Preparation and Magnetic Properties of Nd/FM (FM=Fe, Co, Ni)/PA66 Three-Layer Coaxial Nanocables

Abstract

A new preparation method of three-layer coaxial nanocables has been developed in this work. Nd/FM (FM=Fe, Co, Ni)/PA66 three-layer coaxial nanocables were assembled successfully from outer to inner layer by layer. PA66 nanotubes which served as the outer shell were prepared by polymer solution wetting AAO template. Ferromagnetic metals and Nd were deposited into pre-prepared PA66 nanotubes to be served as the middle layer and inner core, respectively. The results show that the structure has effects on the magnetic properties, and the nanocable preparation allows each layer, length, and thickness of the nanocables to be tuned.

Background

Coaxial nanocable is a special kind of 1D nanostructure in a composite system, which has attracted much interest for its unique structure and properties. Therefore, the nanocables have potential applications in the fields of catalyst, energy storage, photoelectric material, nanobiotechnology, environmental protection, magnetic sensor, and magnetic recording media [1,2,3,4,5,6,7,8,9,10,11]. The development of magnetic recording media is limited by the super-paramagnetic [12] and plane recording limit. Perpendicular recording involves recording data in vertical, three-dimensional columns rather than in two dimensions. To overcome these limitations, either the structure of nanomaterials or the effective anisotropy of the material can be innovated and improved. Ferromagnetic cylinders are suggested as a medium for achieving this objective.

Ferromagnetic cylinders include magnetic multilayer nanowires, nanocables, and ferromagnetic nanotubes and nanowires. Compared with ferromagnetic nanotubes and nanowires, magnetic multilayer nanowires and nanocables have effectively improved magnetic properties [13,14,15,16] and extended application fields. Among the various preparation methods, template-based method is one of the most commonly preparation methods. The size, shape, and structural properties of electrodeposited nanocylinders are controlled by the template and electrodeposition parameters. Well known to all, the permanent magnet materials consist of ferromagnetic materials and a rare earth metal. Inspired by these, ferromagnetic nanowires doped with a rare earth element prepared and can change the magnetic properties of composites [17]. To the best of our knowledge, Nd-doped magnetic nanocables have rarely been reported. We have prepared a series of rare earth-doped multilayer nanocable arrays and investigated their magnetic properties [18].

Here, a brief overview of state-of-art nanocable preparation method without using any modifying agent is presented. We employed the anodized aluminum oxide (AAO) template, which has regular channels and a wide range of size and is suitable for nanotube and nanowire and nanocable, to prepare Nd/FM (FM=Fe, Co, Ni)/PA66 triple-layer coaxial nanocables layer by layer. The outermost layer of PA66 nanotubes were fabricated by solution wetting AAO template. The outer shell consisting of a polymer nanotube can keep the inner metal core from being oxidized and eroded and retain the excellent conductivity and magnetism. The middle-layer ferromagnetic nanotubes and internal Nd nanowires were electrodeposited, and in turn, the electrodeposition can control effectively the geometrical structure. The magnetic properties of the coaxial nanocables were studied.

Methods

Preparation of PA66 Nanotubes and Working Electrode

Polyamide 66 (PA66) nanotubes can be obtained by wetting the AAO templates (the diameter is about 200 nm, and the thickness is about 60 μm) with 2–6 wt% PA66 formic acid solution. A drop of PA66 solution was placed on a glass slide, and then, a piece of AAO template was covered on the PA66 solution. The PA66 nanotubes were obtained after 40 s. A layer of PA66 film was treated with formic acid to make the PA66 nanotubes open. And then a thin film of Au was sputtered on a side of the PA66/AAO composite membrane to be served as a working electrode.

Preparation of FM (FM=Fe, Co, Ni)/PA66 Coaxial Nanotubes

Electrolyte solutions were prepared of 0.7 M Ni2+, 0.8 M Co2+, and 0.8 M Fe2+ aqueous solution separately. − 1.0 V/SCE for Ni2+, − 1.2 V/SCE for Co2+, and − 1.2 V/SCE for Fe2+ were employed to prepare Ni, Co, and Fe nanotubes, respectively, in PA66 nanotubes for 15 min to obtain the FM/PA66 double nanotubes.

