 1.04 | 2.38 | 1.06 |