Figure 2From: Shrinking of Solid-state Nanopores by Direct Thermal Heating TEM micrographs showing thermal shrinking of silicon dioxide nanopore. (a) TEM micrograph of ~250 nm pore drilled with FIB in 300 nm thick oxide membrane. (b) TEM micrograph of the nanopore after 5 min of thermal shrinking at 1150°C. The diameter of the nanopore was ~150 nm. The wavy surface of the oxide at nanopore edges shows the shrinking process due to viscous flow of oxide. (c) Nanopore after 10 min. The diameter is ~20 nm. (d) Nanopore after another 10 min and 40 s showing the diameter of ~3 nm.Back to article page