Preparation of Nd/FM/PA66 Coaxial Nanocables

1.0 M Nd3+ of electrolyte solution was prepared, and then − 2.5 V direct current was input to prepare Nd nanowires into the FM/PA66 coaxial nanotubes for 60 min to form Nd/FM/PA66 coaxial nanocables

In the above electrodeposition experiment, a platinum film was used as the counter electrode and an Ag/AgCl electrode in saturated KCl solution as the reference electrode. Figure 1 shows the schematic diagram of preparing three-layer nanocables, as follows:

Fig. 1
figure 1

Schematic diagram of preparing tri-layer nanocable: (A) AAO template, (B) polymer solution, (C) polymer nanotube, (D) polymer membrane, (E) and (F) structure and section drawings of nanocable

Characterization

Scanning electron microscopy (SEM; JEOL JSM-6390LV) and transmission electron microscopy (TEM; CM200-FEG equipped with a GIF) were used to characterize the nanostructures. For TEM measurement, a drop of (5 μL) diluted sample was placed on a copper grid and evaporated prior to observation. The element analysis was identified by X-ray diffraction (XRD; Bruker D8 Advance with a Cu-Kα radiation, λ = 1.5418 Å). The magnetization measurements of the FM double nanotubes and Nd/FM/PA66 nanocables were carried out at room temperature on a vibrating sample magnetometer (VSM; Lakeshore 7307).

Results and Discussion

We did a series of condition experiments to ensure better conditions which make PA66 nanotubes and FM nanotubes grow into the same length. The nanostructure of FM/PA66 nanotubes is shown in Fig. 2. As seen from the SEM images shown in Fig. 2a, c, e, FM nanotubes and PA66 nanotubes are nearly of the same length, and the mouths of the nanotubes are almost open. After removing the AAO template, the FM/PA66 nanotubes formed regular arrays. The TEM images further prove the nanostructure of double-layer nanotubes. As seen from Fig. 2b, d, f, the walls of PA66 nanotubes as a sheath are continuous. And the nanoparticles of the FM evenly distributed on the inner wall of PA66 nanotubes. As described in our previous study [19], the diameter of nanoparticles is about 5 nm, and each nanoparticle is regarded as a magnetic domain. A certain amount of FM nanoparticles joined together to form FM nanotubes. Therefore, PA66 nanotubes and FM nanotubes formed double-layer coaxial nanotubes.

Fig. 2
figure 2

SEM images: a Ni/PA66, c Co/PA66, e Fe/PA66; TEM images: b Ni/PA66, d Co/PA66, and f Fe/PA66

Rare earth metals are one of the elements of permanent magnets. Inspired by this, Nd was electrodeposited into the above double-layer nanotubes to make three-layer coaxial nanocables. The morphology of Nd/FM/PA66 nanostructure is shown in Fig. 3. SEM images show that the nanostructures are multilayer and have almost the same length (the size parameters of the nanostructures shown in Table 1). The contrast between the interfaces of polymer and metal is clearly shown in the TEM images. Therefore, the TEM image of the Nd/Ni/PA66 nanocable in Fig. 3b shows that the contrast is clear between the outer layer and the inner layer. The outermost layer is PA66 nanotube with uniform and continuous wall, and the inner layer is composed of Nd and Ni. It is displayed that the inner layer is compact. The contrast cannot be recognized between Nd and Ni because they are all metals. As seen from Fig. 3d, f, it is obvious that the nanostructure is a core/shell structure. Likewise, it is clear for the contrast between the interfaces of PA66 and FM and not clear between the two metals.

Fig. 3
figure 3

SEM images: a Nd/Ni/PA66, c Nd/Co/PA66, e Nd/Fe/PA66; typical TEM images: b Nd/Ni/PA66, d Nd/Co/PA66, and f Nd/Fe/PA66

Table 1 Size parameters, length, and (wall) thickness of nanostructure

The X-ray diffraction pattern for the sample is shown in Fig. 4. The distinct diffraction peaks observed at 2θ of 44.32° and 75.72° are consistent with the diffraction peak of (111) and (220) crystalline planes of Co, and the diffraction peaks of Fe (101) and Fe (105) correspond with 2θ = 44.32° and 77.56°, and the diffraction peaks of Ni (011) and Ni (103) correspond with 2θ = 44.32° and 77.56°, respectively. 2θ = 77.56° is also a typical diffraction peak of Nd (206). Diffraction peaks (2θ of 37.78°, 64.48°, 77.56°, and 81.77°) of Au which were introduced by the sputtered Au film used for electrodeposition are comprehensive, because the value of Au is great, so some of peaks of Au overlap those of Fe and Co and Ni.

