Table 2 Electrical conductivity σ dc , dielectric permittivity \( {\varepsilon}_r^{\prime } \), and dielectric loss tangent tanδ for the epoxy CMs versus carbon fillers content C
C, wt.% | σ dc (293 К), S/m | f, GHz | \( {\varepsilon}_r^{\prime } \), | tanδ | Ref. |
---|---|---|---|---|---|
GNP/epoxy ED20 | |||||
1 | 1.0 · 10−11 | 27 | 4.9 | 0.017 | |
2 | 1.7 · 10−11 | 6.1 | 0.036 | ||
5 | 1. 8 · 10−9 | 15 | 0.060 | ||
10 | 0.12 | 52 | 0.175 | ||
CNT(II)/epoxy SEDM2 | |||||
1 | 1.7 · 10−10 | 27 | 4.66 | 0.177 | [43] |
2 | 1.4 · 10−10 | 7.45 | 0.235 | ||
3 | 3.8 · 10−7 | 8.58 | 0.260 | ||
5 | 1.3 · 10−4 | 13 | 0.358 | ||
10 | 1.7 · 10−1 | 22.75 | 0.730 | ||
Epoxy resin L285 | |||||
– | 8.0 · 10−12 | 27 | 2.9 | 0.003 | This work |
CNT/L285 | |||||
2 | 3.2 · 10−5 | 27 | 6 | 0.10 | This work |
46 | 5.6 | 0.24 | |||
GNP/L285 | |||||
5 | 2.8 · 10−4 | 27 | 8.9 | 0.06 | This work |
46 | 8.4 | 0.11 | |||
BaM/L285 | |||||
30 | ~1 · 10−10 | 27 | 3.3a | 0.024a | This work |
37 | 3.4a | 0.028a |