Abstract
We have investigated exciton localization in binary GaN nanorods using micro- and time-resolved photoluminescence measurements. The temperature dependence of the photoluminescence has been measured, and several phonon replicas have been observed at the lower energy side of the exciton bound to basal stacking faults (I 1). By analyzing the Huang-Rhys parameters as a function of temperature, deduced from the phonon replica intensities, we have found that the excitons are strongly localized in the lower energy tails. The lifetimes of the I 1 and I 2 transitions were measured to be < 100 ps due to enhanced surface recombination.
PACS: 78.47.+p, 78.55.-m, 78.55.Cr, 78.66.-w, 78.66.Fd
Introduction
The wide band gap semiconductor, GaN, and its heterojunction systems with AlGaN, has been intensively investigated during the past decade and has shown to be a very useful material for developing light emitting diodes, laser diodes, and high-power and high-temperature electronic devices [1, 2]. It features a parabolic lowest conduction band with a band gap energy of approximately 3.4 eV. The separation between the conduction band and the nearest satellite valley is approximately 1.4 eV. Due to the properties of its constituents, it is also characterized by high-energy optical phonons (ħ ωLO ≈ 92 meV).
Carrier localization in III-nitride materials caused by compositional fluctuations in ternary alloys leads to tailing of the energy bands that is observed in both absorption and photoluminescence (PL) spectra. Furthermore, it has been claimed that this localization gives rise to the high quantum efficiency commonly found in III-nitrides by preventing the carriers from reaching the dislocation level (which acts as many non-radiative recombination centers) [3, 4]. These localizations are caused by alloy fluctuations in ternary semiconductors such as AlGaN [5, 6] and InGaN [7, 8] and in multi-quantum well structures such as AlGaN/GaN [9] and InGaN/GaN [10]. In binary systems such as GaN nanorods, clear identification of exciton localization with an appropriate analysis has rarely been reported. Exciton localization features have, however, been identified on basal stacking faults (BSFs) in a-plane epitaxial laterally overgrown GaN both experimentally [11] and in numerical calculations [12].
In this paper, we report on exciton localization within binary semiconductor GaN nanorods that are grown directly on Si(111) substrates. Time-integrated micro-photoluminescence and time-resolved photoluminescence (TRPL) experiments were carried out in order to study the optical properties of the GaN nanorods. The Huang-Rhys (H-R) parameters were calculated from the phonon replica intensities in order to understand exciton localization due to potential fluctuations.
Experimental
Sample preparation and characterization
The samples used in this study were grown on Si (111) substrates, without a buffer layer, by RF-plasma-assisted molecular beam epitaxy. The Ga source is a 7N5 pure metal in a conventional effusion cell. Nitrogen of 6N purity is further purified through a nitrogen purifier and then introduced into a plasma generator. A Si(111) substrate was degreased and then etched with diluted HF. The substrate was treated by thermal annealing at 1,000°C for 30 min. After deoxidation, the substrate temperature was lowered to 750°C for growth. The nanorod dimensions and density were determined by controlling the III/V ratio as well as growth time. The optical properties of GaN nanorods are determined mainly by the nanorods' dimensions, which in turn are strongly affected by the III/V ratio. More detailed growth conditions and techniques for GaN nanorods have been reported elsewhere [13–16]. Figure 1a, b shows high-resolution field emission scanning electron microscopy images at the cross-sectional and the plan view, respectively, for the bulk-like GaN nanorods. Two growth regimes are present in the sample, that is, a compact columnar growth from the Si substrate, and nanorods which protrude from the compact region. The compact region forms from the coalescence of nanorods. The average nanorod diameter is approximately 100 nm, and the average length is approximately 4 μm. More detailed information on the nanorods can be found in references [13, 14].
Photoluminescence measurements
A commercial micro-PL spectroscopy system (Renishaw Wotton-under-Edge, UK) was used for photoluminescence measurements. The excitation source was a He-Cd laser operating at 325 nm. This was focused to a spot size of approximately 0.8 μm2 (marked with the dotted circle in Figure 1b) on the sample by a 36× reflecting objective positioned above a continuous-flow helium cryostat which housed the sample. The same objective was used to both focus the incident beam and to collect the resulting luminescence, which was subsequently directed to a spectrometer with a spectral resolution of approximately 700 μeV and a spatial resolution of 0.8 μm. The signal was detected using a charge-coupled device detector. For TRPL measurements, a frequency-tripled pulsed Ti:Al2O3 laser (100 fs at 76 MHz) was used to excite the samples at a wavelength of 266 nm. A commercial time-correlated single-photon counting system was used for detection.