Fig. 4
figure 4

X-ray diffraction patterns of Nd/Ni/PA66, Nd/Co/Pa66, and Nd/Fe/PA66

The magnetism of all the samples encapsulated in AAO template was measured. AAO templates have a certain amount of antimagnetism and reduced magnetic energy of the samples slightly. Figure 5af shows the magnetization hysteresis (M-H) loops of both FM/PA66 nanotubes and Nd/FM/PA66 nanocables. It can be seen that both nanotubes and nanocables have magnetic anisotropy. It is very easy to be understood that the two systems have the same outer diameter, which determines the magnetic anisotropy of the nanotubes and nanocables. The magnetism of nanocables is stronger than that of nanotubes after deposited Nd. This is because Nd, as a typical rare earth metal, possesses a large spin-orbital coupling, when Nd nanoparticles diffused into FM in composite interface and worked together with FM metals, which leads to a synergistic effect and enhances magnetic anisotropy of Nd/FM/PA66 nanocables [20]. According to Fig. 5, the magnetic parameters of the three systems are shown in Table 2. It can be clearly seen that the magnetic parameters of the nanocables such as coercivity and residual magnetization parallel to the long axis are greater than those of vertical direction and nanotubes.

Fig. 5
figure 5

Hysteresis loops: a Ni/PA66, b Nd/Ni/PA66, c Fe/PA66, d Nd/Fe/PA66, e Co/PA66, and f Nd/Co/PA66

Table 2 Magnetic parameters, coercivity (Hc), and residual magnetization ratio (Mr/Ms) of the nanostructures with the field applied parallel (//) and perpendicular () to the long axis

Conclusions

The Nd/FM (FM=Fe, Ni, Co)/PA66 three-layer nanocable arrays have been successfully prepared, respectively. Nd/FM/PA66 nanocables show highly magnetic anisotropy due to the characteristics of rare earth metal and its synergistic effect with FM. The nanocable arrays not only provide a novel magnetic nanostructure but also have potential application in perpendicular magnetic storage and electronic devices.

Abbreviations

AAO:

Anodic aluminum oxide

FM:

Fe, Co, Ni

M-H:

Magnetization hysteresis loops

PA66:

Polyamide 66

SEM:

Scanning electron microscope

TEM:

Transmission electron microscope

XRD:

X-ray diffraction

References

  1. Tang YL, Tian JL, Malkoske T, Le WJ, Chen BD (2017) Facile ultrasonic synthesis of novel zinc sulfide/carbon nanotube coaxial nanocables for enhanced photodegradation of methyl orange. J Mater Sci 52:1581–1589

    CAS  Article  Google Scholar 

  2. Zhang Y, Tang YK, Gao SS, Jia DZ, Ma JH, Liu L (2017) Sandwich-like CNT@Fe3O4@C coaxial nanocables with enhanced lithium-storage capability. ACS Appl Mater Interfaces 9:1453–1458

    CAS  Article  Google Scholar 

  3. Wang Y, Qu QT, Li GC, Gao T, Qian F, Shao J, Liu WJ, Shi Q, Zheng HH (2016) 3D interconnected and multiwalled carbon@MoS2@Carbon hollow nanocables as outstanding anodes for Na-Ion batteries. Small 12:033–6041

    Google Scholar 

  4. Lu Y, Wang K, Li JW, Li YH, Zhang W, Sui ML (2016) Oxidative corrosion mechanism for Ag@C coaxial nanocables in radiolytic water. J Phys Chem C 120:27033–27039

    CAS  Article  Google Scholar 

  5. Liu WN, Chen JH, Yang T, Chou KC, Hou XM (2016) Enhancing photoluminescence properties of SiC/SiO2 coaxial nanocables by making oxygen vacancies. Dalton T 45:13503–13508

    CAS  Article  Google Scholar 

  6. Ullah MH, Ha CS (2016) In situ prepared polypyrrole-Ag nanocomposites: optical properties and morphology. J Mater Sci 51:7536–7544

    Article  Google Scholar 

  7. Zhang M, Wang YT, Zhang YW, Ding L, Zheng J, Xu JL (2016) Preparation of magnetic carbon nanotubes with hierarchical copper silicate nanostructure for efficient adsorption and removal of hemoglobin. Appl Surf Sci 375:154–161

    CAS  Article  Google Scholar 

  8. Liu QF, Gao CX, Xiao JJ, Xue DS (2003) Size effects on magnetic properties in Fe0.68Ni0.32 alloy nanowire arrays. J Magn Magn Mater 260:151–155

    CAS  Article  Google Scholar 

  9. Yanagishita T, Nishio K, Masuda H (2008) Antireflection polymer hole array structures by imprinting using metal molds from anodic porous alumina. Appl Phys Express 1:067004

