Synthesis and Characterization of Nanoscale Tungsten Particles with Hollow Superstructure Using Spray Drying Combined with Calcination Process

  • 1Email author,
  • 2,
  • 1,
  • 1,
  • 1,
  • 1 and
  • 2
Nanoscale Research Letters201914:68

https://doi.org/10.1186/s11671-019-2904-3

  • Received: 2 October 2018
  • Accepted: 18 February 2019
  • Published:

Abstract

Nanoscale tungsten (W) powder is used in some special materials. In this study, a hollow superstructure W powder consisting of nanoparticles was synthesized by spray drying combined with two-step calcination from commercial (NH4)6W7O24·6H2O. The high-pressure gas (HPG) was the significant factor in spray drying process, which affect the BET surface area and average particles size of the spray-dried powders. The detailed influences of calcined steps and calcination temperature in the microstructure and average particles size of final W particles were investigated. The size distribution of as-synthesized nanoscale W particles with hollow superstructure was from 40 to 200 nm, and the average size was about 100 nm. The as-synthesized W powder shows good sintering properties. It should be noted that the powder technology in this study can be used to synthesize other powders with high-performance requirements.

Graphical abstract

.
Graphical Abstract image

Keywords

  • Nanoscale tungsten powders
  • Hollow superstructure
  • High-pressure gas
  • Two-step calcination
  • Sinter

Introduction

Tungsten (W) metal is widely used in daily life and modern industry because of its outstanding properties involving high melting point, high thermal conductivity, excellent mechanical properties at elevated temperatures, low sputtering yield, good mechanical strength, low tritium retention, and high erosion resistance [14]. The applications of W metal are also rapidly expanding in the account of increasing development of science and technology. Normally, W powders as raw material are selected to prepare products by powder metallurgical techniques, such as hot pressing (HP), hot isostatic pressing (HIP), and spark plasma sintering (SPS), so the performance of W particles is one of the critical factors to affect the properties of W products [57]. In general, there are many high requirements in W powders for preparing different products, such as the average particle size, distribution of particle size, surface area, and microstructure [8]. Many methods have been developed to synthesize W powders. Ren et al. [9] synthesized W particles with irregular morphology and very fine particle size of about 50 nm W by high-energy planetary milling. Tungsten compacts with relative density of 98.3% were achieved by the two-step sintered of W nanoparticles. Ryu et al. [10] prepared W powders with particle size less than 30 nm in a thermal plasma reactor. The relative density of W compact by sintered nanoscale W particles at 1400 °C was about 92%, while a lower relative density of about 72% was obtained by using micro-sized W particles. To develop high relative density tungsten compacts, suitable nanoscale W particles are desirable.

Compared with micro-sized W particles, nanoscale W particles have excellent superiorities due to their higher surface area and smaller grain, which can be sintered to W compacts with high relative density in relatively low temperature and low pressure [912]. Some methods of preparing nano-sized W particles were reported, including hydrogen reduction, sol-gel, and high-energy ball milling, and a plenty of useful data was obtained from previous study [915]. However, these techniques for synthesizing W nanoparticles still have some disadvantages, such as the multi-step high-temperature reduction process, burning of much energy, and using of expensive raw precursors. Hence, it is necessary to find an effective approach for preparing nano-sized W powder to achieve W sintered bodies with high relative density.

Spray drying technique is developed to be a clean, rapid, reproducible, low-cost, and easily scaled-up method to produce spherical nanoscale particles due to instantaneous transition between liquid (solvent) and solid (solute) phases [1622]. Spray drying method compared with other drying techniques is widely used in industrial milling [16, 20]. It can synthesize sub-5 μm hollow and near-spherical superstructure particles consisted of nanoscale particles by self-assembly [16, 18]. During the process of spray drying, the solution (solute-solvent) is completely atomized and dispersed into chamber (hot gas) when interacted with the high-pressure gas at the nozzle. Afterward, fogdrops atomized are evaporated in the drying chamber and spherical or near-spherical solid particles are formed simultaneously [17, 22]. The particles prepared by spray drying have high dispersibility, good sphericity, and homogeneity. Moreover, different particle size distribution and microstructure of particles atomized can be obtained by controlling spray drying parameters [16, 18, 20, 22, 23]. In our previous study, high-performance ruthenium, micro-spherical tungsten-molybdenum alloy, and ruthenium compound particles were achieved by the spray drying process [2123]. Therefore, the spray drying method can be chosen to synthesize nanoscale spherical W particles by optimizing spray drying parameters.