Results and discussion
The temperature dependence of the PL emission from the nanorods, measured at temperatures from 4.2 to 75 K, is presented in Figure 2a. Figure 2b shows a zoomed-in section of the spectra in which a strong excitonic emission, originating from both donor-bound excitons (I 2 transition or D0X) and free excitons (FX) at energies of 3.468 and 3.476 eV, respectively, is observed. These peaks dominate the spectra at higher temperatures (note the log scale). The FX emission appears as a high-energy shoulder on the I 2 peak, and we observe that it becomes red-shifted as the temperature increases, in line with the band gap energy dependence on temperature. At temperatures above 75 K, the I 2 emission was deionized contributing to the FX emission. In contrast, the I 2 emission energy appears to be temperature independent, which supports the assertion that it originates from a localized source. To the best of our knowledge, this localization effect has not previously been observed in GaN epilayers, and indeed, we only observe the effect in samples such as the one investigated here, which exhibits the coalescence of many nanorods.
In addition to these two peaks, there is a broad emission (full width at half maximum (FWHM), approximately 30 meV) at 3.417 eV, which has been labeled I 1 0. This has been attributed to both extended structural defects located at the bottom of the nanorods [17] and the recombination of excitons bound to the BSFs. The BSFs are produced during the initial phase of the growth and propagate perpendicularly to the c-axis from the substrate toward the surface of the sample [18, 19]. Indeed, densely merged GaN nanorods on the surface (as shown in Figure 1) may result in the formation of the localized defects.
A series of satellite peaks at the low energy side of the aforementioned transitions, which is assigned to phonon replicas of the I 1 0 emission, are also observed. The energy separation of each adjacent peak is approximately 92 meV, in good agreement with the longitudinal optical (LO) phonon energy in GaN. We denote the intensity of the nth phonon replica for I 1 0 as I 1 n (n = 0, 1, 2, etc), where n = 0 corresponds to the main emission line (non-replica). The intensity ratio of adjacent phonon replicas can be expressed as
where S, the H-R parameter, is defined as
Here, E LO is the LO phonon energy and V(q) is the matrix element for the interaction between the exciton and the phonon, with wave vector q. The H-R parameter is therefore a quantitative measure of the exciton-phonon coupling strength [20, 21] and, by extension, a measure of the degree of localization (localized excitons have a stronger interaction with phonons as their wavefunctions contain large q components [22]).
The inset of the Figure 3 shows the extracted H-R parameters for the I 1 transition as a function of temperature (T). The value of S 1 at T = 4.2 K for the I 1 is measured to be 0.29. It is a well-documented phenomenon that the value of S 0 is always smaller than the H-R parameter measured between higher order satellite peaks [21] due to the fact that whilst all recombining excitons contribute to the zero order peak, only those that are deeply confined contribute meaningfully to the higher order satellites. The ratio of S 1/S 0, or the extent to which S 0 is reduced by this effect, can therefore be used as a measure of the proportion of carriers that are localized [5, 21]. Value of S 1/S 0 much in excess of unity represents a situation with few localized carriers. Figure 3 shows the temperature dependence of the ratio S 1/S 0 for the I 1 transition. The value of S 1/S 0 initially decreases with increasing temperature (4.2 to 30 K) before rapidly increasing for temperatures above 30 K. Similar behavior has been observed previously in InGaN QWs [23] and Al x Ga1 - x N alloys [5] and is explained by exciton localization: Carriers that are strongly localized to deeper states at low temperature interact with the phonons but become delocalized by thermal energy with increasing temperature. The rise of S 1/S 0 for temperatures over 40 K roughly corresponds to, and is indeed caused by, the onset of a fall in S 0 while S 1 continues to rise. The continuing increase of S 1 (and S 0 for T < 50 K) with temperature is due to an increased population of phonons. The fall in S 0 (T > 50 K) is most likely due to the delocalization of excitons at I 1 0, causing a reduction in the intensity at I 1 1 (and indeed I 1 2). The emission intensity of I 1 0, however, is due to emission from all recombining excitons, so the thermal delocalization will have a less immediate effect on I 1 0resulting in a decrease of S 0 and hence the increase of the ratio S 1/S 0.
In order to further understand the carrier recombination dynamics of the excitons in GaN nanorods, we performed TRPL measurements on the sample at a range of photon energies. Two representative TRPL decay traces, taken at 10 K, along with the instrument response function (IRF), are presented in Figure 4. The shoulders in the IRF traces are due to electron reflections. This is a common problem in time-correlated photon counting system when relatively short time decays are involved. Software has been used to take into account this response function in the fitting procedure. The FWHM of the IRF is approximately 40 ps and was de-convoluted from the measured decays with commercial decay analysis software (PicoQuant Fluofit, PicoQuant GmbH, Berlin Germany). The mono-exponential lifetimes of the emission at 3.417 and 3.468 eV are calculated to be approximately 68.1 ps and approximately 92.2 ps, respectively. The decay rate is fast due to surface recombination on the nanorods, which is enhanced by the large surface to volume ratio exhibited by the columns. This is consistent with the results by Schlager et al [24]. The surface recombination lifetime, τ s, which is strongly dependent on the surface recombination velocity, v s, can be approximated to d/4v s for the case of a hexagonal column of diameter d [24, 25]. We estimated the surface recombination velocity to be 27 × 103 cm.s-1, which is a little larger, but comparable, than that calculated by Schlager et al, owing to the faster decays observed in our case. It should be noted, however, that in the literature, there is little consistency in the lifetimes quoted for the donor-bound and acceptor-bound excitons. In fact, in GaN, the lifetimes range widely from a few tens to a few hundreds of picoseconds [26–31].
