Table 1 Sample compositions, geometrical features, and properties
From: Manipulation of domain wall dynamics in amorphous microwires through the magnetoelastic anisotropy
Sample composition | Sample number | Sample geometry:ρ ratio, metallic nucleus diameter,d, and total diameter,D | Magnetostriction constanta |
|---|---|---|---|
Co56Fe8Ni10Si10B16 | 1 | ρ ≈ 0.45, d ≈ 13.2 μm, D ≈ 29.6 μm | 10−7 |
Co41.7Fe36.4Si10.1B11.8 | 2A 2B | ρ = 0.39, d ≈ 13.6 μm, D ≈ 34 μm; ρ ≈ 0.55, d ≈ 13.6 μm, D ≈ 24.6 μm | 25 × 10−6 |
Fe55Co23B11.8Si10.2 | 3A 3B | ρ ≈ 0.44, d ≈ 13.2 μm, D = 29.6 μm; ρ ≈ 0.55, d ≈ 12.6 μm, D = 22.8 μm | 30 × 10−6 |
Fe16Co60Si11B13 | 4 | ρ ≈ 0.39, d ≈ 13.6 μm, D ≈ 34.5 μm | 15 × 10−6 |
Fe72.75Co2.25B15Si10 | 5A 5B | ρ ≈ 0.14, d ≈ 1.4 μm, D ≈ 10 μm; ρ ≈ 0.31, d ≈ 2.8 μm, D ≈ 9 μm | 35 × 10−6 |
Fe70B15Si10C5 | 6A 6B 6C 6D 6E | ρ ≈ 0.67, d ≈ 14.6 μm, D ≈ 21.8 μm; ρ ≈ 0.63, d ≈ 15 μm, D ≈ 23.8 μm; ρ ≈ 0.48, d ≈ 10.8 μm, D ≈ 22.5 μm; ρ ≈ 0.26, d ≈ 6 μm, D ≈ 23 μm; ρ ≈ 0.16, d ≈ 3 μm, D ≈ 18 μm | 35 × 10−6 |
Co67Fe3.85Ni1.45B11.5Si14.5Mo1.7 | 7A | ρ ≈ 0.16, d ≈ 21.4 μm, D ≈ 26.2 μm | <10−7 |