CMOS-compatible dense arrays of Ge quantum dots on the Si(001) surface: hut cluster nucleation, atomic structure and array life cycle during UHV MBE growth


We report a direct observation of Ge hut nucleation on Si(001) during UHV molecular beam epitaxy at 360°C. Nuclei of pyramids and wedges were observed on the wetting layer (WL) (M × N) patches starting from the coverage of 5.1 Å and found to have different structures. Atomic models of nuclei of both hut species have been built as well as models of the growing clusters. The growth of huts of each species has been demonstrated to follow generic scenarios. The formation of the second atomic layer of a wedge results in rearrangement of its first layer. Its ridge structure does not repeat the nucleus. A pyramid grows without phase transitions. A structure of its vertex copies the nucleus. Transitions between hut species turned out to be impossible. The wedges contain point defects in the upper corners of the triangular faces and have preferential growth directions along the ridges. The derived structure of the {105} facet follows the paired dimer model. Further growth of hut arrays results in domination of wedges, and the density of pyramids exponentially drops. The second generation of huts arises at coverages > 10 Å; new huts occupy the whole WL at coverages ~14 Å. Nanocrystalline Ge 2D layer begins forming at coverages > 14 Å.


Development of CMOS-compatible processes of formation of germanium quantum dot (QD) dense arrays on the (001) silicon surface as well as multilayer Ge/Si epitaxial heterostructures on their basis is a challenging task of great practical significance [114]. An important direction of applied researches in this area is the development of highly efficient monolithic far and mid infrared detector arrays which could be produced by a standard CMOS technology [914]. Such detectors have to combine high perfection (uniformity, sensitivity, operating life, etc.) with high yield and low production price. A requirement of CMOS compatibility of technological processes imposes a hard constraint on conditions of all the phases of the QD array manufacturing starting from the stage of preparation of a clean Si surface for Ge/Si heterostructure deposition: on the one hand, formation of a photosensitive layer must be one of the latest operations of the whole device production cycle because otherwise the structure with QDs would be destroyed by further high-temperature annealings; on the other hand, high temperature processes during Ge/Si heterostructure formation on the late phase of the detector chip production would certainly wreck the readout circuit formed on the crystal. Therefore, lowering of the array formation temperature down to the values of 450°Ca is strongly required [1, 11], and the Ge QD arrays meeting this requirement are referred to as CMOS-compatible ones.

In addition to the requirement of the low temperature of a Ge QD array formation, both high density of the germanium nanoclusters (> 1011 cm-2) and high uniformity of the cluster shapes and sizes (dispersion < 10%) in the arrays are necessary for employment of such structures in CMOS IR detectors [12]. The molecular beam epitaxy (MBE) is known to be the main technique of formation of Ge/Si heterostructures with QDs [2, 15]. A high density of the self-assembled hut clusters can be obtained in the MBE process of the Ge/Si(001) structure formation when depositing germanium on the Si(001) substrate heated to a temperature T gr 550°C. In this case, the lower the temperature of the silicon substrate during the Ge deposition the higher the density of the clusters at the permanent quantity of the deposited Ge [16, 17]. For example, the density of the Ge clusters in the array was 6 × 1011 cm-2 at T gr = 360°C, and the effective thickness of the deposited germanium layerb h Ge = 8 Å; the cluster density of only ~2 × 1011 cm-2 was obtained at T gr = 530°C and the same value of h Ge[18].

There is another approach for obtaining dense cluster arrays. The authors of Refs. [4, 1921] reached the cluster density of ~9 × 1011 cm-2 using the pulsed irradiation of the substrate by a low-energy Ge+ ion beam during the MBE growth of the Ge/Si(001) heterostructures at T gr as high as 570°C.

Obtaining of the arrays of the densely packed Ge QDs on the Si(001) surface is an important task, but the problem of formation of uniform arrays of the Ge clusters is much more challenging one. The process of Ge/Si(001) heterostructure formation with the Ge QD dense arrays and predetermined electrophysical and photoelectric parameters cannot be developed until both of these tasks are solved. The uniformity of the cluster sizes and shapes in the arrays determines not only the widths of the energy spectra of the charge-carrier bound states in the QD arrays [4], but in a number of cases the optical and electrical properties of both the arrays themselves and the device structures produced on their basis [22]. To find an approach to the improvement of the Ge QD array uniformity on the Si(001) surface, it is necessary to carry out a detailed morphological investigation of them.

This article presents the results of our recent investigations of several important issues of the Ge dense array formation and growth. We have studied the array nucleation phase (the transition from 2D growth of the wetting layer (WL) to 3D formation of the QD array when the nuclei of both species of huts--pyramids and wedges [18]--begin to arise on the (M × N) patches of WL)[23]. We have identified by STM the nuclei of both species, determined their atomic structures [18, 24] and observed the moment of appearance the first generation of the nuclei. We have investigated with high spatial resolution the peculiarities of each species of huts and their growth and derived their atomic structures [24, 25]. We have concluded that the wedge-like huts form because of a phase transition reconstructing the first atomic step of the growing cluster when dimer pairs of its second atomic layer stack up; the pyramids grow without such phase transitions. In addition, we have come to conclusion that wedges contain vacancy-type defects on the penultimate terraces of their triangular facets [24] which may decrease the energy of addition of new atoms to these facets and stimulate the quicker growth on them than on the trapezoidal ones and rapid elongation of wedges. We have shown also comparing the structures and growth of pyramids and wedges that shape transitions between them are very unlikely [24, 25]. Finally, we have explored the array evolution during MBE right up to the end of its life when most of clusters coalesce and start forming a nanocrystalline 2D layer.

In the next sections, we present these results in detail.

