Table 1 Degradation efficiency of CdSe@TiO 2 -NTAs thin films prepared at different cycle after UV irradiation for 2 h
Cyclic time | 0 | r3 | r5 | r7 | r9 |
---|---|---|---|---|---|
Degradation efficiency (%) | 61.28 | 67.64 | 88.20 | 86.39 | 81.42 |