Figure 4From: Mechanically activated catalyst mixing for high-yield boron nitride nanotube growthTGA curves. TGA curves of (i) B powder ball milled alone, (ii) B ink with 0.04 M Fe(NO3)3 ethanol solution and (iii) B powder ball milled with 0.04 M Fe(NO3)3, heated up to 1,300°C in N2 gas with a temperature increasing rate of 10°C/min.Back to article page