Figure 8

TEM BFI, SAED, and lattice image of rice-like tenorite nanoclusters with tilt boundary and dislocation. TEM (a) BFI (left) coupled with SAED pattern (right) of the (Zn,H)-codoped tenorite nanocondensate clusters with slightly preferred orientation of (111) plane. (b) Lattice image of the individual tenorite nanocondensates ca. 5 nm in size which tended to coalesce over (111) to form (111) symmetrical tilt boundary with ($1\overline{1}\overline{1}$) plane off by 20° as indicated by 2-D forward (c) and inverse Fourier transform (d) of the square region near the [101] zone axis. Note also dislocations (denoted as T) with ($1\overline{1}\overline{1}$) half plane at the interface. The same sample as in Figure 6.