Methods, equipment and conditions of experiments

The experiments were made using an integrated ultrahigh vacuum instrument [18] built on the basis of the Riber surface science center with the EVA 32 MBE chamber connected to the STM GPI-300 ultrahigh vacuum scanning tunnelling microscope [2628]. This equipment allows us to carry out the STM study of samples at any phase of a substrate surface preparation and MBE growth. The samples can be transferred into the STM chamber for the examination and moved back into the MBE vessel for further processing as many times as required never leaving the UHV ambient and preserving the required cleanness for STM investigations with atomic resolution and MBE growth.

Initial substrates were 8 × 8 mm2 squares cut from the specially treated commercial B-doped CZ Si(100) wafers (p-type, ρ = 12 Ωcm). After washing and chemical treatment following the standard procedure described elsewhere [29, 30] (which included washing in ethanol, etching in the mixture of HNO3 and HF and rinsing in the deionized water), the silicon substrates were mounted on the molybdenum STM holders and inflexibly clamped with the tantalum fasteners. The STM holders were placed in the holders for MBE made of molybdenum with tantalum inserts. Then, the substrates were loaded into the airlock and transferred into the preliminary annealing chamber where they were outgassed at the temperature of around 565°C and the pressure of about 5 × 10-9 Torr for about 24 h. Eventually, the substrates were moved for final treatment into the MBE chamber evacuated down to about 10-11 Torr. There were two stages of annealing in the process of substrate heating in the MBE chamber--at 600°C for 5 min and at 800°C for 3 min [18]. The final annealing at the temperature greater than 900°C was carried out for nearly 2.5 min with the maximum temperature of about 925°C (1.5 min). Then, the temperature was rapidly lowered to about 750°C. The rate of the further cooling was around 0.4°C/s that corresponded to the 'quenching' mode applied in [30]. The pressure in the MBE chamber grew to nearly 2 × 10-9 Torr during the deoxidization process. The surfaces of the silicon substrates were completely purified of the oxide film as a result of this treatment; more data on the morphology of the prepared Si(001) clean surfaces can be found in Refs. [2931].

Ge was deposited directly on the deoxidized Si(001) surface from the source with the electron beam evaporation.c The Ge deposition rate was about 0.15 Å/s; the effective Ge film thickness h Ge was varied from 4 to 15 Å for different samples. The deposition rate and h Ge were measured using the XTC film thickness monitor equipped with the graduated in-advance quartz sensor installed in the MBE chamber. The substrate temperature T gr was 360°C during Ge deposition; the pressure in the MBE chamber did not exceed 10-9 Torr. The rate of the sample cooling down to the room temperature was approximately 0.4°C/s after the deposition.

The samples were heated by Ta radiators from the rear side in both preliminary annealing and MBE chambers. The temperature was monitored with chromel-alumel and tungsten-rhenium thermocouples in the preliminary annealing and MBE chambers, respectively. The thermocouples were mounted in vacuum near the rear side of the samples and in situ graduated beforehand against the IM-PAC IS 12-Si pyrometer which measured the sample temperature through chamber windows. The atmosphere's composition in the MBE camber was monitored using the SRS RGA-200 residual gas analyser before and during the process.

After Ge deposition and cooling, the prepared samples were moved for analysis into the STM chamber in which the pressure did not exceed 10-10 Torr. The STM tip was ex situ made of the tungsten wire and cleaned by ion bombardment [32] in a special UHV chamber connected to the STM one. The images were obtained in the constant tunnelling current (I t) mode at the room temperature. The STM tip was zero-biased while the sample was positively or negatively biased (U s) when scanned in empty- or filled-states imaging mode.

Original firmware [2628] was used for data acquisition; the STM images were processed afterwards using the WSxM software [33].

Experimental data and structural models

Array and hut cluster nucleation

While investigating an evolution of the hut arrays, we have arrived at a conclusion that a moment of an array nucleation during MBE precedes a moment of formation of the first hut on the WL.d It is not a paradox. Hut cluster arrays nucleate when the first hut nuclei arise on the (M × N) patch of the WL. This process is illustrated in Figure 1. An image (a) demonstrates a typical STM micrograph of the WL with the (M × N)-patched structure (h Ge = 4.4 Å). This image does not demonstrate any feature which might be interpreted as a hut nucleus [24]. Such features first arise at the coverages of ~5 Å: they are clearly seen in the image (b), which demonstrates a moment of the array birth (h Ge = 5.1 Å), and numbered by '1' for the pyramid nucleus, and '2' for the wedge one (several analogous formations can be easily found by the readers on different patches). However, no hut clusters are seen in this picture.

Figure 1
figure 1

STM images of Ge WL on Si(001): (a) before cluster nucleation, h Ge = 4.4 Å (U s = -1.86 V, I t = 100 pA); (b) arising nuclei of pyramidal (1) and wedgelike (2) huts, h Ge = 5.1 Å (U s = +1.73 V, I t = 150 pA).

Our interpretation is based on the results reported in Ref. [24] which evidenced that there are two different types of nuclei on Ge WL, which evolve in the process of Ge deposition to pyramidal and wedge-like hut clusters. Having assumed that nuclei emerge on WL as combinations of dimer pairs and/or longer chains of dimers in epitaxial configuration [34] and correspond to the known structure of apexes specific for each hut species [18, 25], we have investigated WL patches, one monolayer (ML) high formations on them and clusters of different heights (number of steps) over WL. As a result, we succeeded to select two types of formations different in symmetry and satisfying the above requirements, which first appear at a coverage of ~5 Å and then arise on WL during the array growth. We have interpreted them as hut nuclei, despite their sizes being much less than those predicted by the first principle calculations [35], and traced their evolution to huts.

