Skip to main content

Table 2 Stress at several strains and elongation at break for silicone and its composites

From: Functionalised graphene sheets as effective high dielectric constant fillers

Filler content (wt.%) Stress at 100% strain (MPa) Stress at 300% strain (MPa) Stress at 500% strain (MPa) Elongation at
break (%)
  0.0 0.33 ± 0.05 0.71 ± 0.09 1.49 ± 0.18 842 ± 23
CNT 0.5 0.43 ± 0.05 0.83 ± 0.10 1.69 ± 0.22 754 ± 45
  1.0 0.74 ± 0.18 1.38 ± 0.30 2.76 ± 0.59 732 ± 38
  2.0 0.69 ± 0.06 1.35 ± 0.15 2.67 ± 0.39 583 ± 14
FGS 0.5 0.57 ± 0.03 1.33 ± 0.07 2.75 ± 0.19 651 ± 18
  1.0 0.54 ± 0.08 1.29 ± 0.21 2.46 ± 0.43 644 ± 39
  2.0 0.99 ± 0.03 2.15 ± 0.09 3.38 ± 0.17 528 ± 32