Abstract
The Al-doped BiFeO3, i.e., BFAxO powder samples with x = 0, 0.025, 0.05, and 0.1, were prepared via the hydrothermal route. The effects of Al substitution on the structural, electrical, and optical properties of BFAxO samples were investigated. It is found that the substitution of Al ions at B-site of BiFeO3 did not cause structural change and it still retains the rhombohedral perovskite structure with R3c symmetry, which was confirmed by the X-ray diffraction (XRD) and Raman measurements. X-ray absorption fine structure (XAFS) above the Fe K-edge and Bi L3-edge in BFAxO powders was also measured and analyzed. Fe ions exhibit mixed valence states (Fe2+/Fe3+) while Bi ions keep the + 3 valence state in all the samples. Fe K-edge XAFS also indicated that there was a competition between hybridization of Fe 3d and Al 3d with O 2p orbitals and occurrence of the more 4p orbitals with Al doping. The Bi L3-edge XAFS revealed that transition from 2p3/2 to 6d state increased, so did the energy of 6d state. Besides, Al ion doping affected both the nearest-neighbor and next-nearest coordination shells of Fe atom and nearest-neighbor shells of Bi atom. Ultraviolet-visible (UV-Vis) spectroscopy results show the BFAxO prepared by hydrothermal method could be an appropriate visible-light photocatalytic material.
Background
Multiferroics are materials that simultaneously display ferroic properties, such as ferroelectricity, ferromagnetism, and ferroelasticity [1]. Such materials show interesting behaviors such as electrical polarization, which can be controlled with the application of an external electric field or vice-versa. Interest in these materials is owing to their wide applications in chemical biosensors, nanoelectronic and high-density data storage devices, etc [2, 3]. Perovskite structures have the general formula ABO3, where O is an ion (refers to oxygen usually) and A and B are cations, respectively. Generally, A-site cation is larger with a lower valence state, which combines with O2- to form a close-packed layer (i.e., at the corner of the unit cell). B-site cation is smaller with higher valence state, which can be adopted into an oxygen octahedral coordination environment (i.e., at the center of an octahedron of oxygen anions) [4]. By definition, almost all the multiferroics are antiferromagnetic (AFM) or weak ferromagnetic (FM) with low transition temperatures. They are divided into two classes: single phase and composite. However, the single-phase multiferroic materials are rarely found in nature which shows the ferroelectric (FE) and FM properties concurrently [5]. Among all the multiferroic materials known today, bismuth ferrite (BiFeO3; BFO) is one of the single-phase materials that have a rhombohedral distorted perovskite lattice type with polar space group R3c. BFO shows both FE with Curie temperature of TC ≈ 1103 k and G-type AFM ordering with Neel temperature of TN ≈ 643 k above room temperature (RT) [6]. This material exhibits the AFM G-type spin configuration along the [111]c or [001]h directions in its pseudo-cubic or rhombohedral structure and has a superimposed spiral spin structure with a periodicity of about 62 Å along the [110]h axis at RT [7]. It has a large intrinsic spontaneous polarization of about 90 μC/cm2 ascribed to the distortion of octahedral FeO6, owing to the presence of 6 s2 lone pair of electrons [8]. Furthermore, there is a magnetoelectric coupling between FE and magnetic order parameters. FE properties depend on the lone pair electrons, and FM properties rely on the partially filled inner shells, i.e., polarization comes from the Bi-site (A-site), while magnetization comes from the Fe-site (B-site).
