Table 1 Samples of C-Si-nc suspensions to different current densities and different solvents

From: Synthesis of colloidal solutions with silicon nanocrystals from porous silicon

Sample

Current density (A cm-2)

Solvent

Porosity (%)

Thickness (μm)

M-09

1.20

Methanol

70

12

M-10

1.28

Acetone

67

11

M-14

0.25

Ethanol

99

98

M-16

1.00

Acetone

96

41

M-17

1.00

Acetone

92

15

M-19

1.28

Acetone

65

8