Figure 2From: Fabrication and centeracterization of ordered CuIn(1−x)Ga x Se2 nanopore films via template-based electrodepositionFE-SEM images of AAO template, Au-coated AAO template, and as-grown and annealed CIGS nanopore films. (a) Top view of the AAO template prepared by high-field anodization method. (b) Au-coated AAO template after broadening the pores. (c) As-grown CIGS nanopore film deposited with aqueous solution of 2 mM CuCl2, 6 mM InCl3, 16 mM GaCl3, and 4 mM H2SeO3. (d) CIGS nanopore film annealed at 550°C.Back to article page