Apart from above, unfortunately, the main disadvantages of BFO are its low resistivity or large leakage current, due to the charge defects such as bismuth and oxygen vacancies, impurity phases, valence fluctuations of iron, and poor interfacial quality [9]. In addition, it is difficult to obtain the high-quality BFO because of some impurity phases like Bi2Fe4O9 (space group Pbam) and Bi25FeO39 (space group I23). It is inevitable that the impurities are generated in the process of preparation. To address these issues and limitations, several research groups have been using various methods to overcome the defects of BFO, e.g., strain modification, substitution of divalent and rare earth ion doping. Now, within this field of study, with rare earth element or transition metal ion doping at A-site or B-site, or co-doping at A and B-site, the multiferroic properties of BFO can be enhanced. For instance, doping with rare earth element can stabilize the perovskite structure, retain the non-centrosymmetry, and control the vaporization of Bi3+ ions [10]. Doping with transition metal ion can reduce the valence fluctuation of Fe3+ ions. Elements like Pr, Sm, Eu, Gd, and La [11, 12] for A-site substitution and Mn, Cr, and Ti [13,14,15] for B-site substitution have already been reported. Moreover, the magnetic, dielectric, and ferroelectric properties can be enhanced with co-doping. For the co-doping of A- and B-sites of BFO, La-Gd, Ba-Ni, Dy-Cr, Y-Mn, and Tb-Ti have been reported [16,17,18,19,20]. Until now, various routes including sol-gel [21], mechanochemical [22], auto-combustion [23], pulsed laser deposition [24], and hydrothermal [25, 26] have been reported to prepare BFO. The hydrothermal method has been widely applied owing to its energy saving, fine dispersion, low cost, and small particle size properties [27]. The reaction temperature should be high enough to form BFO and also used to remove the secondary phases during sample preparation. Most previous studies of Al doped at both A- and B-site of BFO have been investigated for structural, optical, and transport properties by Azam et al [28]. Madhu et al. [29] have reported the photocatalytic applications of B-site Al-doped BFO. Another report from Jawad et al. [30] explored the dielectric behavior of nanostructured BFO ceramics. The work of Wang et al. [31] studied the hollow crystals of Al-doped BFO in detail. However, some important physical properties are still lack of understanding, such as B-site doping effects on the local electronic structure of the materials. At the present stage, X-ray absorption fine structure spectroscopy (XAFS) is one of the powerful ways to study the local environment of an atom and provides structural information of the materials, as well as absorption energy, element valence state, charge transfer, and type of bonding [32]. To the best of our knowledge, there are no found reports on the effect of Al doping at B-site on the local electronic structure of BFO investigation by XAFS.
In this work, the undoped BFO and target compositions BiFe1-xAlxO3 (BFAxO) with x = 0, 0.025, 0.05, and 0.1 were synthesized via hydrothermal route. The main focus is on the investigation of the effect of Al doping at B-site on the properties of BFO which are compared with undoped BFO. The structural properties were investigated in detail.
Methods
The hydrothermal method was used to obtain undoped BFO and BFAxO samples. Chemical reagents used in this work were bismuth nitrate (Bi(NO3)3·5H2O), iron nitrate (Fe(NO3)3·9H2O), aluminum nitrate (Al(NO3)3·6H2O), and potassium hydroxide (KOH). All chemical reagents were used as received without further purification. Bi(NO3)3·5H2O and Fe(NO3)3·9H2O were used as the source materials, while Al(NO3)3·6H2O and KOH were used as additives. Deionized water was used to make all aqueous solutions. A typical run for preparing BFO powders is as follows: The 20 mL each of Bi(NO3)3·5H2O, Fe(NO3)3·9H2O, and Al(NO3)3·6H2O were put into an 80-mL stainless steel autoclave and mixed well. After then, an appropriate amount of KOH solution was slowly dripped to the previous mixture solution until 65–80% of its volume was filled, which was next transferred into the strong magnetic stirring apparatus to stir for 2~3 h at 80 °C to get a clear solution. According to the method procedure, the obtained dark brown solution was transferred into Teflon-lined stainless steel autoclave. The hydrothermal treatment was carried out at a temperature of 200 °C for 10 h under autogenous pressure. The heating rate was 2 °C/min. After the hydrothermal reaction was complete, the resultant products were cooled down to RT naturally. Subsequently, the resultant powders were collected and washed several times with acetone, deionized water, and ethanol until the pH value of the solutions reached 7. Finally, the BFAxO powders were placed in a thermostat drying oven for 6 h at 70 °C, and then dried for further characterization. We have prepared four sets of samples of BFAxO by varying the concentration of Al(NO3)3·6H2O from 0–0.1 M.
