Table 1 Textual properties and chemical composition of various samples

From: Furfuralcohol Co-Polymerized Urea Formaldehyde Resin-derived N-Doped Microporous Carbon for CO2 Capture

Sample Textual properties Chemical composition by CHN
S Total S Micro S Meso V Total a V Micro V Meso b H C N Oc
m2 g−1 m2 g−1 m2 g−1 cm3 g−1 cm3 g−1 cm3 g−1 wt % wt % wt % wt %
UFC 5.13 5.13 0.0022 0.0022 1.85 66.15 23.73 8.27
UFFC 0.2 2.31 74.84 13.92 8.93
UFA-2-600 1055 861 194 0.58 0.45 0.13 1.77 65.02 13.87 19.34
UFFA1-2-600 1054 931 123 0.55 0.48 0.06 2.95 67.18 7.29 22.58
UFFA-2-600 1093 955 138 0.58 0.49 0.09 2.83 66.96 8.03 22.18
UFFA2-2-600 1000 871 129 0.53 0.45 0.07 2.86 66.01 8.46 22.67
UFFA-1-600 416 384 32 0.23 0.2 0.03 3.23 68.32 10.00 18.45
UFFA-3-600 1175 1043 132 0.61 0.54 0.05 3.30 67.32 7.76 24.62
UFFA-4-600 1639 880 759 0.90 0.48 0.42 2.45 78.3 5.18 14.07
UFFA-2-500 28 19 9 0.03 0.01 0.02 3.32 63.27 10.33 23.08
UFFA-2-700 1925 1456 469 1.04 0.79 0.25 2.03 79.82 6.25 11.9
UFFA-2-800 2273 1248 1025 1.24 0.70 0.54 0.72 89.08 2.93 7.27
  1. S Total, S Micro, and S Meso are calculated by BET analysis, t-Plot analysis, and S BET-S Micro, respectively
  2. aTotal pore volume of pores at P/Po = 0.99
  3. b V Meso is calculated by subtracting V Total to V Micro
  4. cCalculated by subtracting CHN content