Abstract
Cracks appeared in GaN epitaxial layers which were grown by a novel method combining metal organic vapor-phase epitaxy (MOCVD) and hydride vapor-phase epitaxy (HVPE) in one chamber. The origin of cracks in a 22-μm thick GaN film was fully investigated by high-resolution X-ray diffraction (XRD), micro-Raman spectra, and scanning electron microscopy (SEM). Many cracks under the surface were first observed by SEM after etching for 10 min. By investigating the cross section of the sample with high-resolution micro-Raman spectra, the distribution of the stress along the depth was determined. From the interface of the film/substrate to the top surface of the film, several turnings were found. A large compressive stress existed at the interface. The stress went down as the detecting area was moved up from the interface to the overlayer, and it was maintained at a large value for a long depth area. Then it went down again, and it finally increased near the top surface. The cross-section of the film was observed after cleaving and etching for 2 min. It was found that the crystal quality of the healed part was nearly the same as the uncracked region. This indicated that cracking occurred in the growth, when the tensile stress accumulated and reached the critical value. Moreover, the cracks would heal because of high lateral growth rate.
Introduction
Group III nitrides are attracting much attention for short-wavelength light emitters and high-temperature electronic devices. Nitride-based devices are mostly heteroepitaxially grown on non-native substrates, such as sapphire (Al2O3), Si, GaAs, and SiC. The differences of thermal expansion coefficient (TEC) and lattice constant between GaN and foreign substrates usually induce a large residual stress in thick GaN films. Homoepitaxy is very essential to improve the crystal quality. Hydride vapor-phase epitaxy (HVPE) is a promising technique for growing thick GaN film at reasonable cost. The conventional method of growing high quality thick film needs two systems. Before depositing the thick layer by HVPE, a template has been predeposited by MOCVD [1]. Compared with the conventional growth method, the combined hydride and metal organic vapor-phase epitaxial (MOCVD-HVPE) in one chamber has several great advantages: (1) the MOCVD and HVPE run in the same reactor without time-consuming modification or equipments replacement; (2) furthermore, the cracks and contamination introduced in the course of transfer can be voided; and (3) the growth methods can be alternated if necessary.
However, cracks are often produced in GaN thick film grown by HVPE. There are several intriguing aspects for the observed cracks of GaN on sapphire substrates. Itoh et al. [2] proposed that the cracks originated from the static cooling process. As the thermal expansion coefficient of GaN is smaller than that of sapphire [3], the film will suffer from biaxial compressive stress during cooling. Etzkorn and Clarke [4] also observed cracks in GaN film deposited by HVPE on SiC substrate. In our article, the cracks existing in GaN thick films were observed directly and the probable formation mechanism was proposed.
Experiments
The sample was grown using a homemade MOCVD-HVPE system, as shown in Figure 1. The reactor system consists of two temperature zones which are heated by resistance wire heater. The liquid gallium (Ga) was heated to 900°C by the first heater for reacting with hydrogen chloride (HCl); the substrate was heated up to 1050°C using the second heater. Before depositing GaN thick film, a 60-nm thick low temperature (550°C) GaN buffer layer and a 0.82-μm thick high temperature layer were predeposited on a c-plane sapphire substrate by MOCVD. Ammonia (NH3) and trimethylgallium (TMGa) were used as N and Ga sources with the flow rate of 0.18 mol min-1 and 50 μmol min-1, respectively. In addition, N2 was used as carrier gas with the flow rate of 2 standard liters per minute (SLM). In the HVPE experiments, GaCl was formed by the reaction of gaseous HCl and liquid Ga at 900°C, and then reacted with NH3 to grow GaN thick film. A 22-μm thick film was deposited by HVPE, with the HCl flow rate being 50 standard cubic centimeters per minute (sccm), NH3 flow rate being 4 SLM, and the N2 carrier gas flow rate being 2 SLM.
The high-resolution X-ray diffraction (D8 discover) was used to determine the lattice constant c near top surface. The curvature was also determined by this equipment, following the suggestion given by Liu et al. [5]. D8 discover was equipped with a twofold hybrid monochromatic and a threefold Ge (220) analyzer. The crystal quality of the sample was characterized using the high-resolution X-ray diffraction apparatus at Beijing Synchrotron Radiation Facility. The micro-Raman measurements were done using JYHR800 Raman spectrum. The laser was an argon ion laser operating at 514.5 nm. The spectral frequency resolution was less than 0.2 cm-1 and the spatial resolution was less than 1 μm. The error bar is 0.2 cm-1. All micro-Raman spectra were recorded in the backscattering geometry. The spectrometer was calibrated using single-crystal silicon as a reference. The surface morphology and cracks were observed by SEM (using Hitachi S4800). The cathodoluminescence (CL) was performed in a scanning electron microscope (SEM) using Gantan mono CL system at room temperature.