The nuclei formation is illustrated by Figure 2. The surface structure of the (M × N) patches is shown in the micrograph (a). The letter 'c' indicates the c(4 × 2) reconstructed patch, 'p' shows a patch with the p(2 × 2) reconstruction [36, 37]. Both reconstructions are always detected simultaneously, which implies they are very close (or degenerate) by energy. The image (b) shows two adjacent patches reconstructed by the born nuclei: '1' and '2' denote the pyramid (a formation resembling a blossom) and wedge nuclei, respectively [24]. Their structural models derived from many STM images [18, 24, 25] are presented in Figure 3a, b and superimposed on the images of the nuclei in Figure 3c. Note that both types of nuclei arise at the same moment of the MBE growth. It means that they are degenerate by the formation energy. An issue why two different structures, rather than one, arise to relieve the WL strain [18] remains open, however.

Figure 2
figure 2

STM images of Ge WL on Si(001): (a) c(4 × 2) (c) and p(2 × 2) (p) reconstructions within the (M × N) patches, h Ge = 6. 0 Å, U s = +1.80 V, I t = 80 pA; (b) new formations arise on the (M × N) patches due to nucleation of Ge pyramid (1) and wedge (2), h Ge = 6,0 Å, U s = +2.60 V, I t = 80 pA.

Figure 3
figure 3

Models of nuclei of Ge hut clusters corresponding to the images given in Fig. 2b: (a) a pyramid, (b) a wedge [1 is the WL in the plots (a) and (b)]; (c) the models superimposed on the image given in Fig. 2b, the numbering is the same as in Fig. 2b.

It is necessary to remark here that the nuclei are always observed to arise on sufficiently large WL patches. There must be enough room for a nucleus on a single patch. A nucleus cannot be housed on more than one patch. Hence, cluster nucleation is impossible to occur on little (too narrow or short) patches (Figure 2b).

The hut nucleation goes on during the array further evolution. Figure 4 illustrates this process. An array shown in Figure 4a (h Ge = 5.4 Å) consists of 1-ML nuclei ('1' and '2'), 2-ML and 3-ML pyramids and wedges ('3' and '5', '4' and '6' mark pyramids and wedges, respectively).e Figure 4b (h Ge = 6.0 Å) demonstrates the simultaneous presence of nuclei ('1' and '2') and 2 ML huts ('3' and '4') with the growth of much higher clusters.

Figure 4
figure 4

STM images of Ge WL on Si(001): (a) h Ge = 5.4 Å (U s = +1.80 V, I t = 100 pA) and (b) h Ge = 6.0 Å (U s = +2.50 V, I t = 80 pA). Examples of characteristic features are numbered as follows: nuclei of pyramids (1) and wedges (2) [1 ML high over WL], small pyramids (3) and wedges (2) [2 ML high over WL, a Γ-like wedge [18] is observed in the image (a)], 3 ML high pyramids (5) and wedges (6).

Hut cluster nucleation on the WL surface continues until the final phase of the array life. This peculiarity distinguishes low-temperature growth mode from the high-temperature one [18].

Structural models

It is commonly adopted that the hut clusters grow by successively filling the (001) terraces of the {105} faces by the dimer rows [38]. However, formation of the sets of steps and terraces requires the hut base sides to be parallel to the < 100> directions. The pyramid nucleus satisfies this requirement, its sides align with < 100>. Thus, the pyramids grow without phase transition when the second and subsequent layers are added (Figure 5). Only nucleus-like structures of their apexes are rotated 90° with respect to the rows on previous terraces to form the correct epitaxial configuration when the heights are increased by 1 ML, but this rotation does not violate the symmetry of the previous layers of the cluster.

Figure 5
figure 5

Top views of the pyramidal QDs consisting of 2 and 6 monoatomic steps and (001) terraces on the WL: (a) 2 and (b) 6 terraces; 1, 2 and 3 designate WL, the first and the second layers of the clusters, respectively.

A different scenario of growth of the wedge-like clusters has been observed. Two base sides of the wedge nucleus do not align with < 100> (Figure 3b). The ridge structure of a wedge is different from the nucleus structure presented in Figure 3b[18, 24, 25]. It was shown in Ref. [24] that the structure of the wedge-like cluster arises because of rearrangement of rows of the first layer in the process of the second-layer formation (Figure 6a). The phase transition in the first layer generates the base with all sides directed along the < 100> axes which is necessary to give rise to the {105}-faceted cluster. After the transition, the elongation of the elementary structure is possible only along a single axis which is determined by the symmetry (along the arrows in Figure 6a). A formed 2-ML wedge is plotted in Figure 6b. A structure of the 6-ML wedge appearing as a result of further in-height growth is shown in Figure 6c. The ridge structures of the 2-ML and 6-ML wedges are seen to coincide, which is not the case for different cluster heights. A complete set of the wedge ridges for different cluster heights can be obtained by filling the terraces by epi-oriented pairs of dimers.

Figure 6
figure 6

Growth of a wedge-like cluster: (a) reconstruction of the first layer of a forming wedge during addition of epi-oriented dimer pairs of the second (001) terrace; plots of atomic structures of a Ge wedge-shaped hut cluster composed by (b) 2 and (c) 6 monoatomic steps and (001) terraces on the WL (the numbering is the same as in Fig. 5; d marks a defect that has arisen because of one translation uncertainty of the left dimer pair position).