In this work, a systematic investigation was presented on the synthesis of nano-sized W particles with hollow superstructure by spray drying method combined with hydrogen reduction using ammonium paratungstate [(NH4)6W7O24·6H2O] as raw material. The influences of process parameters, including high-pressure gas of spray drying, heating rate of ignition, and reduction temperature, were discussed. The W compacts prepared by nano-sized W particles were also studied. To the best of our knowledge, there is no report on the synthesis of nano-sized W particles with hollow superstructure. The purpose of this research is to acquire the synthesis mechanism of nanoscale spherical particles with hollow superstructure and determine the best parameters by the investigation of parameters of spray drying and calcination process.

Materials and Methods

Commercially available (NH4)6W7O24 ·6H2O powder was purchased from Xiamen Tungsten Co. Ltd. (Xiamen, Fujian, People’s Republic of China). The deionized water was used as the solvent, and all reagents and solvents were used as received without further purification. The (NH4)6W7O24·6H2O powder as a solute was dissolved in deionized water, and the solution was heated from room temperature to 80 °C for promoting dissolution. Then, the (NH4)6W7O24 solution with a certain concentration was obtained. The solution was atomized to micro-spherical particles by spray drying equipment with the optimizing parameters. Subsequently, the spray-dried (NH4)6W7O24 powder was ignited by two different calcined processes (the one-step direct calcination and the two-step calcination). Spray-dried (NH4)6W7O24 particles were heated to 800 °C for 60 min with the heating rate of 5 °C/min in N2/H2 (vol 5:5), which obtained cubic polyhedron W particles in the one-step calcination. The nanoscale near-spherical W particles with hollow superstructure were synthesized by the two-step calcination. The temperature went up to 650 °C for 20 min followed by cooling. Then, the temperature was reheated up to 700 °C for 120 min (heating rate of 5 °C/min in N2/H2 (vol 5:5)). As-synthesized W powder (two-step calcination) was uni-axially compacted to form pellets (10 mm diameter, about 4 mm height) under a pressure of 120 MPa without adding any external lubricant. The compact was sintered under H2 atmosphere for 2 h at 1400 °C (heating rate 20 °C/min).

A commercial spray drying equipment (B290, Buchi, Switzerland) was used to synthesize micro-spherical (NH4)6W7O24·6H2O particles. The solid phases in different stages were characterized by X-ray diffraction (XRD, Empyrean, PANalytical, the Netherlands, CuKα radiation at 40 kV). The microstructure of (NH4)6W7O24·6H2O particles and thermally decomposed products were observed by field emission scanning electron microcopy (FESEM, S-4800, Hitachi, Japan) and transmission electron microscopy (TEM, G2 20 200kV Tecnai). The average particle size, size distribution, and specific surface area of the as-prepared (NH4)6W7O24 powder were measured by the laser particle size analyzer (Mastersizer3000, Malvern, UK) and surface area instrument (Tristar II, Micromeritics, USA), respectively. The density of the sintered specimen was measured by Archimedes method. The hardness of as-sintered W specimen was measured by Vickers hardness tester (VMHT Auto, Leica, Germany).

Results and Discussion

The microstructure of commercial (NH4)6W7O24·6H2O powder is presented in Fig. 1a. A lot of blocks composed of irregular micro-sized polyhedra can be observed. It is difficult to obtain near-spherical W powder with hollow superstructure consisted of nanoscale particles by direct ignition reduction with untreated (NH4)6W7O24·6H2O. So, the modification of microstructure of (NH4)6W7O24·6H2O is quite essential for the next step. The XRD pattern of untreated (NH4)6W7O24·6H2O is shown in Fig. 1b. All observed diffraction peaks observed can be matched in the International Centre for Diffraction Data (formerly Joint Committee on Powder Diffraction Standards JCPDS 7-240 database). So, the purchased powder is identified as (NH4)6W7O24·6H2O [24].
Fig. 1
Fig. 1