The crystal structure of BFAxO samples was determined by X-ray diffraction (XRD, Mac Science M18XHF22-SRA). Raman spectroscopy (Renishaw InVia Reflex) with radiation from an Ar+ laser was employed to determine the structural properties of the powders at RT. XAFS data were collected in the transmission mode at various concentrations at the beamline 1W2B of the Beijing Synchrotron Radiation Facility (BSRF), China. Fe K-edge spectrum with an energy resolution of ΔE/E:2 × 10−4 and Bi L3-edge spectrum with an energy resolution of ΔE/E:1 × 10−4 were measured for the BFAxO samples at RT. In order to obtain best XAFS data, BFAxO powders were ground in an agate mortar, then mixed with BN and finally pressed into pellets. The background correction, normalization, and pre-edge and post-edge region of the absorption spectrum were fitted by ATHENA, a software for XAFS data processing, within the IFEFFIT program [33]. The Eo value was determined by the maximum in the first derivative in the edge region. We extracted the χ(k) profile in the k space of 0–12 Å−1. The k3 × χ(k) profile was Fourier transformed to the R space of 0–8 Å, by using the Hanning window function. The Fe2O3 and Bi2O3 were measured as the reference compounds. The optical properties of the powders were evaluated using ultraviolet-visible spectrophotometer (UV-Vis, UV 3900H). In this work, the investigation is limited to the low doping concentration of 0 ≤ x ≤ 0.1.
Results and Discussion
The XRD patterns of the undoped BFO (x = 0) and BFAxO powders, which scanned from 2θ value of 15–60°, are shown in Fig. 1. The full spectra of XRD patterns in Fig. 1a indicate that all samples can be identified as the standard diffraction data of the corresponding rhombohedral distorted perovskite structure (JCPDS Card File No. 20-0169, space group: R3c). It can also be seen that all samples exhibit neat diffraction patterns with a small amount of secondary phases. Traces of a secondary phase can be seen at 27.6° and 32.8° (marked “*” for Bi2Fe4O9 and “#”for Bi25FeO40) for x = 0.5 and x = 0.1 samples which may be resulting from the volatilization nature of Bi at the high sintering temperature [34]. This is often observed in the BFO powders synthesized by different routes [35,36,37]. Secondary phases are found to increase continuously at the high doping value. Therefore, B-site Al substitution for Fe cannot promote the pure phase of BFO; however, the electrical properties of samples would not be affected. From Fig. 1a, it can be seen that all diffraction peaks for the doped samples first shift to higher 2θ values with Al doping. For clarity, a part of XRD patterns in the 2θ region of 21 to 24° are amplified in Fig. 1b. From this enlarged view of the diffraction peaks, it can be observed that the (101) diffraction peak has an obvious shift toward high 2θ values with respect to undoped BFO, which confirms that Al is successfully doped into B-site of BFO. In analogy with undoped BFO, the (101) diffraction peak for the doped samples undergoes a shift in higher 2θ values first then small shift in lower 2θ values when x = 0.1 (surrounded by a dash line), as shown in Fig. 1c. Magnified XRD patterns in the vicinities of 37–40°, 50–52°, and 55–57° are given in Fig. 1d. There are some twin peaks, viz., (003) and (021), (113) and (211), (104) and (122), in the XRD spectrum. With the increase of Al content, the intensity of these peaks first increases then decreases when x reaches 0.1. As we know, the intensity of the peaks is usually related to the crystallinity. The decrease of the diffraction peaks indicates that the crystallinity of BFAxO decreases. Since Al3+ (0.51 Å) has a smaller ionic radius than Fe3+ (0.65 Å), it is easily incorporated into the BFO lattice when the doping amount is small, but excessive doping ion makes the BFO lattice unstable. The reduced crystallinity may be due to the fact that Al favors the creation of more nucleation sites which, in turn, inhibit the growth of crystal grains. Decreased crystallinity has also been found in other Al-doped BFO [28, 30]. On the other hand, this can occur if there is a creation of oxygen vacancies and transformation of some Fe3+ to Fe2+ due to the charge imbalance created in the system by Al3+ substitution. Similar phenomenon has been observed in Sr-doped BFO [38]. The shift in the diffraction peaks might be ascribed to the unit cell contraction, because of the small ionic radius of Al in comparison with Fe3+. The results of XRD show that the trivalent Al3+ substitution in BFO does not lead to observable structural transformation.