It should be noted also that, according to the proposed model, the wedge-like clusters always contain point defects on the triangular (short) facets. The defects are located in the upper corners of the facets and caused by uncertainty of one translation in the position of a dimer pair which forms the penultimate terrace of the triangular facet (Figure 6). The predicted presence of these defects removes the degeneracy of the facets, and hence, an issue of the pyramid symmetry violation which occurs if the pyramid-to-wedge transition is assumed (this issue was discussed in detail in Ref. [18]). In addition, the vacancy-type defects may decrease the energy of addition of new atoms to the triangular facets and stimulate the quicker growth on them than on the trapezoidal ones and rapid elongation of wedges. These defects are absent on the facets of the pyramidal huts. Their triangular facets are degenerate. Therefore, as it follows from our model, the trapezoidal and triangular facets of the wedge are not degenerate with respect to one another even at the very beginning of cluster growth. The wedges can easily elongate by growing on the triangular facets faster than on trapezoidal ones. Pyramids, having degenerate facets, cannot elongate and can grow only in height outrunning wedges. This explains greater heights of pyramids [18].

Analysing the deduced structural models of pyramids and wedges, as well as their behaviour during the array nucleation and growth, we have concluded that shape transitions between the clusters of different species are prohibited [18, 24, 25].


The presented models allowed us to deduce a structure of the {105} facets (Figure 7a). This model resulting from the above simple crystallographic consideration corresponds to the paired dimers (PD) [39] rather than more recent rebonded step (RS) model [40, 41] which is now believed to be an improvement over the previous PD model proposed by Mo et al.

Figure 7
figure 7

A structure of hut facets: (a) a structural model of the {105} facet of hut clusters derived from the plots given in Figs. 5 and 6 corresponds to the PD (pairs of dimers) model [39], SA and SB are commonly adopted designations of the monoatomic steps [45]: atoms situated on higher terraces are shown by larger circles. (b) The schematic of the facet superimposed on its STM image (4.3 × 4.4 nm, U s = +3.0 V, I t = 100 pA): the [100] direction is parallel to the corresponding base side, the steps rise from the lower right to the upper left corner.

A direct STM exploration of the {105} facets confirms the derived model. Being superposed with the empty-state STM image of the cluster {105} facet, it demonstrates an excellent agreement with the experiment (Figure 7b). A typical STM image of the QD facet is presented in Figure 8. Characteristic distances on the facets are as follows: ~10.5 Å in the < 100> directions (along the corresponding side of the base) and ~14 Å in the normal (< 051>) directions. The facets are composed by structural units which are outlined by ellipses in Figure 8a and can be arranged along either [110] or [] direction on the (001) plane. We have interpreted them as pairs of dimers. Their positional relationship is obviously seen in the 3D micrograph presented in Figure 8b.

Figure 8
figure 8

STM 2D and 3D images of the same area on a Ge hut cluster facet: (a) 2D micrograph and (b) 3D topograph; h Ge = 10Å, T gr = 360°C, U s = +2.1 V, I t = 80 pA. The sides of the cluster base lie along the [100] direction; structural units revealed on the free surfaces of the (001) terraces and interpreted as PD are marked out.

Dangling bonds of the derived {105}-PD facets, due to high chemical activity, may stimulate Ge atom addition and cluster growth. Thus, less stability and higher activity of the {105}-PD facets compared with the Ge(105)/Si(105)-RS plane, which is usually adopted in the literature for simulation of hut {105} facets, may cause fast completion of hut terraces during epitaxy and be responsible (or even be necessary) for hut formation and growth.

Cluster density and fractions

Figure 9a plots the dependence of the cluster density on h Ge for different clusters in the arrays. It is seen that the density of wedges rises starting from D w ≈ 1.8 × 1011 cm-2 at the beginning of the 3D growth of Ge (the estimate is obtained by data extrapolation to h Ge = 5 Å) and reaches the maximum of ~ 5 × 1011 cm-2 at h Ge ~ 8 Å, and the total density of clusters at this point D Σ ~ 6 × 1011 cm-2 is also maximum. Then, both D w and D Σ slowly go down until the 2D growth of Ge starts at h Ge ~ 14 Å and D ΣD w ~ 2 × 1011 cm-2 (the contribution of pyramids from D p to D Σ becomes negligible--about 3 × 1010 cm-2--at this value of h Ge). The pyramid density exponentially drops as the value of h Ge grows (D p ≈ 5 × 1011 exp{2.0 × 107 h Ge}; h Ge is measured in centimetres). The maximum value of D p ≈ 1.8 × 1011 cm-2 obtained from extrapolation to h Ge = 5 Å coincides with the estimated initial value of D w.

Figure 9
figure 9

Density and fractions of the Ge clusters of different species in the arrays formed at T gr = 360°C: (a) number density and (b) fractions; open squares mark the pyramids, black squares designate the wedges, open circles correspond to the total density of huts.

The graphs of cluster fractions in the arrays versus h Ge are presented in Figure 9b. Portions of pyramids and wedges initially very closely similar (~50% at h Ge ~ 5 Å) rapidly become different as h Ge rises. The content of pyramids monotonically falls. The fraction of the wedge-like clusters is approximately 57% at the early stage of the array growth (h Ge = 6 Å) and becomes 82% at h Ge = 8 Å. On further growth of the array, the content of the wedges reaches the saturation at the level of approximately 88% at h Ge = 10 Å.

It may be inferred from this observation that contrary to the intuitively expected from the consideration of symmetry, the wedge-like shape of the clusters is energetically more advantageous than the pyramidal one, and the more the Ge atoms (and the more the number of terraces) constitute the cluster, the more advantageous it is. The probability of nucleation appears to be close to 1/2 for both wedges-like and pyramidal clusters at the initial stage of the array formation and low growth temperatures. Then, as the array grows, the formation of pyramids becomes hardly probable and most of them, which have already formed, vanish, whereas the nucleation and further growth of wedges continue. The Ge pyramids on the Si(001) surface turned out to be less stable objects than the wedges.