Conclusions
In summary, we have investigated the exciton localization in bulk-like GaN nanorods by micro- and time-resolved photoluminescence measurements. In the temperature-dependent photoluminescence measurements, several phonon replicas at the lower energy side of the exciton bound to the BSFs (I 1 0) are observed. By analyzing the H-R parameter as a function of temperature deduced from the phonon replica intensities, we found that the excitons are strongly localized in the lower energy tails. For the I 1 transition, the value of S 1/S 0 slightly decreases when the temperature increases from 4.2 to 30 K and then rapidly increases with further temperature increase, up to a value of 75 K. The PL decay times for the emissions at 3.468 and 3.417 eV were measured to be 92.2 and 68.1 ps, respectively. These fast decays are due to surface recombination, which is enhanced due to the large surface to volume ratio of the columns. It is finally concluded that exciton localizations in III-nitride materials can be observed not only in ternary alloys but also in binary semiconductors.
References
Nakamura S, Senoh M, Nagahama S, Iwasa N, Yamada T, Matsushita T, Sugimoto Y, Kiyoku H: High-power, long-lifetime InGaN multi-quantum-well-structure laser diodes. Jpn J Appl Phys 1997, 36(Part 2):L1059.
Ventury R, Zhang NQ, Keller S, Mishra UK: The impact of surface states on the DC and RF characteristics of AlGaN/GaN HFETs. IEEE Trans Electron Devices 2001, 48: 560.
Steude G, Meyer BK, Goldner A, Hoffman A, Bertram F, Christen J, Amano H, Akasaki I: Optical investigations of AlGaN on GaN epitaxial films. Appl Phys Lett 1999, 74: 2456.
Cho YH, Gainer GH, Lam JB, Song JJ, Yang W, Jhe W: Dynamics of anomalous optical transitions in Al x Ga 1 -x N alloys. Phys Rev B 2000, 61: 7203.
Lee KB, Parbrook PJ, Wang T, Ranalli F, Martin T, Balmer RS, Wallis DJ: Optical investigation of exciton localization in Al x Ga 1- x N. J Appl Phys 2007, 101: 053513.
Li J, Nam KB, Lin JY, Jiang HX: Optical and electrical properties of Al-rich AlGaN alloys. Appl Phys Lett 2001, 79: 3245.
Satake A, Masumoto Y, Takao M, Tsunenori A, Fumihiko N, Masao I: Localized exciton and its stimulated emission in surface mode from single-layer In x Ga 1 -x N. Phys Rev B 1998, 57: R2041.
Pecharroman-Gallego R, Edwards PR, Martin RW, Watson IM: Investigations of phonon sidebands in InGaN/GaN multi-quantum well luminescence. Mater Sci Eng B 2002, 93: 94.
Sabooni M, Esmaeili M, Haratizadeh H, Monemar B, Paskov P, Kamiyama S, Iwaya M, Amano H, Akasaki I: Exciton localization behaviour in different well width undoped GaN/Al 0.07 Ga 0.93 N nanostructures. Opto-electro Rev 2007, 15: 163.
Pecharroman-Gallego R: Temperature and well number dependence of exciton localization in InGaN/GaN quantum wells. Semicond Sci Technol 2007, 22: 1276.
Cordir P, Lefebvre P, Levrat J, Dussaigne A, Ganiere JD, Martin D, Ristic J, Zhu T, Grandjean N, Deveaud-Pledran B: Exciton localization on basal stacking faults in a -plane epitaxial lateral overgrown GaN grown by hydride vapor phase epitaxy. J Appl Phys 2009, 105: 43102.
Cordir P, Lefebvre P, Ristic J, Ganiere J-D, Deveaud-Pledran B: Electron localization by a donor in the vicinity of a basal stacking fault in GaN. Phys Rev B 2009, 80: 153309.
Park YS, Lee SH, Oh JE, Park CM, Kang TW: Self-assembled GaN nanorods grown directly on (111) Si substrates: Dependence on growth conditions. J Crystal Growth 2005, 282: 313.
Park CM, Park YS, Im H, Kang TW: Optical properties of GaN nanorods grown by molecular-beam epitaxy; dependence on growth time. Nanotechnology 2006, 17: 952.
