Fig. 4 | Nanoscale Research Letters

Fig. 4

From: Achievement of Diverse Domain Structures in Soft Magnetic Thin Film through Adjusting Intrinsic Magnetocrystalline Anisotropy

Fig. 4

MFM pattern of Co1-xIrx films with a scanning area of 5μm×5μm. a out-of-plane stray field is not detected for Co81.1Ir18.9; (b)-(c) out-of-plane stray field in transition area of magnetic moment reversal is detected for Co85.7Ir14.3 and Co90.2Ir9.8, respectively (d) a stripe domain structure is clearly shown with bright and black stripes for Co91.1Ir8.9