Notice also that at T gr = 360°C and the flux of Ge atoms dh Ge / dt = 0.15 Å/s, the point h Ge = 10 Å is particular. Not only the fraction of pyramids saturates at this point but the array overall has the most uniform sizes of the clusters composing it (Figures 4, 10 and 11). We concluded this not only on the basis of analysis of the STM images of the Ge/Si(001) arrays but also from the data of the Raman scattering by the Ge/Si heterostructures with different low-temperature arrays of Ge QDs [42, 43]. We refer to such arrays as optimal.

Figure 10
figure 10

STM 2D and 3D micrographs of Ge hut cluster dense arrays at different coverages ( T gr = 360°C): (a, b) h Ge = 8 Å [(a) 50.6 × 49.9 nm, w is WL, U s = +2.0 V, I t = 80 pA; (b) U s = +2.0 V, I t = 100 pA]; (c, d) h Ge = 10 Å [ U s = +2.1 V, I t = 100 pA].

Figure 11
figure 11

STM topographs of Ge hut cluster dense arrays at different coverages ( T gr = 360°C): (a, b) h Ge = 14 Å [(a) U s = +1.75 V, I t = 80 pA, (b) U s = +3.0 V, I t = 100 pA]; (c, d) h Ge = 15 Å [(c) U s = +2.0 V, I t = 120 pA, (d) 20.3 × 20.4 nm, U s = +3.6 V, I t = 120 pA]; w indicates the WL patches, and i shows a distorted small Ge island 3 ML high over WL.

Array life cycle

A qualitative model accounting for the presence of the particular point at the low-temperature array growth is simple. The case is that at low enough temperatures of the array growth, the new Ge cluster nucleation competes with the process of growth of earlier formed clusters. The height of the dominating wedge-like clusters is observed to be limited by some value depending on T gr.f At small h Ge, Ge clusters are small enough, and the distances between them are large enough compared with the Ge atom (or dimer) diffusion (migration) length on the surface for nucleation of new clusters on the Ge WL in the space between the clusters (Figures 4 and 10a, b). At h Ge = 10 Å and the above dh Ge / dt values, the equilibrium of parameters (cluster sizes and distances between them, diffusion length at given temperature, Ge deposition rate, etc.) sets in, the rate of new cluster nucleation is decreased, and the abundant Ge atoms are mainly spent to the growth of the available clusters (Figure 10c, d). After the clusters reach their height limit and in spite of it, Ge atoms continue to form up their facets. As soon as the most of the clusters reach the height limit, nucleation of new clusters becomes energetically advantageous again, and the nucleation rate rises. The second phase of clusters appears on the WL and fills whole its free surface as h Ge is increased (Figure 11). Further increase of h Ge results in 2D growth mode. It is clear now why the array is the most homogeneous (optimal) at T gr = 360°C and h Ge = 10 Å, whereas the dispersion of the cluster sizes is increased at higher and lower values of h Ge because of the small clusters contained in the array. It is clear also that the optimal array will appear at different values of h Ge when T gr or dh Ge = dt are different.

As it follows from the data presented in this section and the section 'Array and hut cluster nucleation', the Ge hut array evolution and life cycle goes through three main phases: at T gr = 360°C, the array nucleates at h Ge ~ 5 Å (Figure 1), it reaches ripeness and optimum to h Ge ~ 10 Å (Figure 10) and finishes its evolution at h Ge ~ 14 Å by filling the entire surface (Figure 11). Most of the clusters start coalescing (Figure 11b), and 2D growth begins at greater h Ge (Figure 11c).

Nevertheless, free areas of WL still remain even at h Ge = 15 Å (Figure 11d). The structure of the parches ('w') remains the same as in the beginning of the array formation although the WL regions are surrounded by large huts. Small 3D islands ('i'), although very distorted, are still recognizable on WL between the large huts. The hut nucleation on WL goes on even at as high coverages as 15 Å, when virtually total coalescence of the mature huts have already happened.


In summary, we have studied the array nucleation phase and identified the nuclei of both hut species, determined their atomic structure, and observed the moment of appearance of the first generation of the nuclei on WL. We have investigated with high spatial resolution the peculiarities of each species of huts and their growth and derived their atomic structures. We have concluded that the wedge-like huts form due to a phase transition reconstructing the first atomic terrace of the growing cluster when dimer pairs of its second atomic layer stack up; the pyramids grow without phase transitions. In addition, we have concluded that wedges contain vacancy-type defects on the penultimate terraces of their triangular facets which may decrease the energy of addition of new atoms to these facets and stimulate the quicker growth on them than on the trapezoidal ones and rapid elongation of wedges. We have shown also, comparing the structures and growth of pyramids and wedges, that shape transitions between them are impossible. And finally, we have explored the array evolution during MBE right up to the concluding phase of its life when most clusters coalesce and start forming a nanocrystalline 2D layer.



complementary metal-oxide semiconductor




molecular beam epitaxy


ultra-high vacuum


scanning tunneling microscope




quantum dot


wetting layer


pairs of dimers


rebonded step.