    Article  Google Scholar 

  10. Cernea H, Vasile BS, Surdu VA, Trusca R, Craciun F, Falassi C (2018) Synthesis and characterization of CoFe2O4/BNT-BT0.08 core–shell nanotubes by a template based sol-gel method. Ceram Int 44:10813–10819

    CAS  Article  Google Scholar 

  11. Kalidasan V, Liu XL, Herng TS, Yang Y, Ding J (2016) Bovine serum albumin-conjugated ferrimagnetic iron oxide nanoparticles to enhance the biocompatibility and magnetic hyperthermia performance. Nano-Micro Lett 8(1):80–93

    Article  Google Scholar 

  12. Han XF, Shamaila S, Sharif R, Chen JY, Liu HR, Liu DP (2009) Structural and magnetic properties of various ferromagnetic nanotubes. Adv Mater 21:1–6

    Google Scholar 

  13. Shakya P, Cox B, Davis D (2012) Giant magnetoresistance and coercivity of electrodeposited multilayered FeCoNi/Cu and CrFeCoNi/Cu. J Magn Magn Mater 324:453–459

    CAS  Article  Google Scholar 

  14. Béron F, Carignan LP, Ménard D, Yelon A (2008) Magnetic behavior of Ni/Cu multilayer nanowire arrays studied by first-order reversal curve diagrams. IEEE Trans Magn 44:2745–2748

    Article  Google Scholar 

  15. Li XR, Wang YQ, Song GJ, Peng Z, Yu YM, She XL, Sun J, Li JJ, Li PD, Wang ZF, Duan XF (2010) Fabrication and magnetic properties of Ni/Cu Shell/Core nanocable arrays. J Phys Chem C 114:6914–6916

    CAS  Article  Google Scholar 

  16. Li XR, Yang C, Han P, Zhao QP, Song GJ (2016) Facile synthesis and magnetic study of Ni@polyamide 66 coaxial nanotube arrays. J Magn Magn Mater 419:57–61

    CAS  Article  Google Scholar 

  17. Wang Q, Yang XW, Li SM, Yan C, Zhang H, Yang H (2008) Hydrothermal-induced oriented growth of Fe–Co alloy and Sm3+-substituted magnetite nanowire composites. J Magn Magn Mater 320:3297–3302

    CAS  Article  Google Scholar 

  18. Li XR, Wang XX, Ma LC, Peng Z, Yang C, Han P, Li HY, Miao YC, Long YZ, Song GJ (2018) Effect of each layer on anisotropic magnetic properties of Nd/Fe/polyamide 66 three-layer coaxial nanocables. ACS Omega 3:3617–3621

    CAS  Article  Google Scholar 

  19. Li XR, Wang YQ, Song GJ, Peng Z, Yu YM, She XL, Li JJ (2009) Synthesis and growth mechanism of Ni nanotubes and nanowires. Nanoscale Res Lett 4:1015–1020

    CAS  Article  Google Scholar 

  20. Sepehri-Amin H, Ohkubo T, Hono K (2013) The mechanism of coercivity enhancement by the grain boundary diffusion process of Nd-Fe-B sintered magnets. Acta Mater 61:1982–1990

    CAS  Article  Google Scholar 

Download references

Acknowledgements

This work was supported by the Shandong Province Natural Science Foundation of China (No. ZR2014EMQ002), the Project Funded by China Postdoctoral Science Foundation (No. 2017M612196), and the Qingdao Postdoctoral Scientific Research Foundation.

Funding

Funding was received from the Shandong Province Natural Science Foundation of China (No. ZR2014EMQ002), the Project Funded by China Postdoctoral Science Foundation (No. 2017M612196), and the Qingdao Postdoctoral Scientific Research Foundation.

Availability of Data and Materials

The authors declare that materials and data are promptly available to readers without undue qualifications in material transfer agreements. All data generated or analyzed during this study are included in this article.

Author information

Authors and Affiliations

Authors

Contributions

The work presented here was performed in collaboration of all the authors. HYL is a master student of Qingdao University. GJS and ZP are professors of Qingdao University. LCM is a lecture of Qingdao University. All authors read and approved the final manuscript.

Corresponding author

Correspondence to Xiaoru Li.

Ethics declarations

Competing Interests

The authors declare that they have no competing interest.

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Li, X., Li, H., Song, G. et al. Preparation and Magnetic Properties of Nd/FM (FM=Fe, Co, Ni)/PA66 Three-Layer Coaxial Nanocables. Nanoscale Res Lett 13, 326 (2018). https://doi.org/10.1186/s11671-018-2742-8

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s11671-018-2742-8

Keywords

  • Nanocable
  • Magnetic property
  • Rare earth metal
  • Electrodeposition