Table 2 Lattice parameters of the PbTiO3 powders synthesized by template MSS method*

From: Structural Characterizations and Dielectric Properties of Sphere- and Rod-Like PbTiO3 Powders Synthesized via Molten Salt Synthesis

Temperature (°C) Reaction time (h) Molar ratio of PbC2O4:TiO2:NaCl:KCl in template MSS method
1:1:20:20 1:1:60:60
a (nm) c (nm) c/a a (nm) c (nm) c/a
800 1 0.3906 0.4107 1.051 0.3906 0.4101 1.05
800 5 0.3908 0.4100 1.049 0.3907 0.4095 1.048
800 10 0.3907 0.4101 1.050 0.3905 0.4100 1.050
  1. *The rod-like TiO2 templates annealed at 800 °C for 1 h with anatase phase structure were used as the titanium source in the template MSS process