  1. Yuryev VA, Arapkina LV, Chapnin VA, Kalinushkin VP, Kiryanova NV, Uvarov OV, Chizh KV, Krylova LA, Stepanov RO, Zaytsev OO: Development of physical and technological basis of the controllable formation of densely packed Ge nanocluster arrays on the silicon (100) surface by means of ultrahigh vacuum molecular beam epitaxy. Report on Research Project 2007–3-1.3–25–01–303 of the Science and Innovations Agency of the Russian Federation, A. M. Prokhorov General Physics Institute of the Russian Academy of Sciences, Moscow, Russia 2007. [State Reg. No. 0220.0 802501 (VNITC)] [State Reg. No. 0220.0 802501 (VNITC)]

    Google Scholar 

  2. Pchelyakov OP, Bolkhovitjanov YB, Dvurechenskiĭ AV, Sokolov LV, Nikiforov AI, Yakimov AI, Voigtländer B: Silicon-germanium nanostructures with quantum dots: Formation mechanisms and electrical properties. Semicond 2000, 34: 1229. 10.1134/1.1325416

    Article  Google Scholar 

  3. Wang KL, Tong S, Kim HJ: Properties and applications of SiGe nanodots. Materials Science in Semiconductor Processing 2005, 8: 389. 10.1016/j.mssp.2004.09.134

    Article  Google Scholar 

  4. Smagina JV, Zinovyev VA, Nenashev AV, Dvurechenskiĭ AV, Armbrister VA, Teys SA: Self-assembly of germanium islands under pulsed irradiation by a low-energy ion beam during heteroepitaxy of Ge/Si(100) structures. JETP 2008, 106: 517. 10.1134/S1063776108030114

    Article  Google Scholar 

  5. Wang KL, Cha D, Liu J, Chen C: Ge/Si self-assembled quantum dots and their optoelectronic device applications. Proc of the IEEE 2007, 95(9):1866. 10.1109/JPROC.2007.900971

    Article  Google Scholar 

  6. Elkurdi M, Boucaud P, Sauvage S, Kermarrec O, Campidelli Y, Bensahel D, Saint-Girons G, Sagnes I: Near-infrared waveguide photodetector with Ge/Si self-assembled quantum dots. Appl Phys Lett 2002, 80(3):509. 10.1063/1.1435063

    Article  Google Scholar 

  7. David S, Kurdi ME, Boucaud P, Kammerer C, Xiang L, Sauvage S, Thanh VL, Sagnes I, Bouchier D, Lourtioz JM: Ge/Si self-assembled islands integrated in 2D photonic crystal microcavities for realisation of silicon-based light-emitting devices. Proc SPIE 2004, 5450: 369. 10.1117/12.546572

    Article  Google Scholar 

  8. Yakimov AI, Dvurechenskii AV, Kirienko VV, Nikiforov AI: Ge/Si quantum-dot metal-oxide-semiconductor field-effect transistor. Appl Phys Lett 2002, 80(25):4783. 10.1063/1.1488688

    Article  Google Scholar 

  9. Liu F, Tong S, Liu J, Wang KL: Normal incident mid-infrared Ge quantum dot photodetector. J Electron Mater 2004, 33(8):846. 10.1007/s11664-004-0210-y

    Article  Google Scholar 

  10. Tong S, Lee JY, Kim HJ, Liu F, Wang KL: Ge dot mid-infrared photodetectors. Optical Materials 2005, 27: 1097. 10.1016/j.optmat.2004.08.065

    Article  Google Scholar 

  11. Yuryev VA, Chapnin VA, Kalinushkin VP, Arapkina LV, Kiryanova NV, Uvarov OV, Chizh KV, Stepanov RO, Krylova LA, Voitsehovsky AV, Nesmelov SN: Development of new quantum dot infrared focal plain array photodetectors for thermographic surveillance systems. Report on "Sabelnik-2" Research Project, A. M. Prokhorov General Physics Institute of the Russian Academy of Sciences, Moscow, Russia 2008. [State Reg. No. 1603925] [State Reg. No. 1603925]

    Google Scholar 

  12. Yakimov AI, Dvurechenskii AV, Nikiforov AI, Proskuryakov YY: Interlevel Ge/Si quantum dot infrared photodetector. J Appl Phys 2001, 89: 5676. 10.1063/1.1346651

    Article  Google Scholar 

  13. Hsu BC, Lin CH, Kuo PS, Chang ST, Chen PS, Liu CW, Lu JH, Kuan CH: Novel MIS Ge-Si quantum-dot infrared photodetectors. IEEE Electron Device Lett 2004, 25(8):544. 10.1109/LED.2004.831969

    Article  Google Scholar 

  14. Tong S, Liu F, Khitun A, Wang KL: Tunable normal incidence Ge quantum dot midinfrared detectors. J Appl Phys 2004, 96: 773. 10.1063/1.1759081

    Article  Google Scholar 

  15. Brunner K: Si/Ge nanostructures. Rep Prog Phys 2002, 65: 27. 10.1088/0034-4885/65/1/202

    Article  Google Scholar 

  16. Yakimov AI, Markov VA, Dvurechenskii AV, Pchelyakov OP: Coulomb staircase in Si/Ge structure. Phil Mag B 1992, 65: 701. 10.1080/13642819208204906

    Article  Google Scholar 

  17. Jin G, Liu JL, Wang KL: Temperature effect on the formation of uniform self-assembled Ge dots. Appl Phys Lett 2003, 83(14):2847. 10.1063/1.1616978

    Article  Google Scholar 

  18. Arapkina LV, Yuryev VA: Classification of Ge hut clusters in arrays formed by molecular beam epitaxy at low temperatures on the Si(001) surface. Phys Usp 2010, 53(3):279. [ArXiv:0907.4770] [ArXiv:0907.4770] 10.3367/UFNe.0180.201003e.0289

    Article  Google Scholar 

  19. Dvurechenskii AV, Zinoviev VA, Smagina JV: Self-organization of an ensemble of Ge nanoclusters upon pulsed irradiation with low-energy ions during heteroepitaxy on Si. JETP Lett 2001, 74: 267. 10.1134/1.1417163

