Table 1 The X-ray analysis results

From: The Effect of a Small Amount SiO2 on Sintering Kinetics of Tetragonal Zirconia Nanopowders

No.

Nanopowders composition

Region of coherent scattering, nm

The phase composition, % M-phase

Lattice parameters, nm

1

3Y-TZP

31.5

3%M + 97%T

a = 5.09801

c = 5.17396

2

PM4- 3Y-TZP

31.5

8%M + 92%T

a = 5.09565

c = 5.16945

3

PM8- 3Y-TZP

28

15,5%M + 84,5%T

a = 5.09516

c = 5.16670

4

3Y-TZP-0.2 wt % SiO2

31.5

1,3%M + 98,7%T

a = 5.09555

c = 5.16953

5

PMM4-3Y-TZP-0.2 wt % SiO2

28.5

6% M + 94%T

a = 5.09561

c = 5.16940

6

PMM8-3Y-TZP-0.2 wt % SiO2

26.5

10% M + 90%T

a = 5.09510

c = 5.16668

  1. T tetragonal phase, M monoclinic phase