Table 3 The structural parameters of SnC2O4 samples
From: Synthesis and Characterization of Tin(IV) Oxide Obtained by Chemical Vapor Deposition Method
Sample | hkl | 2θ, deg. | Glancing angle d, nm | Crystallite size, nm | Lattice constant, nm | ||
---|---|---|---|---|---|---|---|
a | b | c | |||||
Sample A | 110 | 19.26 | 0.46058 | 45.7 | 1.035 | 0.549 | 0.821 |
−202 | 22.30 | 0.39671 | |||||
−112 | 27.51 | 0.32391 | |||||
−313 | 37.71 | 0.23834 | |||||
−131 | 51.11 | 0.17858 | |||||
Sample B | 110 | 19.29 | 0.45074 | 67.9 | 1.033 | 0.548 | 0.820 |
−202 | 22.44 | 0.39596 | |||||
−112 | 27.57 | 0.32330 | |||||
−313 | 37.06 | 0.24239 | |||||
−131 | 51.12 | 0.17855 |