The microstructure (a) and XRD pattern (b) of commercially available (NH4)6W7O24·6H2O powders, or (a) the microstructure of commercially available (NH4)6W7O24·6H2O powders, and (b) the XRD pattern commercially available (NH4)6W7O24·6H2O powders

The detailed schematic of particles formed in spray drying is shown in Fig. 2i. The solution and high-pressure gas interact at the nozzle zone due to their high relative speed. Then, the solution is crashed into a lot of small fogdrops in the drying chamber. Subsequently, the atomized fogdrops are instantaneously dried to micro-sized spherical solid particles. The specific process of fogdrops transformation in the drying chamber is observed in Fig. 2ii. At the beginning, the volume of fogdrops became small because of evaporation of solvent (deionized water) from the surface of droplets, to increase the concentration of solute at fogdrops surface. Then, the solute starts to be separated out, forming solid (NH4)6W7O24 in the exterior of fogdrops. The volume of the fogdrops ceased to change when the concentration of solute at fogdrops surface reached saturation. After that, a shell formed on the surface of the fogdrops where the interior solute constantly formed into solid (NH4)6W7O24. The internal water vapor escaped from the shell to produce numerous nano-sized capillary pores which were hard to be observed. Finally, the micro-sized hollow spherical particles were obtained.
Fig. 2
Fig. 2

The schematic of spray drying process. i The detailed schematic of formed process of particles. ii The specific process of transformation of droplets

The microstructures of the (NH4)6W7O24 particles atomized by spray drying method are shown in Fig. 3a, in which nearly spherical and submicron particles are observed. There are numerous concaves on the surface of the sphere while the broken sphere is almost observed even in a miniscule amount in Fig. 3b. The detailed schematic of collisions between particles in Fig. 3c can provide a clue as to why the particles contain concaves and breaks. According to Fig. 3c, it is indicated that a large number of particles in the drying chamber can collide with each other due to the high-speed particles produced by high-pressure gas, and the main collision pattern is the bounced off each other resulted formation of concaves while the rare non-bounced collision causes the fracture of the sphere surface. The XRD pattern of spray-dried (NH4)6W7O24·6H2O is shown in Fig. 3d. Obviously, the amorphous peaks are observed, which indicates that the spray-dried particles are completely noncrystalline substance. It is quite likely because a very short drying time (approximately 0.2 s) of each fogdrops cannot provide enough time for crystallization.
Fig. 3
Fig. 3

The microstructure and XRD pattern of spray-dried (NH4)6W7O24·6H2O particles. a, b The morphology of the (NH4)6W7O24·6H2O particles atomized by spray drying method. c The schematic of collision between particles. d The XRD pattern of spray-dried (NH4)6W7O24·6H2O powder

The microstructures of spray-dried (NH4)6W7O24 particles in different high-pressure gas (HPG) are shown in Fig. 4, where significantly different microstructures of (NH4)6W7O24 particles are observed. The BET surface area and average particle size of as-prepared (NH4)6W7O24 powders are also presented in Fig. 4. During spray drying, the HPG as another critical parameter which can influence the microstructure and particle size distribution was investigated, and the drying temperature, solution concentration, and gas/liquid rates were studied in our previous work [21, 22]. In this part of the experiment, the drying temperature, solution concentration, and gas/liquid rates were controlled at 210 °C, 0.01 mol/L and 5 nL/5 mL, respectively. When the HPG was 150 L/min, submicron nearly spherical (NH4)6W7O24 particles without any agglomeration were obtained (Fig. 4a). The BET surface area and average particle size (in Fig. 4e, f) were circa 0.5 m2/g and 8.3 μm, respectively. The distribution range of particle size distribution was quite large (Fig. 4a). When the HPG got to 200 L/min, the surface features were almost the same as that at 150 L/min. However, the BET surface area and average particle size were about 2.1 m2/g and 3.8 μm, respectively, which were obviously different from those at 150 L/min. The distribution range of particles size distribution was declined slightly, as shown in Fig. 4b, e, and f. In Fig. 4c, e, and f, when the HPG went up to 250 L/min, the characteristics of particles were changed except the surface features. And the BET surface area increased to about 5.1 m2/g, the average particle size reduced to approximately 2.1 μm, and the range of particles size distribution became very narrow. When the HPG reached the maximum value of the spray drying device (300 L/min), the concaves on the exterior of particles were noticeably reduced (Fig. 4d). The BET surface area and average particle size were about 6.8 m2/g and 0.9 μm, respectively. The range of particles size distribution range was quite small as shown in Fig. 4 e, f.
Fig. 4
Fig. 4

