Table 2 Lattice periods (d hkl, nm) and crystallinity (k, %) for cellulose samples: starting microcellulose (SC), micro/nanocellulose (C0), cellulose-oxide micro/nanocomposites (COM/NC) with oxide concentration 0.2% (C1), 2.2% (C2), and 18.2% (C3)
Sample | d \( 1\overline{1}0 \) | d 200 | d 004 | k |
---|---|---|---|---|
SC | 5.56 | 3.95 | 2.60 | 66 |
C0 | 5.85 | 4.02 | 2.62 | 56 |
C1 | 5.79 | 3.95 | 2.62 | 57 |
C2 | 5.72 | 3.98 | 2.61 | 58 |
C3 | 5.55 | 3.95 | 2.60 | 58 |