Table 1 Mesoporous structures of the α-Fe 2 O 3 synthesized at different temperatures for 12.0 h (FeCl 3 /H 3 BO 3 /NaOH = 2:3:4)
α-Fe2O3 nanoarchitecture | Temperature | Multipoint BET | Total pore volume | Average pore diameter |
---|---|---|---|---|
(°C) | (m2 g−1) | (cm3 g−1) | (nm) | |
1 | 120 | 21.3 | 3.9 × 10−2 | 7.3 |
2 | 150 | 5.2 | 2.9 × 10−2 | 22.1 |
3 | 180 | 2.6 | 2.9 × 10−2 | 44.7 |
4 | 210 | 2.0 | 2.1 × 10−2 | 40.3 |