Table 1 Comparison of electrochemical performance for the ferric oxide/hydroxide based electrodes
From: Tuning Hierarchical Ferric Nanostructures-Decorated Diatomite for Supercapacitors
Ferric oxide/hydroxide-based electrode | Electrolyte | Potential range (vs. SCE) | Specific capacitance (F g−1) | Ref (year) |
---|---|---|---|---|
FeOOH nanoparticles | 1 M Li2SO4 | − 0.85 to − 0.1 V | 148 at 0.5 A g−1 | [16] (2014) |
FeOOH nanorods | 1 M Li2SO4 | − 0.85 to − 0.1 V | 116 at 0.5 A g−1 | [17] (2008) |
FeOOH@MnO2 core-shell | 1 M LiOH | − 0.15 to 0.6 V | 178.6 at 0.1 A g− 1 | [18] (2017) |
Porous flower-like Fe2O3 | 0.5 M Na2SO3 | − 0.8 to 0 V | 127 at 1 A g−1 | [19] (2013) |
Fe2O3 sheets | 1 M Li2SO4 | − 0.8 to − 0.2 V | 147 at 0.36 A g−1 | [20] (2014) |
Fe3O4 nanosheets/carbon nanofibers | 1 M Na2SO3 | − 0.9 to 0.1 V | 127 at 10 mV s−1 | [21] (2011) |
Diatomite@FeOOH | 1 M Na2SO4 | − 1 to 0 V | 157.9 at 0.5 A g−1 | This work |