Results and discussion
The overall crystal quality of the sample was determined by high-resolution X-ray diffraction with Synchrotron Radiation as light source. As illustrated in Figure 2a, the rocking curves of (0002) and (101 2) were obtained and the full widths at half maximum (FWHM) were 970 and 1358 arc seconds, respectively. The phi scan presents a sixfold symmetry of wurtzite structure of GaN, as shown in Figure 2b. The dislocation density of the crystal was about 2 × 109 cm-2 determined by XRC and AFM after selective etching [6, 7].
In order to observe the cracks under the surface, the sample was etched for 5 and 10 min in a solution of H2SO4:H3PO3 (3:1) at 200°C, and the two samples were marked as Af5 and Af10, respectively. The unetched sample was labeled as A. The etching rate was about 0.2 μm min-1. Cracks were observed on surface till the sample was etched for 10 min, as illustrated in Figure 3c. The underlayer cracks were also observed by optical microscope, as illustrated in Figure 3d. In the transmitted light image, the cracks were parallel to {1010} plane and formed a network arranged at 120° with each other. The effects of grain boundaries and dislocations have been revealed by CL mapping. The crystal quality of the grain boundaries is inferior to the other regions. High density of dislocations and other extended defects exist at the grain boundaries. If the cracks were located near the grain boundaries, various brightness distributions would exist between the cracked regions and the far away cracked regions [8, 9]. As shown in Figure 4a, c, the bright distribution near the cracked regions and regions far away from cracks was nearly the same. We believe that the dislocations and grain boundaries do not interact with the cracks. This conclusion is also consistent with Figure 6b.
The stresses were determined by HR-XRD and Raman, as shown in Figure 5. The lattice constant c is calculated by [10]
where d 0001 equals to the lattice constant c; λ is the wavelength of the X-ray; θ 0002 and θ 0004 are the (0002) and (0004) plane diffraction peaks, respectively. The curves were determined using θ-2θ mode. Δθ is zero error. The strain along the c direction is expressed as
According to the relationship between the strain and stress [11], the stress in the plane can be expressed as
where c 0 is the lattice constant of stress-free GaN. At room temperature, the free-stress lattice constant c 0 is referenced to 0.51850 nm [12]. σ xx and ε zz are the biaxial stress and strain in the growth plane, respectively. E and ν are Young's modulus and Poisson's ratio, respectively. The determined and concluded data are shown in Table 1. These results suggest that the stress decreases with increasing etching time. The values of the stress and curvature in A and Af5 are nearly the same. However, the lattice constant c and the curvature rapidly changed in Af10.
The Raman scattering is a useful tool for investigating the strain of epitaxial film. The frequency of E 2 (high) phonon is very sensitive to the in-plane strain. As illustrated in Figure 5a, the frequencies of E 2 high exhibit redshift with increasing etching time, which is consistent with the variations of lattice constant c. Many articles reported that the strain-free frequency of E 2 high mode was 567.5, 567.6, and 568 cm-1[13–15]. If the frequency is larger than the value of reference, the presence of compressive stress will be expected; on the other hand, the stress will be tensile. This effect had already been observed for hydrostatic pressure, biaxial strain, and uniaxial strain [11]. The obtained lattice constants c were larger than the reference value, so the samples suffered from compressive stress at room temperature. The variation of the stress which was calculated along depth was in agreement with the shift of E 2 (high) phonon frequency. Furthermore, this trend was consistent with the variation of the curvature. Sample Af10 had two notable features: the cracks were observed in the surface; stress rapidly dropped. We could believe that the stresses were mainly relaxed by producing cracks.
In order to gain further insight into the nature of the cracks, we observed the cross-sections of films after cleaving. The cleavage plane was (1010). A typical cross-sectional SEM image was shown in Figure 6a. The cracks marked in black frame had a number of notable features: the cracks were perpendicular to the film/substrate interface; the cracks neither approached to the surface nor extended to the substrate; and the cracks appeared to be pinched off at several locations, and with well-rounded ends, suggesting the cracks may heal up.
