Abstract
FeOOH nanosheets on porous diatomite have been successfully prepared by a facile two-step hydrothermal approach for supercapacitors, and then α-Fe2O3 and γ-Fe2O3 nanostructures are obtained via calcination under different atmospheres and temperatures. The morphologies and structures of all the samples are investigated in detail to make the hierarchical architecture clear. Besides, systemic tests are carried out in 1 M Na2SO4 electrolyte to characterize the electrochemical properties of these materials. Among the iron-related composite electrodes, diatomite@FeOOH owns the highest specific capacitance (157.9 F g−1 at a current density of 0.5 A g−1) and best cycling performance (98.95% retention after 1000 cycles), which is considered to be a potential material for high-performance supercapacitors. Furthermore, the synthesizing strategy can be extended to the preparation of other metallic oxide-derived functional materials towards energy storage and conversion.
Background
Up to now, major challenges for supercapacitor technologies include low-energy density and high production cost. Some research efforts have been devoted to improving its disadvantages [1]. Some transition metal oxides or hydroxides, such as MnO2 [2,3,4], FeOOH [5], NiO [6], and CuO [7], are regarded as potential candidates for active electrode materials. Among these transition metal oxides, ferric oxides/hydroxides have drawn considerable attention due to their nature abundance, variable oxidation states and environmental friendliness [8,9,10]. Besides, ferric oxides/hydroxides have been considered as especially desirable electrode materials for supercapacitors because its structure (like tunnel-type FeOOH) can accelerate ion transport. However, ferric oxides/hydroxides still own two major obstacles (small surface area and low electro-conductivity). Nanostructures can change the obstacles and provide enormous advantages in energy storage system, which are considered to be high charge-discharge rates by accelerating high specific surface areas, fast redox reactions, and short diffusion paths for electrons and ion [11]. Nevertheless, researches indicated that ferric oxide nanostructures had a tendency to get aggregate and transform into large particles causing a severe loss of specific surface area, which has a seriously terrible effect on electrochemical properties [12]. Therefore, the primary issue currently is to find a simple and feasible way to effectively disperse the nanostructures of ferric oxides, such as fabricating ferric metal oxides on the surface of porous templates.
As an important natural porous nanomaterial, diatomite is an attractive porous template on account of its high porosity, low-volume density, stable chemical property, and large specific area [13,14,15]. Diatomite template can increase the low surface area and avoid aggregation of nanostructures. Until now, despite that the characteristics of their structures are obvious and promising, ferric oxides/hydroxides-based diatomite composites to form a hierarchically porous structure have rarely yet to be studied in supercapacitors.
In this paper, we report successful fabrication of ferric oxides/hydroxides on diatomite as supercapacitor electrode materials by an effective two-step hydrothermal approach. We aimed to use diatomite as a template to distribute evenly ferric oxide/hydroxide nanostructures on the diatomite surface, which solves the problem on how to effectively disperse its nanostructures and greatly improve the surface area and electrochemical properties of ferric oxides/hydroxides, as shown in Additional file 1: SI-5. Remarkably, with diatomite and ferric oxides/hydroxides’ synergistic effect, the final composite, diatomite@FeOOH, indicated promising electrochemical properties in supercapacitors.
Experimental Section
Materials Synthesis
All the chemical reagents were of analytical purity and used without any further purification. Synthetic processes are as follows (Fig. 1; more details in Additional file 1: SI-1).
Initially, the natural diatomite was purified via a simple oil bath method by the following procedures. Then, the MnO2-decorated diatomite were prepared by a hydrothermal method. Typically, the KMnO4 solution (30 mL, 0.05 M) was mixed with the purified diatomite (30 mg). Afterwards, the mixture was transferred into a Teflon-lined autoclave (50 mL) which was heat-treated at 160 °C for 24 h. The as-prepared diatomite was centrifuged, washed by distilled water and then dried at 60 °C. After that, MnO2-decorated diatomite was obtained.