The microstructure of spray-dried (NH4)6W7O24·6H2O particles in different high-pressure gas. a 150 L/min. b 200 L/min. c 250 L/min. d 300 L/min. e BET surface area. f Average particle size

The HPG is one of the most important factors in atomization process, which can influence the BET surface area and average particle size of spray-dried particles. When the HPG was 150 L/min, the (NH4)6W7O24 solution at the nozzle was not sufficiently crashed into micro-sized fogdrops by HPS owing to the low relative speed between solution and HPG. As a result, the dried powders had larger average particles size and lower BET surface area (Fig. 4a, e, f). On the other hand, when the HPG was adjusted to the largest (300 L/min), the solution of (NH4)6W7O24 was completely transformed into ultrafine fogdrops because of a high relative speed between them, so the spray-dried particles had a small average size (0.9 μm) and a large BET surface area (6.8 m2/g), as shown in Fig. 4d, e, f. Consequently, the larger average (NH4)6W7O24 particles with lower BET surface area could be acquired by using a small HPG. The result could be the opposite when the HPG were larger.

In this work, spray-dried (NH4)6W7O24 particles (HPG was 300 L/min) were calcined by two different reduction calcination processes. The one-step direct calcination was carried out, as shown in Fig. 5a. The microstructures of W particles are presented in Fig. 6a, in which cubic polyhedron W particles with average size of 1.6 μm are observed. On the one hand, the nanoscale near-spherical W particles with hollow superstructure cannot be obtained by one-step direct calcination. On the other hand, the two-step calcination was illustrated in detail in Fig. 5b. The microstructures of W powders are shown in Fig. 6b, and the hollow superstructure W consisting of nanoparticles are observed in the insert of Fig. 6b. The TEM photographs of W nanoparticles are shown in Fig. 6c. The near-spherical particles are observed, and the average particle size is about 100 nm. The lattice structure and the diffraction pattern of nano-sized W particles are observed in Fig. 6d, and the interplanar spacing of nano-sized W was determined to be about 0.22 nm. According to the interplanar spacing and the diffraction pattern in the illustration of Fig. 6d, it is confirmed that the nanosized particles are single-crystal W [25].
Fig. 5
Fig. 5

The two different reduction calcination processes of spray-dried (NH4)6W7O24·6H2O particles. a One-step direct calcination. b Two-step calcination

Fig. 6
Fig. 6

Characterization of W powders. a Microstructure of W particles prepared by one-step calcination. b Microstructure of W particles prepared by two-step calcination. c TEM image of W particles with particle size distribution by two-step calcination and d HRTEM image of W particles with SAED pattern inset by two-step calcination

The different results of W particles were caused by two different calcined processes. In the one-step direct calcination process, when the temperature was heated to 650 °C, the new W-phase was generated and weak, as shown in Fig. 7a. The newborn W particles were easily agglomerated due to their high activity and energy. When the temperature continued to rose up to 800 °C, the W particles grew up rapidly. It should be noted that WOx is easy to sublimate at 720 °C or higher temperature [26], and WOx sublimation can promote W shift to fall on the newly formed W particles, which lead to the growth of W particles. As a result, the lager W particles with an average size of 1.6 μm were obtained (in Fig. 6a).
Fig. 7
Fig. 7

The XRD pattern and microstructure of products. a The XRD pattern of intermediates in one-step direct calcination at 650 °C. b The XRD pattern of intermediates in two-step calcination in second heating at 650 °C for 20 min. c The XRD pattern of final W powder in two-step calcination. d The microstructure of final W powder in two-step calcination

