Figure 2From: Crystallization of Ti33Cu67 metallic glass under high-current density electrical pulses TEM characterization of the Ti 33 Cu 67 ribbon crystallized under a pulse of electrical current, sample N1. (a) HRTEM micrograph; (b) selected area diffraction pattern; (c) dark-field electron image showing a larger area of the sample.Back to article page