In order to gain a deep insight into the origin of the cracks, stress distribution along depth was measured by cross-sectional micro-Raman spectral. Raman spectra were conducted in 2 μm steps along the depth. The frequencies and the linewidths of the Raman mode were shown as a function of the distance from the interface of GaN/substrate as shown in Figure 7b. It was noticeable that the peaks of Raman E 2 (high) phonon mode were variable; it blueshifts at the interface of film/substrate, then goes to steadiness in the following, after that the peaks fall down and then returned to blueshift; the linewidth of the E 2 phonon was approximately 2.6 cm-1 near the surface and increased with decreasing distance from the interface of film/substrate. The linewidths were mainly affected by stress and defects. Many articles reported that columnar structures and defects existed at the near interface region [8, 16]. It is reasonable to conclude that the broader E 2 linewidth near the interface is due to the disorder and strain associated with these defects. With increasing thickness, the crystal quality gets better. This result is in agreement with the variation of the linewidths.
The determined stress is the sum of the intrinsic and extrinsic at room temperature. The stress is affected by lattice mismatch, coefficient of thermal expansion mismatch, islands coalescence, grain growth, and gas impurity [17]. Thermal strains induced by the expansion coefficient difference between the substrate and GaN film dominate in the extrinsic stress. This strain is expressed as
where αf(T) and αs(T) are the thermal expansion coefficients of the film and substrate, respectively. αs(T) is larger than αf(T) [18]. The film/substrate system reduces their elastic potential energy by bending, resulting in a strain gradient along the depth. It is assumed that the stress distribution in the substrate and film is a linear function along the depth. The elastic energy in the z th layer U(z) caused by bending is given by [19]
where h f and h s are the thicknesses of the film and the substrate and their values are 22 and 430 μm, respectively. z is the distance from the bottom of the substrate. M s and M f are the elastic constants of the substrate and film, respectively. ε 0 is the strain in the central plane of substrate. The system potential energy V system is
.
Based on energy minimization principle, k and ε 0 can be obtained by ∂V/∂ε0 = 0 and ∂V/∂k = 0, We defined r as the weighted ratio of elastic constant of the film and the substrate.
and
where M f and M s are the elastic constants and can be calculated by
where C ij are the stiffness constants (as shown in Table 2) and the x, y, and z axes are chosen along the GaN 1120, 1100, and 0001 directions, respectively. Since these directions are parallel to the crystal principal axis, the shear stress components (i ≠ j) are zero. The values of M f and M s are 455 and 603 GPa, respectively. We calculated that the radius of curvature was 0.123 m and ε 0 was 6.4 × 10-4, assuming the film and the substrate were not in the plastically deforming area in the cooling process. As illustrated in Figure 8b, the largest tensile strain is 0.0025 located at substrate side near the interface and whole GaN film suffers from the compressive stress. If cracking happened in the cooling process, it would be difficult to explain why the cracks did not appear in the substrate but in the film. It is reasonable to believe that the cracks are generated in the growth process.
The cracks nucleation and extension are the consequences of both the existence of tensile stress and exceeding the critical thickness during the growth process. We should explain the origin of the tensile stress. Many authors observed intrinsic tensile stress using in situ measurements of wafer bending curvature [20–22]. They found that the compressive stress appeared first, and then the compressive stress switched to steady tensile stress. This tensile stress was attributed to islands coalescence. This phenomenon was independent of the substrate. Hoffman [23] proposed that adjacent islands with vertical surface grew closer to one another and then elastically snapped together when the gap between the islands reached some critical size. The decrease of the solid-vapor interfacial energy balances the increase of the stress-related mechanical energy and grain boundary-related surface energy. Cracks will occur once the stressed films reach the critical thickness. Once the cracks have been introduced, an opening channel would be left. However, it is difficult to explain that the cracks do not extend to the surface and many cracks are buried in the consequence growth. Etzkom and Clarke [4] proposed several possibilities for the cracks that get closed up and buried: film lateral growth at the crack opening; concurrent diffusion transport by surface diffusion, driven by capillarity; and cracks face touch in cooling process. However, only at high temperature the atom have high diffusing rate. In our system, the temperature dropping from 1050 to 600°C only needs 3 min. Some authors had calculated the Ga atom surface diffuse length and the value was less than 13 nm min-1 at 1050°C [24]. A large number of Ga and N atoms concurrent diffusion along the cracks surface are very difficult. If the healed part originates from the face touch in cooling, the crystal quality would be inferior to the uncracked part. In order to compare crystal quality of the cracks edge with that of healed part, the cross was etched for 2 min at 200°C in mixed solution of H2SO4:H3PO3 (3:1). Only crack edges were etched faster than those of the healed part, as shown in the Figure 6b. It would be concluded that the lateral growth predominates in the healing process. The tensile stress was mainly relaxed by the cracks, but residual tensile stress also was present in the uncracked region [25]. The cracking will be reproduced in the uncracked region.
