Table 1 Performance comparison of SiO2 and SiO2@C electrodes for LIBs

From: Facile Synthesis of SiO2@C Nanoparticles Anchored on MWNT as High-Performance Anode Materials for Li-ion Batteries

Materials Reversible capacity (mAh g−1) Initial discharge/charge specific capacity (mAh g−1) Current density Cutoff potential range (V) Ref.
Carbon-coated SiO2 nanoparticles Above 500 (50th) 900/536 50 mA g−1 0.001–3 [10]
Silicon oxide-carbon 601 (100th) 1055/458 70 mA g−1 0.01–2 [28]
SiO2@GA composite 300 (110th) 1042.7/453.3 500 mA g−1 0.01–3 [29]
SiOx@C 630 (150th) 1160/820 50 mA g−1 0.01–3 [22]
Ag-deposited 3D porous Si 755 (50th) 1906/– 50 mA g−1 0.02–1.5 [30]
SiO2@C/MWNT 557 (40th) 991/615 100 mA g−1 0.01–2.5 This work