Figure 12 | Nanoscale Research Letters

Figure 12

From: Soft magnetic properties of nanocrystalline Fe73B7Si16Nb3Cu1 alloy after rapid heating under tensile stress

Figure 12

Dependencies of core loss (a) and initial magnetic permeability (b) on frequency. (1) Core annealed in furnace (T a  = 550°C, t a  = 90 min). (2) Core made of ribbon heated by electric current (j h  = 42 A/mm2, t h  = 3.7 s) under tensile stress 100 MPa. (3) Cut core with non-magnetic gap 0.045 mm (T a  = 550°C, t a  = 90 min).