In addition, a solution of FeSO4·7H2O (0.01 M, 30 mL) was applied towards totally transformation of the pretreated diatomite@MnO2 (30 mg) at 120 °C for 2 h. In the end, the different crystal forms (α-Fe2O3 and γ-Fe2O3) of ferric oxide-decorated diatomite were prepared by calcining at 350 °C for 2 h under O2 atmosphere and 500 °C for 2 h under N2 atmosphere, respectively.
Characterization
Focused ion beam scanning electron microscopy (Zeiss Auriga FIB/SEM) was employed for observing the morphologies. And the phase analysis and structure were established by powder X-ray diffraction (XRD; D/max 2500, Cu Kα).
Electrochemical Measurements
Electrochemical study on the materials in a three-electrode system: All the electrochemical properties of the as-obtained diatomite composites were characterized though a conventional three-electrode equipment filled with 1 M Na2SO4 electrolyte. Before the measurements, the working electrodes were formed with mixing active material (diatomite@MnO2, diatomite@FeOOH, diatomite@α-Fe2O3, and diatomite@γ-Fe2O3), acetylene black, and polyvinylidene fluoride (PVDF) at a weight ratio of 7:2:1 in N-methyl-2-pyrrolidone (NMP). The slurry was coated on pieces of foamed nickel foam (1 × 1 cm2), which was heated to evaporate the dissolvent (120 °C for 12 h). About 2 mg electrode material was loaded on the nickel foam. The electrochemical performances and capacitance values of the composites electrodes were characterized with cyclic voltammetry (CV), galvanostatic charging/discharging (CC) methods, and electrochemical impedance spectroscopy (EIS).
The specific capacitance (Cm) is calculated by the following equation:
where I is the discharging current, △t is the discharging time, △V is the potential window during discharging, and m is the weight of active materials.
Results and Discussion
Figure 2 presents SEM images of MnO2, FeOOH, and α-Fe2O3/γ-Fe2O3 nanoarrays on the diatomite. Figure 2a show the uniform and discrete MnO2 nanosheets (diatomite@MnO2) grown on the diatomite via a facile hydrothermal method. By virtue of acid treatment and calcination, MnO2 can combine with diatomite firmly by the interaction force, which facilitates reactions between MnO2 and Fe2+. Meanwhile, plenty pores of diatomite increase the diffusion of ions. Figure 2b exhibits diatomite@FeOOH have similar morphology compared with MnO2 arrays. Indeed, MnO2 is reduced by Fe2+ ions, and Fe2+ ions in solution take the place of Mn. In addition, the pretreatment for stabilization of the crystal MnO2 and the assistance of ethylene glycol probably generate the similar nanosheets morphology. The size of α-Fe2O3 nanosheets (Fig. 2c) is bigger, and the distance between the sheets is larger under the same high-magnification condition, compared with that of γ-Fe2O3 (Fig. 2d). The morphology of the samples in low magnification can be seen in Additional file 1: SI-2(a–d). Additionally, Additional file 1: SI-2(e, f) exhibit the corresponding EDS mappings of diatomite@MnO2 and diatomite@Fe2O3 and further prove the existence of convictive elements (Mn, Fe, and O), confirming the formation of MnO2 and Fe2O3 nanosheets. Besides, Additional file 1: SI-2(f) shows that there is no Mn element existing in the FeOOH loaded on diatomite, indicating that the MnO2 nanosheets were totally transferred into iron hydroxides.