In the two-step calcination process, the detailed formation mechanism of hollow W nanoparticles is shown in Fig. 8. Firstly, when the temperature was heated to 650 °C for 20 min followed by cooling, spray-dried (NH4)6W7O24 decomposed to NH3, H2O, and intermediates (WO2, WO2.83, W). The newborn W had low activity and energy because of cooling, which had a restriction on the growth of W particles. When the intermediates were reheated to 650 °C, the W particles started to increase slightly because of a few WOx sublimated, and the XRD patterns of intermediate products are shown in Fig. 7b. When the temperature of reduction calcination was increased to 700 °C, the gases (N2/H2) were easy to enter into the pores between W nanoparticles, which could increase the reaction rate and contaction between gases and intermediates. The sublimated WOx decreased obviously at 700 °C due to the sublimation of WOx at 720 °C or higher temperature [26]; thus, the hollow superstructure W composing of W nanoparticles could be obtained. The XRD patterns and microstructure of the final W powders are presented in Fig. 7c and Fig. 7d, respectively.
Fig. 8
Fig. 8

The microstructural transformation mechanisms of spray dried (NH4)6W7O24·6H2O particles reduction calcination

As-synthesized W powder (two-step calcination) was sintered at 1400 °C. The microstructure of W compact is shown in Fig. 9, where uniform granular structure with polyhedral shapes and defined grain boundaries is observed. The density of as-sintered W specimen, 18.97 g/cm3, was obtained, and this corresponds to a relative density of 98.55% based on the tungsten theoretical density. Moreover, Vickers hardness of as-fabricated W compact was 384 ± 10 Hv. It is indicated that the W powder prepared by spray drying and two-step reaction has good sintering property.
Fig. 9
Fig. 9

The microstructure of the W compact

Conclusions

The hollow superstructure W powders composed of nanoparticles were synthesized by spray drying combined with two-step calcination from commercial (NH4)6W7O24·6H2O. The three-dimensional irregular polyhedral (NH4)6W7O24·6H2O was successfully turned into the micro-sized near-spherical particles by spray drying method, from which the high-pressure gas (HPG) was one significant factor to synthesized near-spherical (NH4)6W7O24 powders. When the HPG was 300 L/min, well near-spherical particles with a small average size (0.9 μm) and large BET surface area (6.8 m2/g) could be obtained. Different reduction calcination process had great influence on the microstructures of W particles. The cubic polyhedron W particles with average size of 1.6 μm were synthesized by one-step reduction calcination. In the two-step reduction calcination process, the hollow superstructure W composed of nanoparticles were obtained. The particle size distribution of as-synthesized W powders by two-step reduction calcination ranged from 40 to 200 nm, and the average particle size was about 100 nm. W target was acquired by sintering hollow superstructure W powders. The relative density and Vickers hardness were 98.55% and 384 ± 10 Hv, respectively. The as-synthesized W powder showed good sintering properties. The powder technology in this study can be applied to synthesize other powders with high-performance requirements.

Abbreviations

BET: 

Brunauer, Emmett and Teller

FESEM: 

Field emission scanning electron microcopy

HIP: 

Hot isostatic pressing

HP: 

Hot pressing

HPG: 

High-pressure gas

SAED: 

Selected area electron diffraction

SPS: 

Spark plasma sintering

TEM: 

Transmission electron microscopy

W: 

Tungsten

XRD: 

X-ray diffraction

Declarations

Acknowledgements

The research is supported by the fund of the National Natural Science Foundation of China (51864022), the fund of the State Key Laboratory of Advanced Technologyies for Comprehensive Utilization of Platinum Metals (SKL-SPM-2018011), the fund of the Science and Technology Project of Yunnan Province-New Products (2016BA001), and Shaanxi province innovative talent promotion program - young science and technology nova project(2018KJXX-055). The authors thank the facilities and technical assistance of Centre for Microscopy, Characterization & Analysis at the Northwest Institute For Non-ferrous Metal Research.

Funding

The research is supported by the fund of the National Natural Science Foundation of China (51864022), the fund of the State Key Laboratory of Advanced Technologyies for Comprehensive Utilization of Platinum Metals (SKL-SPM-2018011), the fund of the Science and Technology Project of Yunnan Province-New Products (2016BA001), and Shaanxi province innovative talent promotion program - young science and technology nova project(2018KJXX-055).

Availability of Data and Materials

It is provided by Northwest Institute For Non-ferrous Metal research and Kunming Institute of Precious Metals.

Authors’ Contributions

This article was written by PZ. PZ, WY, and QC gave ideas. The experiment has been done by BZ, KC, and PZ. The test was carried out by RD and JC. All authors read and approved the final manuscript.

Competing Interests

The authors declare that they have no competing interests.

