Table 1 Microhardness of alloys after different TMT
From: Effect of Thermomagnetic Treatment on Structure and Properties of Cu–Al–Mn Alloy
Treatment (annealing at 200 °C for 3 h) | Average microhardness H μ(ave) (GPa) |
|---|---|
Without magnetic field | 4.4 |
In magnetic field perpendicular to the sample axis | 4.6 |
In magnetic field parallel to the sample axis | 4.8 |