Table 4 Mechanical properties of nanocomposite materials
Item | HV | Compressive strength (MPa) | Tensile strength (MPa) | Shear strength (MPa) |
---|---|---|---|---|
Cu/Ti3SiC2/C① | 97.787 (± 4.6847) | 468.94 (± 4.33) | 177.23 (± 3.23) | 108.38 (± 11.17) |
Cu/Ti3SiC2/C② | 96.859 (± 2.7743) | 459.03 (± 7.26) | 176.24 (± 1.85) | 104.49 (± 0.98) |
Cu/Ti3SiC2/C③ | 88.626 (± 3.3447) | 412.87 (± 1.81) | 156.11 (± 4.91) | 86 (± 4.96) |
Cu/Ti3SiC2/C[6] | 85 | / | 113 | / |
Cu/Ti3SiC2/C/ | ||||
MWCNTs [10] | 91 | 301.8 | 126.92 | / |