XRD patterns of the as-obtained samples are exhibited in Fig. 2e to confirm the phase composition and structure of the products. It is noted that the strongest peaks of the four samples marked with dot symbol in all the curves are the characteristic peaks of diatomite substrate. The diatomite@MnO2 sample showed diffraction peaks at 2θ = 12.784°, 25.711°, and 37.522°, corresponding to the (110), (220), and (211) crystal planes (JCPDS card no. 44-0141). As for FeOOH nanosheet arrays, three diffraction peaks of the MnO2 disappear in the red curve, while a few well-defined diffraction peaks are well consistent with the standard XRD pattern of FeOOH (JCPDS card no. 29-0713), matching with the (130), (021), (111), (121), (140), (221), (151), and (002) plane. The XRD results of the ferric oxide/hydroxide samples show that the MnO2 peaks disappeared and reveal that there are no MnO2 nanosheets existing. Therefore, both EDS mapping and XRD results reveal that MnO2 is completely replaced by Fe2+ ions in this work. Moreover, the diffraction peaks of α-Fe2O3 are weaker than that of γ-Fe2O3 about 24.138° and 62.449°, assigned to the (012) and (214) planes of hematite-type ferric oxide crystal (both are JCPDS card no. 33-0664). It confirms again that the replacement between MnO2 and Fe2+ ions successfully occur at the interfaces of the diatomite and solution.
To investigate the electrochemical properties of the four samples, a three-electrode system was carried out in 1 M Na2SO4 aqueous electrolyte. The differences in morphologies and structures of these four samples can lead to diverse electrochemical performances. Diatomite served as a substrate contributes to efficient transport of ions owing to its porous structures.
As shown in Additional file 1: SI-3(a, b), the CV and CC curves of diatomite@MnO2 electrode are quasi-rectangular and nearly symmetrical triangular, respectively. There are no distinct redox peaks, which deviates from the ideal rectangle manifesting faradic pseudocapacitive nature of the electrode. As revealed in Additional file 1: SI-3(c, d), diatomite@FeOOH has the better capacitive properties than other two samples (diatomite@α/γ-Fe2O3). The specific capacitance of diatomite@FeOOH electrodes is about 157.9 F g−1 at a current density of 0.5 A g−1, demonstrating that the highly porous structure can transfer more ions into its surface and can promote more redox faradic reactions. Agreeing with the SEM results, the distances of α-Fe2O3 nanosheets are so large that the surface of active material make less use of the cations, while γ-Fe2O3 can provide the smallest specific area for ions among the three ferric oxide samples. Therefore, the distance of the nanosheets of the samples is very important. Besides, as showed in Table 1, the diatomite@FeOOH electrode in this work has a higher specific capacitance among these ferric oxide/hydroxide-based electrodes compared with previous work.
Such being the case, systematic tests are carried out to better investigate the electrochemical properties of diatomite@FeOOH electrode. Figure 3a shows typical CV curves of FeOOH sample in potential range from − 1 to 0 V at different scan rates. Galvanostatic charge-discharge curves of diatomite@FeOOH electrode at different current densities are presented in Fig. 3b. The shape of CV and CC curves of diatomite@FeOOH electrode demonstrates the pseudocapacitance characteristics of diatomite@FeOOH. Figure 3c further illustrates the relationship between specific and current density. The cycling ability of diatomite@FeOOH electrode was subjected to a long-cycle test for consecutive 1000 cycles (Fig. 3d), and capacity retention after 1000 cycles is about 98.95%. The CC curves of the last 10 cycles suggest no major structure variation during the charge-discharge processes. Additionally, the Nyquist plots for the FeOOH sample electrode (Additional file 1: SI-4) contain a semicircle in the high-frequency boundary and a straight line in the low-frequency range. The internal resistance (Rs) of the electrode is about 3.0 Ω and 3.5 before and after 1000 cycles without much variation, while the charge-transfer resistance (Rct) is about 1.2 and 4.0 Ω before and after 1000 cycles. These findings could be responsible for the good electrochemical properties of the diatomite@FeOOH electrode.
Conclusions
In summary, we prepare ferric oxides-decorated diatomite combined with a subsequent replacement process by a facile and effective hydrothermal approach. These ferric oxides/hydroxides own finely controlled morphologies and nanosheet structures. Diatomite@FeOOH material exhibits promising electrochemical properties, which is superior to the other ferric oxide materials. The specific capacitance of diatomite@FeOOH is 157.9 F g−1 at a current density of 0.5 A g−1, and its cycle performance is good (98.95% retention after 1000 cycles). Actually, the hierarchical and porous diatomite@FeOOH could be a promising active material for supercapacitors. Furthermore, such synthesizing strategy can be extended to the preparation of other metallic oxide-derived functional materials towards energy storage and conversion.
