Table 1 A summary of prior works of Au-Ag alloy nanostructures
From: Effect of Ag Templates on the Formation of Au-Ag Hollow/Core-Shell Nanostructures
Structures | Ag template crystal | Ag template size | Ag specific surface area (nm−1) | AuAg nanostructure size (nm) | Ref. | |
---|---|---|---|---|---|---|
AuAg NPs | n/a | 6.1 nm | 0.98 | 13 | 19 | |
AuAg NPs | n/a | 7.4 nm | 0.81 | 16 | 19 | |
Ag@Au NPs | n/a | 9.6 nm | 0.63 | 15 | 19 | |
Solid | AuAg NPs | n/a | 20.7 nm | 0.29 | ~20 | 20 |
Ag@Au NPs | n/a | 9.8 nm | 0.61 | Agcore = 8.1, Aushell = 6 | 22 | |
Ag@AuAg NPs | Single crystalline | 18.6 nm | 0.32 | n/a | 23 | |
Ag@AuAg NWs | Single crystalline | d = 90 nm h = 10 μm | 0.02 | Agcore = 85, AuAgshell = 6 | this study | |
AuAg hollow NPs | Twined | 11 nm, 14 nm | 0.42, 0.54 | dinner = 12.4, douter = 16.9 | [24] | |
AuAg hollow NPs | n/a | 41 nm | 0.14 | 46–53 | [6] | |
AuAg hollow NPs | Twined | 53 nm | 0.11 | 68 | [25] | |
Hollow | AuAg hollow NPs | n/a | 20–100 nm | 0.3-0.06 | dinner = 88, douter = 128 | [26] |
AuAg hollow NPs | Twined | 75 nm | 0.08 | n/a | [27] | |
AuAg nanotubes | Twined | d = 50 nm | n/a | n/a | [28] | |
AuAg nanotubes | Twined | d = 30–60 nm h = 1-50 μm | 0.06–0.13 | n/a | ||
AuAg nanorings | Twined | 14 nm | 0.42 | dinner = 2–4.5, douter = 12–15 | this study |