Table 2 Temperature dependence of FWHM of E2ghigh peak and G peak are fitted by Γph = Γph0 + ct, and the constants of Γph0 and c are given in the table
From: Temperature Dependence of Raman-Active In-Plane E2g Phonons in Layered Graphene and h-BN Flakes
Flake | Phonon | Thickness | Γ ph 0 | c |
|---|---|---|---|---|
h-BNs | E2ghigh | 16.2 nm | 13.62 cm− 1 | 4.707 × 10−4 cm−1 °C |
E2ghigh | 36.2 nm | 13.69 cm− 1 | 1.727 × 10−3 cm−1 °C | |
Graphenes | G | 16.5 nm | 8.061 cm− 1 | 2.533 × 10− 3 cm−1 °C |
G | 35.6 nm | 8.874 cm−1 | 3.604 × 10− 3 cm−1 °C |