Table 1 A comparison of the characteristics of various MoS2 or PANI for supercapacitors
Electrode materials | Electrolyte | Specific capacitances | Capacity retention rates | Ref. |
---|---|---|---|---|
CNTs|MoS2 | 1 M Na2SO4 | 74.05 F/g at 2 A/g | 81% after 1000 cycles | [56] |
Tubular C|MoS2 | 3 M KOH | 210 F/g at 1 A/g | 105% after 1000 cycles | [18] |
CNTs|PANI | 1 M H2SO4 | 113.64 F/cm2 at 1 mA | 90.2% after 1000 bending cycles | [28] |
MoS2|rGO|Ti mesh | PVA-1 M NaCl | 17.6 mF/cm2 at 10 mV/s | – | [35] |
MoS2|Mo | 1 M Na2SO4 | 192.7 F/g at 1 mA/cm2 | 98% after 1000 cycles | [54] |
MoS2|SiO2 | 2 M KOH | 683 F/g at 1 A/g | 85% after 10,000 cycles | [39] |
MoS2 nanosheets | 1 M Na2SO4 | 129.2 F/g at 1 A/g | 85% after 500 cycles | [40] |
1D PANI|2D MoS2 | 1 M Na2SO4 | 485 F/g at 1 mA/cm2 | – | [51] |
MS1MWCN1 | 0.5 M Na2SO4 | 255.8 F/g at 1 A/g | 95.02% after 500 cycles | This work |
PANI|MWCNTs | 0.5 M Na2SO4 | 267.49 F/g at 1 A/g | 94.5% after 500 cycles | This work |
Quasi-solid-state MM//PM | PVA-Na2SO4 | 138.13 F/g at 1 A/g | – | This work |