    Article  Google Scholar 

  20. Dvurechenskii AV, Smagina JV, Zinoviev VA, Armbrister VA, Volodin VA, Efremov MD: Elemental composition of nanoclusters formed by pulsed irradiation with low-energy ions during Ge/Si epitaxy. JETP Lett 2004, 79(7):333. 10.1134/1.1765177

    Article  Google Scholar 

  21. Stepina NP, Dvurechenskii AV, Armbrister VA, Smagina JV, Volodin VA, Nenashev AV, Leitão JP, do Carmo MC, Sobolev NA: MBE growth of Ge/Si quantum dots upon low-energy pulsed ion irradiation. Thin Solid Films 2008, 517: 309. 10.1016/j.tsf.2008.08.166

    Article  Google Scholar 

  22. Vescan L, Stoica T, Chretien O, Goryll M, Mateeva E, Muck A: Size distribution and electroluminescence of self-assembled Ge dots. J Appl Phys 2000, 87(10):7275. 10.1063/1.372980

    Article  Google Scholar 

  23. Arapkina LV, Yuryev VA: An initial phase of Ge hut array formation at low temperature on Si(001). arXiv:1102.1305 2011.

    Google Scholar 

  24. Arapkina LV, Yuryev VA: Nucleation of Ge quantum dots on the Si(001) surface. Phys Rev B 2010, 82: 045315. [ArXiv:0907.4665] [ArXiv:0907.4665] 10.1103/PhysRevB.82.045315

    Article  Google Scholar 

  25. Arapkina LV, Yuryev VA: Atomic structure of Ge quantum dots on the Si(001) surface. JETP Lett 2010, 91(6):281. [ArXiv:0908.0883] [ArXiv:0908.0883] 10.1134/S0021364010060056

    Article  Google Scholar 

  26. Ultrahigh vacuum scanning tunneling microscope STM GPI-300[]

  27. Eltsov KN, Klimov AN, Kosyakov AN, Obyedkov OV, Shevlyuga VM, Yurov VY: Ultrahigh vacuum scanning funnelling microscope GPI-300. In Chemical state and atomic structure of fcc metal surfaces in chemical reaction with halogens, Volume 59 of Proceedings of General Physics Institute. Edited by: Konov VI, Eltsov KN. Moscow, Russia: Nauka; 2003:45.

    Google Scholar 

  28. Yurov VY, Klimov AN: Scanning tunneling microscope calibration and reconstruction of real image: Drift and slope elimination. Rev Sci Instrum 1994, 65: 1551. 10.1063/1.1144890

    Article  Google Scholar 

  29. Arapkina LV, Yuryev VA, Shevlyuga VM, Chizh KV: Phase transition between (2 × 1) and c(8 × 8) reconstructions observed on the Si(001) surface around 600°C. JETP Lett 2010, 92(5):310. [ArXiv:1007.0329] [ArXiv:1007.0329] 10.1134/S0021364010170091

    Article  Google Scholar 

  30. Arapkina LV, Yuryev VA, Chizh KV, Shevlyuga VM, Storojevyh MS, Krylova LA: Phase transition on the Si(001) clean surface prepared in UHV MBE chamber: A study by high resolution STM and in situ RHEED. Nanoscale Res Lett 2011, 6: 218. [ArXiv:1009.3909] [ArXiv:1009.3909] 10.1186/1556-276X-6-218

    Article  Google Scholar 

  31. Arapkina LV, Shevlyuga VM, Yuryev VA: Structure and peculiarities of the (8 × n )-type Si(001) surface prepared in a molecular beam epitaxy chamber: A scanning tunneling microscopy study. JETP Lett 2008, 87: 215. [ArXiv:0908.1346] [ArXiv:0908.1346] 10.1134/S0021364008040085

    Article  Google Scholar 

  32. Eltsov KN, Shevlyuga VM, Yurov VY, Kvit AV, Kogan MS: Sharp tungsten tips prepared for STM study of deep nanostructures in UHV. Phys Low-Dim Struct 1996, 9/10: 7.

    Google Scholar 

  33. Horcas I, Fernandez R, Gomez-Rodriguez JM, Colchero J, Gomez-Herrero J, Baro AM: WSxM: A software for scanning probe microscopy and a tool for nanotechnology. Rev Sci Instrum 2007, 78: 013705. 10.1063/1.2432410

    Article  Google Scholar 

  34. Pala RGS, Liu F: Critical epinucleation on reconstructed surfaces and first-principle calculation of homonucleation on Si(001). Phys Rev Lett 2005, 95: 136106. 10.1103/PhysRevLett.95.136106

    Article  Google Scholar 

  35. Lu GH, Liu F: Towards quantitative understanding of formation and stability of Ge hut islands on Si(001). Phys Rev Lett 2005, 94: 176103. 10.1103/PhysRevLett.94.176103

    Article  Google Scholar 

  36. Iwawaki F, Tomitori M, Nishikawa O: STM study of initial stage of Ge epitaxy on Si(001). Ultramicroscopy 1992, 42–44: 902. 10.1016/0304-3991(92)90376-U

    Article  Google Scholar 

  37. Iwawaki F, Kato H, Tomitori M, Nishikawa O: STM study of geometric and electronic structures of Ge dimers on Si(001). Ultramicroscopy 1992, 42–44: 895. 10.1016/0304-3991(92)90375-T

    Article  Google Scholar 

  38. Kästner M, Voigtländer B: Kinetically self-limiting growth of Ge islands on Si(001). Phys Rev Lett 1999, 82(13):2745. 10.1103/PhysRevLett.82.2745