The structure confirmed by XRD can also be characterized by the position and intensity of Raman active modes. Raman spectrum is sensitive to the atomic displacement and distribution. The Raman scattering spectra of the undoped BFO and BFAxO powders are given in Fig. 2. On the basis of group theory, the 13 optical-phonon Raman active modes and 5 inactive modes (i.e., 5A2) of BFO are predicted for the rhombohedral distortion perovskites with space group R3c [39]. The theoretical analysis of the lattice vibrations in the perovskite R3c structure is as follows:
where A is longitudinal optical (LO) mode and E is the transverse optical mode (TO). In the full spectra shown in Fig. 2a, the number of clearly seen Raman active modes at RT is much less than predicted. In this work, we have observed six Raman active modes (3A1(LO) + 3E(TO)) for BFAxO powders. This may be due to the accidental degeneracies between bands in the spectra and the inability to distinguish weak bands from background noise [40], or dielectric leakage in the sample. For the undoped BFO, the strong and wide peaks at 68.7 cm−1, 127.3 cm−1, and 164.9 cm−1 were assigned to A1-1(LO), A1-2(LO), and A1-3(LO) modes, respectively. Peaks at 204.7 cm−1, 220.2 cm−1, and 251.8 cm−1 were assigned to E-1(TO), E-2(TO), and E-3(TO) modes, respectively (see Table 1 in Fig. 2). From the spectra, it can be clearly seen that these E(TO) modes are invisible. It is known that A1-1(LO) modes are attributed to the Bi-O bonds, while the tilt A1-3(LO) modes are viewed as the FeO6 octahedron. E(TO) modes are assigned to the Fe-O vibration [41]. The Raman result confirms that the prepared undoped BFO belongs to the rhombohedral distorted perovskite structure with space group R3c. It is noted that all four samples show similar Raman pattern and vibration modes. This indicated the same rhombohedral R3c space group, but their intensities and frequencies were somewhat different. At the whole view of Raman pattern of BFAxO samples, the peak position of the A1-1(LO) modes is slightly shifted to a higher frequency and the peaks of A1-3(LO) modes were broadened, indicating that the dopant Al is going to the B-site of BFO. The intensities of the E-1(TO), E-2(TO), and E-3(TO) modes are found to be slightly increased for the doped samples. For clarity, the A1-1(LO) and A1-3(LO) modes in the region of 50–100 cm−1 and 125–200 cm−1 are shown in Fig. 2b and c. From this enlarged spectrum, it is clear that A1-1(LO) modes exhibit a small shift to higher frequencies with increasing Al content. Compared to those of the undoped BFO, the peaks for A1-3(LO) modes were broadened for the doped samples. The small shift of the A1-1(LO) modes, slight broadening of A1-3(LO) modes, and change of the intensities of some E(TO) modes may be related to the change of the Bi-O and Fe-O covalent bonds and a compressive stress in the Al-doped sample [42, 36]. On the other hand, it is possible that all the above changes could be due to the fact that the B-site Fe3+ ions have been partially substituted by Al3+ ions. Apparently, these Raman results are consistent with the XRD observations. The Goldschmidt tolerance factor (t) is widely used to assess the geometric stability and distortion of crystal structures [43], where t is defined by the ratio of three kinds of ionic radii, as follows:
where rA is the radius of Bi3+, rB is the average radii of Fe3+ and Al, and rO is the radius of O2-. However, the radii of Al and Fe3+ are 0.51 Å and 0.65 Å, while the Bi3+ and O2- have the radii of 1.03 Å (according to Ref. [44]) and 1.38 Å, respectively. The t values for our studied perovskite composites BFAxO are found to be 0.839, 1.001, 1.001, and 1.003 for x = 0, 0.025, 0.05, and 0.1, respectively (see Table 1 in Fig. 2). The ideal ABO3 compounds adopt a cubic close-packed structure when the value of t is 1, while when t < 1 or > 1, a geometric strain arises [45, 46]. As the Al concentration increases, the average B-site ionic radius decreases, which leads to a further increase in the t value from 0.839 to 1.003. This may be due to the small change in a low symmetric state of BFO. It is well known that the B-site cation in perovskite is surrounded by six oxygen anions, and when replaced by smaller ions, the coordination distance will decrease. Hence, to clearly analyze the effects of the Al substitution, it is necessary to study the local electronic structure of the BFAxO samples.