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Authors’ Affiliations

(1)
Northwest Institute for Nonferrous Metal Research, Xian, 710000, China
(2)
State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming, 650106, China

References

  1. Sun WM, Yeung MT, Lech AT, Lin CW, Lee C, Li TQ, Duan XF, Zhou J, Kaner RB (2015) High surface area tunnels in hexagonal WO3. Nano Lett 15:4834–4838. https://doi.org/10.1021/acs.nanolett.5b02013 View ArticleGoogle Scholar
  2. Zhu HB, Tan DQ, Li YL, Yang X, He W (2015) Refining mechanisms of arsenic in the hydrogen reduction process of tungsten oxide. Adv Powder Technol 26:1013–1020. https://doi.org/10.1016/j.apt.2015.04.007 View ArticleGoogle Scholar
  3. Wang SL, He YH, Liu XL, Zhang Q, Zou J, Huang H, Song M, Huang BY, Liu CT, Du Y (2011) Large-scale synthesis of tungsten single-crystal microtubes via vapor-deposition process. J Cryst Growth 316:137–144. https://doi.org/10.1016/j.jcrysgro.2010.10.222 View ArticleGoogle Scholar
  4. Mandal P, Das B, Raychaudhuri AK (2016) Stability of a current carrying single nanowire of tungsten (W) deposited by focused ion beam. Journal of Applied Physics. 119:084301. DOI: https://doi.org/10.1063/1.4942164
  5. Erdoğan M, İshak K (2010) Electrochemical reduction of tungsten compounds to produce tungsten powder. Metallurgical Mater Trans B 41:798–804. https://doi.org/10.1007/s11663-010-9374-4 View ArticleGoogle Scholar
  6. Amitava M, Kim S, Kim SG, Park SJ, German RM, Horstemeyer MF (2010) Investigation on sintering mechanism of nanoscale tungsten powder based on atomistic simulation. Am Inst Physics 58(11):3939–3951. https://doi.org/10.1063/1.3457516 View ArticleGoogle Scholar
  7. Sarkar R, Ghosal P, Premkumar M, Singh AK, Muraleedharan K, Chakraborti AT, Bagchi P, Sarma B (2013) Characterisation and sintering studies of mechanically milled nano tungsten powder. Powder Metall 51:166–170. https://doi.org/10.1179/174329008X284787 View ArticleGoogle Scholar
  8. Kurishita H, Matsuo S, Arakawa H, Sakamoto T, Kobayashi S, Nakai K, Okano H, Watanabe H, Yoshida N, Torikai Y, Hatano Y, Takida T, Kato M, Ikegaya A, Ueda Y, Hatakeyama M, Shikama T (2014) Current status of nanostructured tungsten-based materials development. Phys Scr 159:014032. https://doi.org/10.1088/0031-8949/2014/T159/014032 View ArticleGoogle Scholar
  9. Ren C, Fang ZZ, Zhang H, Koopman M (2016) The study on low temperature sintering of nano-tungsten powders. Int J Refractory Metals Hard Mater 61:273–278. https://doi.org/10.1016/j.ijrmhm.2016.10.003 View ArticleGoogle Scholar
  10. Ryu T, Hwang KS, Choi YJ, Hong YS (2009) The sintering behavior of nanosized tungsten powder prepared by a plasma process. Int J Refractory Metals Hard Mater 27:701–704. https://doi.org/10.1016/j.ijrmhm.2008.11.004. View ArticleGoogle Scholar
  11. Wang J, Zeng Z, Weinberger CR, Zhang Z, Zhu T, Mao SX (2015) In situ atomic-scale observation of twinning-dominated deformation in nanoscale body-centred cubic tungsten. Nat Mater 14:594–600. https://doi.org/10.1038/nmat4228 View ArticleGoogle Scholar
  12. Zhang XS, Niu LL, Xu K, Hao JN, Zhang Y, Shu XL, Lu GH (2016) Atomistic simulations of nanoscale tungsten clusters: from structure and energetics to melting properties. Nucl Inst Methods Phys Res B. https://doi.org/10.1016/j.nimb.2016.09.009
  13. Wu ZM, Liang YX, Fu EG, Du JL, Wang PP (2018) The process and mechanisms for the transformation of coarse grain to nanoscale grain in tungsten by ball milling. Powder Technol 326:222–227. https://doi.org/10.1016/j.powtec.2017.11.059 View ArticleGoogle Scholar
