Table 1 Contact angles of the nanostructured quartz
Plain quartz | A2 pattern | A8 pattern | A11 pattern | |
---|---|---|---|---|
θadv (°) | 119.0 ± 0.9 | 158.0 ± 1.4 | 157.4 ± 1.4 | 159.0 ± 1.0 |
θrec (°) | 79.0 ± 2.5 | 145.0 ± 7.0 | 148.2 ± 3.8 | 147.0 ± 2.0 |
Hysteresis | 40.0 | 13.0 | 9.2 | 12.0 |