Table 1 Discharge capacity and capacity retention of the Li[Li0.2Ni0.16Mn0.56Co0.08]O2/Super P composite for various current densities. The listed values are obtained from the initial cycle at each current density

From: Li[Li0.2Ni0.16Mn0.56Co0.08]O2 Nanoparticle/Carbon Composite Using Polydopamine Binding Agent for Enhanced Electrochemical Performance

  44 mA g−1 110 mA g−1 220 mA g−1 660 mA g−1 1320 mA g−1
(mAh g−1) (%) (mAh g−1) (%) (mAh g−1) (%) (mAh g−1) (%) (mAh g−1) (%)
Pristine H 246.1 100 212.9 86.5 187.3 76.1 139.3 56.6 84.8 34.4
Composite HA 246.4 100 204.9 83.2 175.2 71.1 133.2 54 94.6 38.4
Composite HN 253 100 221 87.4 196.5 77.7 157.4 62.2 127.5 50.4
Pristine G 220.5 100 190.3 86.3 166.3 75.4 114.8 52.1 36.4 16.5
Composite GA 219.5 100 183.3 83.5 157.1 71.6 117.8 53.6 89.2 40.6
Composite GN 253.6 100 232 91.5 213.7 84.3 171.3 67.6 138.2 54.5