Abbreviations
- CC:
-
Galvanostatic charging/discharging
- CV:
-
Cyclic voltammetry
- EIS:
-
Electrochemical impedance spectroscopy
- FIB/SEM:
-
Focused ion beam scanning electron microscopy
- NMP:
-
N-methyl-2-pyrrolidone
- PVDF:
-
Polyvinylidene fluoride
- XRD:
-
Powder X-ray diffraction
References
Liu C, Li F, Ma LP, Cheng HM (2010) Advanced materials for energy storage. Adv Mater 22(8):E28–E62
Huang M, Zhang Y, Li F, Zhang L, Ruoff RS, Wen Z, Liu Q (2014) Self-assembly of mesoporous nanotubes assembled from interwoven ultrathin Birnessite-type MnO2 nanosheets for asymmetric supercapacitors. Sci Rep 4(4):3878
Zhu SJ, Li L, Liu JB, Wang HT, Wang T, Zhang YX, Zhang LL, Ruoff RS, Dong F (2018) Structural directed growth of ultrathin parallel Birnessite on β-MnO2 for high-performance asymmetric supercapacitors. ACS Nano 12(2):1033–1042
Guo XL, Wang T, Zheng TX, Xu CH, Zhang JT, Zhang YX, Liu XY, Dong F (2018) Quasi-parallel arrays of 2D-on-2D structure for electrochemical supercapacitors. J Mater Chem A. https://doi.org/10.1039/c8ta07869f
Liu J, Zheng M, Shi X, Zeng H, Xia H (2016) Amorphous FeOOH quantum dots assembled mesoporous film anchored on graphene nanosheets with superior electrochemical performance for supercapacitors. Adv Funct Mater 26(6):919–930
Lee WJ, Ahn T, Kim JH, Ko JM, Kim JD (2011) Nanosheets based mesoporous NiO microspherical structures via facile and template-free method for high performance supercapacitors. Electrochim Acta 56(13):4849–4857
Zhang YX, Huang M, Kuang M, Liu CP, Tan JL, Dong M, Yuan Y, Zhao XL, Wen Z (2013) Facile synthesis of mesoporous CuO nanoribbons for electrochemical capacitors applications. Int J Electrochem Sci 8(1):1366–1381
Yang P, Ding Y, Lin Z, Chen Z, Li Y, Qiang P, Ebrahimi M, Mai W, Wong CP, Wang ZL (2014) Low-cost high-performance solid-state asymmetric supercapacitors based on MnO2 nanowires and Fe2O3 nanotubes. Nano Lett 14(2):731
Chen LF, Yu ZY, Ma X, Li ZY, Yu SH (2014) In situ hydrothermal growth of ferric oxides on carbon cloth for low-cost and scalable high-energy-density supercapacitors. Nano Energy 9(9):345–354
Lu XF, Chen XY, Zhou W, Tong YX, Li GR (2015) α-Fe2O3@PANI core-shell nanowire arrays as negative electrodes for asymmetric supercapacitors. Acs Appl Mater Inter 7(27):14843
Shivakumara S, Penki TR, Munichandraiah N (2014) High specific surface area α-Fe2O3 nanostructures as high performance electrode material for supercapacitors. Mater Lett 131:100–103
Ma Z, Huang X, Dou S, Wu J, Wang S (2014) One-pot synthesis of Fe2O3 nanoparticles on nitrogen-doped graphene as advanced supercapacitor electrode materials. J Phys Chem C 118(31):17231–17239
Yu Y, Addaimensah J, Losic D (2010) Synthesis of self-supporting gold microstructures with three-dimensional morphologies by direct replication of diatom templates. Langmuir 26(17):14068–14072
Losic D, Mitchell JG, Lal R, Voelcker NH (2010) Rapid fabrication of micro- and nanoscale patterns by replica molding from diatom biosilica. Adv Funct Mater 17(14):2439–2446
Sun XW, Zhang YX, Losic D (2017) Diatom silica, an emerging biomaterial for energy conversion and storage. J Mater Chem A 5(19):8847–8859