    Article  Google Scholar 

  39. Mo YW, Savage DE, Swartzentruber BS, Lagally MG: Kinetic pathway in Stranski-Krastanov growth of Ge on Si(001). Phys Rev Lett 1990, 65: 1020. 10.1103/PhysRevLett.65.1020

    Article  Google Scholar 

  40. Fujikawa Y, Akiyama K, Nagao T, Sakurai T, Lagally MG, Hashimoto T, Morikawa Y, Terakura K: Origin of the stability of Ge(105) on Si: a new structure model and surface strain relaxation. Phys Rev Lett 2002, 88(13):176101. 10.1103/PhysRevLett.88.176101

    Article  Google Scholar 

  41. Raiteri P, Migas DB, Miglio L, Rastelli A, von Känel H: Critical role of the surface reconstruction in the thermodynamic stability of {105} Ge pyramids on Si(001). Phys Rev Lett 2002, 88(25):256103. 10.1103/PhysRevLett.88.256103

    Article  Google Scholar 

  42. Kucherenko IV, Vinogradov VS, Mel'nik NN, Arapkina LV, Chapnin VA, Chizh KV, Yuryev VA: The role of interdiffusion and spatial confinement in the formation of resonant Raman spectra of Ge/Si(100) heterostructures with quantum-dot arrays. Phys Solid State 2008, 50: 1970. [ArXiv:1010.1927] [ArXiv:1010.1927] 10.1134/S1063783408100302

    Article  Google Scholar 

  43. Kucherenko IV, Vinogradov VS, Melnik NN, Arapkina LV, Chapnin VA, Chizh KV, Yuryev VA: Effect of interdiffusion and quantum confinement on Raman spectra of the Ge/Si(100) heterostructures with quantum dots. In Proceedings of the 16th International Symposium "Nanostructures: Physics and Technology". Vladivostok, Russia: Ioffe Physico-Technical Institute, St. Petersburg, Russia; 2008:199. [ArXiv:0908.1378] [ArXiv:0908.1378]

    Google Scholar 

  44. Yuryev VA, Arapkina LV: Defects of Ge quantum dot arrays on the Si(001) surface. Physica B 2009, 404: 4719. [ArXiv:0908.0841] [ArXiv:0908.0841] 10.1016/j.physb.2009.08.118

    Article  Google Scholar 

  45. Chadi DJ: Stabilities of single-layer and bilayer steps on Si(001) surfaces. Phys Rev Lett 1987, 59: 1691. 10.1103/PhysRevLett.59.1691

    Article  Google Scholar 

Download references


This research was supported by the Ministry of Education and Science of the Russian Federation, the State Contract No. 02.513.11.3130 and the State Contract No. 14.740.11.0069. It was also partially financed within the "Sabelnik-2" Research Project.


aAs well as decreasing of the wafer annealing temperatures and times during the clean Si(001) surface preparation.

bThat is the Ge coverage or, in other words, the thickness of the Ge film measured by the graduated in-advance film thickness monitor using the quartz sensor installed in the MBE chamber.

cThe Si source was switched offduring the experiments.

dIn other words, it foreruns a moment of formation of the first {105}-faceted cluster with the height-to-width ratio of 1:10 on WL.

eHereinafter, the cluster heights are counted from the WL top.

f Note that we did not observe a height limitation of pyramids. We suppose that they may give rise to one of the types of array defects--huge clusters--which sometimes appear among ordinary huts [44].

Author information

Authors and Affiliations


Corresponding author

Correspondence to Vladimir A Yuryev.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

LA participated in the design of the study, carried out the experiments, performed data analysis, took part in discussions and interpretation of the results; she proposed the structural models. VY conceived of the study and designed it, processed images and performed data analysis, took part in discussions and interpretation of the results; he also supervised and coordinated the research projects.

Authors’ original submitted files for images

Below are the links to the authors’ original submitted files for images.

Authors’ original file for figure 1

Authors’ original file for figure 2

Authors’ original file for figure 3

Authors’ original file for figure 4

Authors’ original file for figure 5

Authors’ original file for figure 6

Authors’ original file for figure 7

Authors’ original file for figure 8

Authors’ original file for figure 9

Authors’ original file for figure 10

Authors’ original file for figure 11

Authors’ original file for figure 12

Authors’ original file for figure 13

Authors’ original file for figure 14

Authors’ original file for figure 15

Authors’ original file for figure 16

Authors’ original file for figure 17

Authors’ original file for figure 18

Authors’ original file for figure 19

Authors’ original file for figure 20

Authors’ original file for figure 21

Authors’ original file for figure 22

Authors’ original file for figure 23

Authors’ original file for figure 24

Authors’ original file for figure 25

Authors’ original file for figure 26

Authors’ original file for figure 27

Authors’ original file for figure 28

Authors’ original file for figure 29

Authors’ original file for figure 30

Authors’ original file for figure 31

Authors’ original file for figure 32

Authors’ original file for figure 33

Authors’ original file for figure 34

Authors’ original file for figure 35

Authors’ original file for figure 36

Authors’ original file for figure 37

Authors’ original file for figure 38

Authors’ original file for figure 39

Authors’ original file for figure 40

Authors’ original file for figure 41

Authors’ original file for figure 42

Authors’ original file for figure 43

Authors’ original file for figure 44

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Reprints and Permissions

About this article

Cite this article

Arapkina, L.V., Yuryev, V.A. CMOS-compatible dense arrays of Ge quantum dots on the Si(001) surface: hut cluster nucleation, atomic structure and array life cycle during UHV MBE growth. Nanoscale Res Lett 6, 345 (2011).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:


  • Molecular Beam Epitaxy
  • Molecular Beam Epitaxy Growth
  • Triangular Facet
  • Paired Dimer
  • Molecular Beam Epitaxy Chamber