Figure 5From: Core-shell-structured silica/polyacrylate particles prepared by Pickering emulsion: influence of the nucleation model on particle interfacial organization and emulsion stabilitySize distributions of polymer/silica (5 wt.%) composite particles at different polymerization times. (1) 2 min, (2) 5 min, (3) 8 min, (4) 11 min, and (5) 311 min. Mass ratio of MMA to BA is 1/2.Back to article page