Table 1 RSM L16(44) array of the combinations of parameters for the experimental runs

From: Evolution of Zinc Oxide Nanostructures Grown on Graphene by Ultrasonic Spray Pyrolysis and Its Statistical Growth Modelling

Run (R i)

Flow rate (ml/min)

Substrate temperature (°C)

Deposition time (min)

Molarity (M)

Nano rods density (%)

Nanorods shape factor

Nanorods size (Nm)

1

8

500

0.5

0.4

0.36

1

39.2

2

1

575

15.25

0.0

8.79

0.23

35.0

3

1

355

15.25

0.7

31.07

1.1

26.3

4

0.05

500

0.5

0.4

28.03

1

36.4

5

10

355

15.25

0.0

31.06

1.1

32.2

6

0.05

500

30

0.4

19.56

0.57

11.8

7

1

355

38

0.0

76.54

1.1

30.5

8

8

210

0.5

0.4

1.51

1.1

28.0

9

0.05

210

30

0.4

94.17

0.36

10.6

10

0.05

210

0.5

0.4

1.53

0.09

25.2

11

1

355

15.25

0.2

30.92

0.36

29.0

12

0.01

355

15.25

0.0

31.03

1.1

28.0

13

8

500

30

0.4

19.54

0.01

14.6

14

8

210

30

0.4

95.15

0.09

13.4

15

1

135

15.25

0.0

0.15

1

18.2

16

1

355

0.5

0.0

1.05

1

26.6