When the temperature dropped from the growth temperature to the room temperature, the thermal stress mostly exerted in the healed apartment and uncracked region. These explanations are consistent with the result of Raman spectra in Figure 7b and surface stress analysis in Table 1. The variation of phonon frequency appeared as S-shaped distribution along depth; the cracks did not extend to the surface or approach the substrate; the crystal quality of healed part is comparable with the uncracked part.
Conclusion
The origin of cracks in GaN film grown by MOCVD-HVPE system has been analyzed by SEM, HR-XRD, Raman, and CL. The stress distribution was obtained by cross-sectional Raman spectra. According to the stress distribution and the cracks distribution, it would be expected that the cracks originate from the growth process. When the films reach the critical thickness, cracks will be generated. Then the cracks will be healed in the consequent growth by lateral growth. So the cracks do not extend to either the substrate or the film surface.
Abbreviations
- CL:
-
cathodoluminescence
- Ga:
-
gallium
- HCl:
-
hydrogen chloride
- HVPE:
-
hydride vapor-phase epitaxy
- MOCVD:
-
metal organic vapor-phase epitaxy
- NH3 :
-
ammonia
- SEM:
-
scanning electron microscopy
- SLM:
-
standard liters per minute
- sccm:
-
standard cubic centimeters per minute
- TEC:
-
thermal expansion coefficient
- TMGa:
-
trimethylgallium
- XRD:
-
X-ray diffraction.
References
Jain RB, Fareed RSQ, Zhang J, Gaska R, Kuokstis E, Yang J, Maruska HP, Khan MA, Mickevicius J, Tamulaitis G, Shur MS: Growth of high resistance thick GaN templates by HVPE. Phys Stat Sol (c) 2005, 7: 2091.
Itoh N, Rhee JC, Kawabata T, Koike S: Study of cracking mechanism in GaN/α-Al 2 O 3 . J Appl Phys 1985, 58: 1828.
Leszczynski M, Teisseyre H, Suski T, Grzegory I, Bockowski M, Jun J, Palosz B, Porowski S, Pakula K, Baranowski JM, Barski A: Acta Phys Pol A. 1996, 90: 887.
Etzkorn EV, Clarke DR: Cracking of GaN films. J Appl Phys 2001, 89: 1025.
Liu JQ, Wang JF, Qiu YX, Guo X, Huang K, Zhang YM, Hu XJ, Xu Y, Xu K, Huang XH, Yang H: Determination of the tilt and twist angles of curved GaN layers by high-resolution x-ray diffraction. Semicond Sci Technol 2009, 24: 125007.
Tavernier PR, Etzkorn EV, Wang Y, Clarke DR: Two-step growth of high-quality GaN by hydride vapor-phase epitaxy. Appl Phys Lett 2000, 77: 1804.
Dam CEC, Grzegoczyk AP, Hagenman PR, Larsen PK: Method for HVPE growth of thick crack-free GaN layers. J Cryst Growth 2006, 290: 473.
Hwa-Mok Kim, Jun-Sung Choi, Jae-Eung OH, Tae-Kyung Yoo: Cathodoluminescence Characterization of GaN Thick Films Grown by Using the HVPE Method. J Korean Phys Soc 2000, 37: 956.
Lu H, Cao XA, LeBoeuf SF, Hong HC, Kaminsky EB, Arthur SD: Cathodoluminescence mapping and selective etching of defects in bulk GaN. J Cryst Growth 2006, 291: 82.
Zheng XH, Wang YT, Feng ZH, Yang H, Chen H, Zhou JM, Liang JW: Method for measurement of lattice parameter of cubic GaNlayers on GaAs (0 0 1). J Cryst Growth 2003, 250: 345.
