Table 2 Effective mass, 2D carrier density, and Fermi energy values found from analysis of SdH oscillations
Samples | n2D(×1012 cm-2) | (EF-E1) (meV) | |||
---|---|---|---|---|---|
p-type | n-type | p-type | n-type | ||
Ga0.62In0.38As | As-grown | 1.38 | 2.02 | 36.8 | 113.8 |
Annealed (60 s) | 1.34 | 1.95 | 41.5 | 101.7 | |
Annealed (600 s) | - | 1.92 | - | 90.9 | |
Ga0.62In0.38 N0.009As0.991 | As-grown | 1.18 | 2.30 | 52.7 | 99.5 |
Annealed (60 s) | 1.16 | 2.29 | 52.0 | 82.1 | |
Annealed (600 s) | 1.17 | 2.32 | 52.8 | 83.1 | |
Ga0.62In0.38 N0.012As0.988 | As-grown | 1.20 | 2.50 | 40.0 | 0.0686 |
Annealed (60 s) | 1.06 | 2.59 | 55.5 | 0.0699 | |
Annealed (600 s) | - | 2.71 | - | 0.0788 |