XAFS is divided into two types, i.e., X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS). In this measurement, when the X-ray penetrates through the slab with distance x, the intensity of the X-ray beam will be reduced to I = Ioe-μx. XAFS measures the absorption of X-rays as a function of X-ray energy E, that is, the X-ray absorption coefficient μ(E) = − d ln I/dx is determined from the decay in the X-ray beam intensity I with distance x [47]. The ratio of I/Io is plotted as a function of E above the thresholds Fe K-edge (7112 eV) and Bi L3 (13,419 eV), which can provide important information about the shape of the μ(E). The electronic transitions shall be following the dipole selection rule. An X-ray absorbance μ(ω) can be obtained by Fermi’s golden rule, as follows:
where |i⟩ is the initial state, |f⟩ is the final state, D is the dipole operator, Ei is the energy of |i⟩, Ef is the energy of |f⟩, and ω is the photon frequency. The XANES features contain useful information that are associated with the electronic structure of the absorber and local environment of an atomic structure. XANES function χ(E) is defined as follows:
where μo(E) is the smooth atomic-like background and Δμo is a normalization factor that arises from the net increase in the total atomic background absorption edge. The standard Eq. (4) was used for the background subtraction and removal during the processing of XANES data. Firstly, a smooth pre-edge function is subtracted to remove the background from the instruments. Secondly, μ(E) is normalized and then a smooth post-edge background function is subtracted from the μ(E) to obtain the μo(E). Figure 3a shows the full spectra of the Fe K-edge XANES of an undoped BFO and BFAxO powders along with the reference compound Fe2O3 investigated in this work, while Fig. 3b reports the XANES spectrum in the energy range of 7100–7180 eV. From Fig. 3b, it can be seen that the shape of all spectra and peak positions is similar to each other. The absorption edges slightly shift toward lower energies with increasing Al concentration, which can be attributed to the chemical shift effect. The absorption edge energy shifts to lower energy with decreasing charge state, suggesting a complex bond configuration at the B-site. It is well known that edge shift could be used to obtain a mean oxidation state. The absorption edge energies for our studied samples BFAxO are found to be 7124.95 eV, 7123.87 eV, 7123.84 eV, and 7123.80 eV for x = 0, 0.025, 0.05, and 0.1, respectively. For the reference compound Fe2O3, the absorption edge energy is 7126.14 eV (see Table 2 in Fig. 3). The absorption edge of doped samples is lower than that of the Fe2O3 (Fe3+) reference compound. Increasing x values leads to the gradual shift of the absorption edge toward that of FeO (Fe2+) [48]. From this, we can note that BFAxO is a mixed-valent (Fe3+/Fe2+) system. In another aspect, three major features, pre-edge peak A1 and post-edge peaks A2 and A3, are observed in all four samples. The pre-edge peak A1, typical for BFO, corresponds to the electric quadrupole-forbidden transition from the O 1s level to Fe 3d ones, with a small admixture of Al 3d states. As the Al concentration increases, the intensity of the pre-edge peak A1 exhibits a small increase for the doped samples (see Fig. 3c). The post-edge peak A2 is attributed to the O 2p band transfer to the Fe 3d orbit, the so-called ligand-to-metal charge transfer process [49], whereas peak A3 is caused by the 1s to 4p dipole-allowed transition [50]. With increasing Al concentration, the intensity of these two post-edge peaks can be clearly seen to increase for the doped samples (see Fig. 3d). All the above changes in pre-edge and post-edge peak intensity can be understood in terms of competition between hybridization of Fe 3d and Al 3d with O 2p orbitals. Besides, after Al ion doping, there are more unoccupied 4p orbitals occurring in BFAxO. Except these, the whole spectra do not show significant changes and these results prove that Al ions are partially doped into B-site of BFAxO.