  14. El-Atwani O, Quach DV, Efe M, Patrick C, Bryan H, Bradley S, Eric AS, Groza JR, Allain JP (2011) Multimodal grain size distribution and high hardness in fine grained tungsten fabricated by spark plasma sintering. Mater Sci Eng A 528:5670–5677. https://doi.org/10.1016/j.msea.2011.04.015 View ArticleGoogle Scholar
  15. Vilémová M, Nevrlá B, Pala Z, Kocmanová L, Janata M, Matějíček J, Tonarová D (2016) Properties of ultrafine-grained tungsten prepared by ball milling and spark plasma sintering. Appl Mechanics Mater 821:399–404. https://doi.org/10.4028/www.scientific.net/AMM.821.399 View ArticleGoogle Scholar
  16. Carné-Sánchez A, Imaz I, Canosarabia M, Maspoch D (2013) A spray-drying strategy for synthesis of nanoscale metal-organic frameworks and their assembly into hollow superstructures. Nat Chem 5:203–211. https://doi.org/10.1038/nchem.1569 View ArticleGoogle Scholar
  17. Vehring R (2008) Pharmaceutical particle engineering via spray drying. Pharm Res 25:999–1022. https://doi.org/10.1007/s11095-007-9475-1 View ArticleGoogle Scholar
  18. Cheow WS, Li S, Hadinoto K (2010) Spray drying formulation of hollow spherical aggregates of silica nanoparticles by experimental design. Chem Eng Res Design 88:673–685. https://doi.org/10.1016/j.cherd.2009.11.012 View ArticleGoogle Scholar
  19. Xu H, Tan Z, Abe H, Naito M (2011) Microcapsule assembly of single-walled carbon nanotubes from spray-dried hollow microspheres. J Ceramic Soc Jpn 119:180–184. https://doi.org/10.2109/jcersj2.119.180 View ArticleGoogle Scholar
  20. Luo P, Nieh TG (1995) Synthesis of ultrafine hydroxyapatite particles by a spray dry method. Mater Sci Eng C 3:75–78. https://doi.org/10.1016/0928-4931(95)00089-5 View ArticleGoogle Scholar
  21. Bi J, Yi W, Chen JL, Wen M, Guan W (2016) Synthesis of high-purity micro-spherical ruthenium particles by chemical refining method. Adv Powder Technol 27:53–56. https://doi.org/10.1016/j.apt.2015.11.001 View ArticleGoogle Scholar
  22. Zhao PC, Chen JL, Xin ZN, Yi W (2017) Synthesis and characterization of high-purity micro-spherical (NH4)2RuCl6 particles using chemical separation combined with spray dried techniques. Powder Technol 317:275–280. https://doi.org/10.1016/j.powtec.2017.04.040 View ArticleGoogle Scholar
  23. Guo L, Zhang YH, Yi W, Xin ZN, Li JG, Zhang JM, Zhao JC, Chen JL, Yao CSQ (2019) Synthesis and characterization of micro-spherical tungsten-molybdenum alloy particles using spray drying combined with microwave assisted calcination process. Int J Refractory Metals Hard Mater 78:45–50. https://doi.org/10.1016/j.ijrmhm.2018.08.004 View ArticleGoogle Scholar
  24. Fait MJG, Lunk HJ, Feist M, Schneidera M, Dannb JN, Friskb TA (2008) Thermal decomposition of ammonium paratungstate tetrahydrate under non-reducing conditions: characterization by thermal analysis, X-ray diffraction and spectroscopic methods. Thermochim Acta 469:12–22. https://doi.org/10.1016/j.tca.2007.12.007. View ArticleGoogle Scholar
  25. Huang H, Wu YQ, Wang SL, He YH, Zou J, Huang BY, Liu CT (2009) Mechanical properties of single crystal tungsten microwhiskers characterized by nanoindentation. Mater Sci Eng A. 523:193–198. https://doi.org/10.1016/j.msea.2009.05.060 View ArticleGoogle Scholar
  26. Greene GA, Finfrock CC (2000) Vaporization of tungsten in flowing steam at high temperatures. Particle Accelerators 25:87–99. https://doi.org/10.1016/S0894-1777(01)00063-2 View ArticleGoogle Scholar