Wagner JM, Bechstedt F: Properties of strained wurtzite GaN and AlN: Ab initio studies. Phys Rev B 2002, 66: 115202.
Detchprohm T, Hiramstsu K, Itoh K, Akasaki I: Relaxtion Process of the thermal Strain in the GaN/α-Al 2 O 3 Heterostructure and Determination of the Insrinsic Lattice Constants of GaN Free from the strain. Jpn J Appl Phys 1992, 31: L.1454.
Tripathy S, Chua S, Chen P, Miao Z: Micro-Raman investigation of strain in GaN and Al x Ga 1-x N/GaN heterostructures grown on Si (111). J Appl Phys 2002, 92: 3503.
Davydov VYu, Kitaev YuE, Goncharuk IN, Smirnov AN, Graul J: Semchinova O, Uffmann D, Smirnov MB, Mirgorodsky AP, Evarestov RA. Phonon dispersion and Raman scattering in hexagonal GaN and AlN. Phys Rev B 1998, 58: 91289.
Perlin P, Jauberthie-Carillon C, Itie JP, San Miguel A, Grzegory I, Polian A: Raman scattering and x-ray-absorption spectroscopy in gallium nitride under high pressure. Phys Rev B 1992, 45: 83.
Paskova T, Goldys EM, Monemar B: Hydride vapour-phase epitaxy growth and cathodoluminescence characterization of thick GaN films. J Cryst Growth 1999, 203: 1.
Koch R: The intrinsic stress of polycrystalline and epitaxial thin metal films. J Phys Condens Matter 1994, 6: 9519.
Gil B: Group III Nitride Semiconductor Compounds-Physics and Application. Oxford: Oxford University Press; 1998.
Freund LB, Suresh S: Thin film material: stress, defect formation, and evolution. Cambridge: Cambridge University Press; 2003.
Raghavan S, Redwing JM: Growth stresses and cracking in GaN films on (111) Si grownby metal-organic chemical-vapor deposition. I. AlN buffer layers. J Appl Phys 2005, 98: 023514. Raghavan S, Redwing JM: J Appl Phys 2004, 96: 2995 Raghavan S, Redwing JM: J Appl Phys 2004, 96: 2995
Raghavan S, Acord J, Redwing JM: Intrinsic stresses in AlN layers grown by metal organic chemical vapor deposition on (0001) sapphire and (111) Si substrates. Appl Phys Lett 2005, 86: 261907.
Raghavan S, Acord J, Redwing JM: In situ observation of coalescence-related tensile stresses during metalorganic chemical vapor deposition of GaN on sapphire. Appl Phys Lett 2005, 86: 261907.
Hoffman RW: In situ observation of coalescence-related tensile stresses during metalorganic chemical vapor deposition of GaN on sapphire. Thin Solid Films 1976, 34: 185.
Morkoc H: Handbook of Nitride Semiconductors and Devices: Materials Properties, Physics and Growth. Volume 1. Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA; 2008:464.
Hiramatsu K, Detchprohm T, Akasaki I: Relaxation Mechanism of Thermal Stresses in the Heterostructure of GaN Growth on Sapphire by Hapor Phase Epitaxy. Jpn J Appl Phys 1993, 32: 1528.
Polian A, Grimsditch M, Grzegory I: Elastic constants of gallium nitride. J Appl Phys 1996, 79: 3343.
Simmons G, Wang H: Single Crystal Elastic Constants and Calculated Aggregate Properties: A Handbook. 2nd edition. Cambridge, MA: Massachusetts Institute of Technology Press; 1970.
Acknowledgements
This work was supported by National Science Foundation of China (Nos. 60776015, 60976008), the Special Funds for Major State Basic Research Project (973 program) of China (No. 2006 CB604907), and the 863 High Technology R&D Program of China (Nos. 2007AA03Z402, 2007AA03Z451).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
JL carried out the experiments and measured the material, drafted the manuscript. XL, SY, QZ and ZW directed the experiments and the drafting of the paper. CL and YG participated the growth of material. ZL and XX carried out the measurement of Raman. TY and HW carried out the measurement of XRD. AY and HS carried out the etching. HW and CJ carried out the measurement of CL.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Liu, J., Liu, X., Li, C. et al. Investigation of cracks in GaN films grown by combined hydride and metal organic vapor-phase epitaxial method. Nanoscale Res Lett 6, 69 (2011). https://doi.org/10.1186/1556-276X-6-69
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-6-69