Park YS, Park CM, Fu DJ, Kang TW, Oh JE: Photoluminescence studies of GaN nanorods on Si (111) substrates grown by molecular-beam epitaxy. Appl Phys Lett 2005, 85: 5718.
Park YS, Kang TW, Taylor RA: Abnormal photoluminescence properties of GaN nanorods grown on Si (111) by molecular-beam epitaxy. Nanotechnology 2008, 19: 475402.
Ristic J, Calleja E, Sanchez-Garcia MA, Ulloa JM, Sanchez-Paramo J, Calleja JM, Jahn U, Trampert A, Ploog KH: Characterization of GaN quantum discs embedded in Al x Ga 1 -x N nanocolumns grown by molecular beam epitaxy. Phys Rev B 2003, 68: 125303.
Shreter G, Guzzi M, Melnik YV, Vassilevski K, Dmitiev VA, Strunk HP: Cathodoluminescence and transmission electron microscopy study of the influence of crystal defects on optical transitions in GaN. Phys Status Solidi A 1999, 171: 325.
Liu R, Bell A, Ponce FA, Chen CQ, Yang JW, Khan MA: Luminescence from stacking faults in gallium nitride. Appl Phys Lett 2005, 86: 021908.
Huang K, Rhys A: Theory of light absorption and non-radiative transitions in F-centres. Proc R Soc A 1950, 204: 404.
Mowbray DJ, Kowalski OP, Skolnick MS, Hopkinson M, David JPR: Optical spectroscopy of AlGaInP based wide band gap quantum wells. Superlatt Microstruct 1994, 15: 313.
Brener I, Olszakier M, Cohen E, Ehrenfreund E, Azra R, Pfeiffer L: Particle localization and phonon sidebands in GaAs/Al x Ga 1- x As multiple quantum wells. Phys Rev B 1992, 46: 7927.
Paskov PP, Holtz PO, Monemar B, Kamiyama S, Iwaya M, Amano H, Akasaki I: Phonon-assisted photoluminescence in InGaN/GaN multiple quantum wells. Phys Status Solidi B 2002, 234: 755.
Schlager JB, Bertness KA, Blanchard PT, Robins LH, Roshko A, Sanford NA: Steady-state and time-resolved photoluminescence from relaxed and strained GaN nanowires grown by catalyst-free molecular-beam epitaxy. J Appl Phys 2008, 103: 124309.
Zhao QX, Yang LL, Millander M, Sernelius BE, Holtz PO: Surface recombination in ZnO nanorods grown by chemical bath deposition. J Appl Phys 2008, 104: 073526.
Eckey L, Holst CJ, Maxim P, Hoffmann A, Broser I, Meyer BK, Wetzel C, Mohov EN, Baranov PG: Dynamics of bound-exciton luminescences from epitaxial GaN. Appl Phys Lett 1996, 68: 415.
Shan W, Xie XC, Song JJ, Goldenberg B: Time-resolved exciton luminescence in GaN grown by metalorganic chemical vapor deposition. Appl Phys Lett 1995, 67: 2512.
Godlewski M, Bergman JP, Monemar B, Rossner U, Barski A: Time-resolved photoluminescence studies of GaN epilayers grown by gas source molecular beam epitaxy on an AlN buffer layer on (111) Si. Appl Phys Lett 1999, 69: 2089.
Im JS, Moritz A, Stevber F, Harle V, Scholz F, Hangleiter A: Radiative carrier lifetime, momentum matrix element, and hole effective mass in GaN. Appl Phys Lett 1997, 70: 631.
Harris JS, Monemar B, Amano H, Akasaki I: Exciton lifetimes in GaN and GaInN. Appl Phys Lett 1995, 67: 840.
Smith M, Chen GD, Li JZ, Lin JY, Jiang HX, Salvador A, Kim WK, Aktas O, Botchkarev A, Morkoc H: Excitonic recombination in GaN grown by molecular beam epitaxy. Appl Phys Lett 1995, 67: 3387.
Acknowledgements
This research was supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) (grant numbers K20901000002-09E0100-00210, 2010-0023856, and 2009-0076332). M. Holmes acknowledges funding from the Engineering and Physical Sciences Research Council (EPSRC) U.K. (GR/S82176/01).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
YP carried out sample growth, performed PL measurements and drafted the manuscript. MH participated in PL measurements. YS participated in the structural analysis of the sample. IY participated in the growth of the sample. HI performed the data analysis and drafted the manuscript. RT participated in PL measurements and in the design of the study. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Park, Y.S., Holmes, M.J., Shon, Y. et al. GaN nanorods grown on Si (111) substrates and exciton localization. Nanoscale Res Lett 6, 81 (2011). https://doi.org/10.1186/1556-276X-6-81
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-6-81