From: Structure and properties of Co-doped ZnO films prepared by thermal oxidization under a high magnetic field

Figure 2

Morphology of samples. SEM images of (a) as-deposited Zn/Co bilayer film, (b) Co-doped ZnO film oxidized without an applied magnetic field, (c) Co-doped ZnO film oxidized under an applied magnetic field of 6 T, (d) Zn particles deposited at 460°C for 15 min on Si (100), (e) ZnO particles formed by oxidation of the particles in (d) at 500°C for 40 min without an applied magnetic field, (f) ZnO particles formed by oxidation of the particles in (d) at 500°C for 40 min under an applied magnetic field of 6 T, (g) high-magnification view of (e). TEM images of the ZnO particles oxidized under applied magnetic fields of (h) 0 T and (i) 6 T. Insets are the corresponding selected area electron diffraction patterns.