Table 3 Typical XRD diffraction peaks of the Si-nc powders obtained by PSi with different current densities
From: Synthesis of colloidal solutions with silicon nanocrystals from porous silicon
Sample M-09 | Sample M-10 | Sample M-14 | Sample M-16 | Sample M-17 | Sample M-19 | |||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
PP | Size (nm) | PP | Size (nm) | PP | Size (nm) | PP | Size (nm) | PP | Size (nm) | PP | Size (nm) | |
28.44 | 28.34 | 41.57 | 28.33 | 98.63 | 28.33 | 61.83 | 28.41 | 72.43 | 28.32 | 43.30 | 28.18 | 52.22 |
47.30 | 47.19 | 44.75 | 47.19 | 42.53 | 47.24 | 60.37 | 47.25 | 41.64 | 47.24 | 39.34 | 47.06 | 32.20 |
56.12 | 56.02 | 50.28 | 56.02 | 122.7 | 56.02 | 56.10 | 56.08 | 38.19 | 55.99 | 37.48 | 55.85 | 56.9 |
69.13 | 68.98 | 48.35 | 68.97 | 39.10 | 68.12 | 32.75 | 69.06 | 80.54 | 68.91 | 60.07 | 69.06 | 99.88 |
76.38 | 76.26 | 44.5 | 76.26 | 40.27 | 76.27 | 39.26 | 76.31 | 38.16 | 76.17 | 44.05 | 76.13 | 48.98 |