Table 4 The structural parameters of SnO2 samples

From: Synthesis and Characterization of Tin(IV) Oxide Obtained by Chemical Vapor Deposition Method

Sample hkl 2θ, deg. Glancing angle d, nm Crystallite size, nm Lattice constant, nm
a c
Sample 1 110 26.59 0.33494 45.3 0.474 0.319
101 33.90 0.26419
211 51.79 0.17637
Sample 2 110 26.59 0.33490 64.7 0.474 0.319
101 33.90 0.26419
211 51.81 0.17632
Sample 3 110 26.59 0.33502 80.7 0.474 0.319
101 33.90 0.26425
211 51.79 0.17637
Sample 4 110 26.64 0.33437 57.8 0.474 0.319
101 33.94 0.26391
211 51.85 0.17620
Sample 5 110 26.67 0.33402 73.6 0.474 0.319
101 33.94 0.26393
211 51.84 0.17621
Sample 6 110 26.60 0.33490 74.3 0.474 0.319
101 33.91 0.26415
211 51.78 0.17641