Table 1 The results of action of fabrics impregnated with different concentrations of Ag NPs on bacteria, fungi of the genus Candida and mikromycetes
Test-culture | E.coli | K. pneumoniae | E. aerogenes | P. vulagaris | P. aeruginosa | S. aureus | E. faecalis | C. albicans | C. non-albicans | Rhodotorula glut. | Rhodotorula spp. | A.niger | A.flavus | Penicillium spp. | Alternaria alternata | ||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
nano-particles in colloid | Ag/glycerin | + | + | + | + | + | + | 0 | 0 | + | n/s | n/s | n/s | n/s | n/s | n/s | |
Ag/SDS/PVP | + | + | + | + | + | + | 0 | + | + | n/s | n/s | n/s | n/s | n/s | n/s | ||
non-particles on SiO2 powder | Ag | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | n/s | + | + | + | + | + | |
nonoparticiples on the cotton fabrics | Ag/ Cu (10·10−3) | gause | 0 | 0 | 0 | n/s | 0 | 0 | n/s | + | + | + | + | + | n/s | + | + |
Ag/Cu (1·10−2) | 0 | n/s | 0 | n/s | 0 | n/s | n/s | + | + | n/s | n/s | n/s | n/s | n/s | n/s | ||
Ag/Cu (1·10−1) | 0 | 0 | 0 | n/s | 0 | 0 | 0/+ | + | + | + | n/s | + | n/s | + | + | ||
Ag (1·10−3) | madapollam | + | + | 0 | + | + | + | 0 | + | + | n/s | + | + | 0/+ | + | + | |
Ag (1·10−2) | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | n/s | + | + | 0/+ | + | + | ||
Ag (1·10−1) | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | n/s | + | + | 0/+ | + | + | ||
Ag (1·10−3) | gause | 0 | + | + | + | + | + | + | + | + | n/s | n/s | n/s | 0/+ | n/s | n/s | |
Ag (1·10−2) | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | n/s | + | + | 0/+ | + | + | ||
Ag (1·10−1) | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | n/s | n/s | + | 0/+ | + | + | ||
ions on the cotton fabrics | Ag+/Cu2+(1·10−3) | gause | + | + | + | n/s | + | + | n/s | + | + | n/s | n/s | n/s | n/s | n/s | n/s |
Ag+/Cu2+(1·10−2) | + | + | + | n/s | + | + | n/s | + | + | n/s | n/s | n/s | n/s | n/s | n/s | ||
Ag+/Cu2+(1·10−1) | + | + | + | n/s | + | + | + | + | + | + | n/s | + | n/s | + | + | ||
Cu2+(1·10−3) | + | + | + | n/s | + | + | n/s | + | + | n/s | n/s | + | n/s | n/s | n/s | ||
Cu2+(1·10−2) | + | 0 | 0 | n/s | + | 0 | n/s | + | + | n/s | n/s | + | n/s | n/s | n/s | ||
Cu2+(1·10−1) | 0 | + | 0 | n/s | 0 | 0 | 0 | + | + | + | n/s | + | n/s | + | + | ||
Ag+(1·10−3) | 0 | + | 0 | n/s | + | + | n/s | + | n/s | n/s | n/s | n/s | n/s | n/s | n/s | ||
Ag+(1·10−2) | 0 | 0 | 0 | n/s | 0 | 0 | n/s | + | n/s | n/s | n/s | n/s | n/s | n/s | n/s | ||
Ag+(1·10−1) | 0 | 0 | 0 | n/s | 0 | 0 | + | + | + | + | n/s | + | n/s | + | + |