Long C, Jiang L, Wei T, Yan J, Fan Z (2014) High-performance asymmetric supercapacitors with lithium intercalation reaction using metal oxide-based composites as electrode materials. J Mater Chem A 2(39):16678–16686
Jin WH, Cao GT, Sun JY (2008) Hybrid supercapacitor based on MnO2 and columned FeOOH using Li2SO4 electrolyte solution. J Power Sources 175(1):686–691
Yang J, Wang H, Wang R (2017) Facile synthesis of core–shell FeOOH@MnO2 nanomaterials with excellent cycling stability for supercapacitor electrodes. J Mater Sci Mater El 28(9):6481–6487
Shivakumara S, Tirupathi Z, Rao P, Munichandraiah N (2013) Synthesis and characterization of porous flowerlike-Fe2O3 nanostructures for supercapacitor application. Ecs Electrochem Lett 2(7):A60–A62
Huang J, Yang S, Xu Y, Zhou X, Jiang X, Shi N, Cao D, Yin J, Wang G (2014) Fe2O3 sheets grown on nickel foam as electrode material for electrochemical capacitors. J Electroanal Chem 713(3):98–102
Mu J, Chen B, Guo Z, Zhang M, Zhang Z, Zhang P, Shao C, Liu Y (2011) Highly dispersed Fe3O4 nanosheets on one-dimensional carbon nanofibers: synthesis, formation mechanism, and electrochemical performance as supercapacitor electrode materials. Nanoscale 3(12):5034–5040
Acknowledgements
The authors gratefully acknowledge the financial support provided by the National Natural Science Foundation of China (Grant no. 21576034), the State Education Ministry and Fundamental Research Funds for the Central Universities (106112017CDJXSYY0001, 2018CDYJSY0055, 106112017CDJQJ138802, 106112017CDJXSYY0001, 106112017CDJSK04XK11, and 2018CDQYCL0027), and the Innovative Research Team of Chongqing (CXTDG201602014). MHW and XYZ thank the support of the National Undergraduate Training Program for Innovation and Entrepreneurship (201710611052). The authors would like to extend special thanks to Ms. Qian Chen of Chongqing University for language polishing. The authors also thank the Electron Microscopy Center of Chongqing University for material characterizations.
Availability of Data and Materials
All datasets are presented in the main paper or in the additional supporting files.
Author information
Authors and Affiliations
Contributions
PG and YXZ designed the experiments and conducted all results. MHW, KLL, and XYZ participated in the experiment and prepared the manuscript including discussion of the results. DBJ and XYL analyzed and processed the dates and helped modify the manuscript. JLG and DNW helped to do basic operations of experiments under KLL’s supervision. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional File
Additional file 1:
Experimental section. Figure S1. The SEM images of the samples in low magnification. Figure S2. (a) CV and (b) CC curves of the diatomite@MnO2 in 1 M Na2SO4; (c) CV and (d) CC curves of three kinds of ferric oxides-decorated diatomite. Figure S3. The EIS curve of Diatomite@FeOOH. Figure S4. The CV (a) curves at 100 mV s−1 and CC (b) curves at 1 A g−1 of diatomite, FeOOH and D@FeOOH. (DOC 22468 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Wu, M.H., Li, K.L., Zhang, X.Y. et al. Tuning Hierarchical Ferric Nanostructures-Decorated Diatomite for Supercapacitors. Nanoscale Res Lett 13, 407 (2018). https://doi.org/10.1186/s11671-018-2822-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2822-9