The Fe-O, Fe-Fe/Al (i.e., Fe-O-Fe/Al), and Bi-O bond distributions are obtained by fitting the k3-weighted (k3 × χ(k)) raw data, as follows:
where Eo is the absorption edge energy and ħ is the Planck constant. Further fitting (some approximations and oscillations) is made using the standard EXAFS equation, as follows:
where \( {S}_{\mathrm{o}}^2 \) (\( 0<{S}_{\mathrm{o}}^2<1 \)) is the reduction factor, NR is the number of backscattering atoms at distance R, f(k) is the backscattering amplitude, δc is the phase shift from central, ϕ is the backscattering atoms, λ is the core-hole lifetime, σ2 is the Debye-Waller factor from multiple distances, and k is the photoelectron mean free path. The EXAFS region is typically referred to the energy range of 20–30 eV above the edge jump, which is sensitive to short-range order types, bond distances, and coordination numbers in materials. Although, Eq. (6) could give some information about the EXAFS approximations and oscillations, it is not a particularly convenient form for visualizing the information content of an EXAFS spectrum. Therefore, Fourier transformation can be used to decompose a k space signal into its different constituent frequencies [32]. Fourier transformation is a complex function of interatomic distance R, the amplitude of which is represented by the real function of χ(R). In this function, the position of peaks is related to bond distances and neighboring ions. Equation (6) can be transformed from k space to R space by Fourier transform, as follows:
where kmax and kmin are the maximum and minimum values of transformed k space, respectively, χ(R) is the Hanning window function, ω(k) is the Gaussian window function, and kn is the weight factor (n = 0, 1, 2, 3). The k2 and k3 values for the BFAxO are 2 and 10, respectively, and the value of n is 2. Fourier transform of Fe K-edge EXAFS of the BFAxO samples is performed, as shown in Fig. 4a. The asymmetric peak (surrounded by the first dash line) centered at ~ 1.503 Å is identified as a Fe-O bond, owing to scattering from the oxygen anions. The second strong peak (surrounded by the second dash line) around ~ 3.527 Å is corresponding to the Fe-Fe/Al bonds, which can be explained by the scattering of oxygen anions from the next-to-nearest-neighboring Fe/Al atomic shells. The distance for the first and second coordination shells has been summarized in Table 3 in Fig. 4. From the peak position, compared with undoped BFO sample, Fe-O and Fe-Fe/Al bond tends to slightly shift toward smaller R values with increasing x. This indicates that doping by Al ions not only affects the nearest-neighbor local structure of central Fe atom but also affects the next-nearest coordination shells of the Fe atom. On the other hand, the shift of the Fe-O bond to smaller R values may result from that the radius of Al ions is smaller than that of Fe ions. This is consistent with the XRD data. The shift of Fe-Fe/Al to smaller R values also indicates that the average Fe-Fe/Al bond length (where the two Fe3+ ions are in the centers of neighboring oxygen octahedral) gradually becomes shorter and the bond angle is modified in the Al-doped samples. However, there is a small increase of peak intensity of the Fe-O distribution for the doped samples while the peak intensity of the Fe-Fe/Al distribution is almost not changed. This reveals that the iron-neighboring structure of Fe-O has been modified by Al doping. The shorter Fe-Fe/Al bonds in Al-doped samples can explain why the major peaks (101) in XRD shift to higher 2θ angles (see Fig. 1b). This indicates that the substitution of Al for Fe could affect oxygen octahedral, which further reduces the coordination distance between the two neighboring Fe atoms. Figure 4b shows the Fe K-edge EXAFS of the BFAxO samples processed on k3 × χ(k) oscillation with a k space of 0–10 Å−1. As can be seen, all the k3 × χ(k) spectra show similar patterns at the smaller k values but different at larger k values with some various noise (surrounded by the dash line). Al-doped samples show a broader k2× χ(k) spectrum than those of undoped BFO in the k space of 8.2–9.3 Å−1, implying an enhanced short-range structural disorder in BFAxO samples. The noises are observed in a k space of 10–10.4 Å−1. These changes indicated that the local structure of center atoms has changed due to B-site Al doping, similar to what was reported by Li et al. [51].
The peak positions, intensities, and shapes of the line in the Bi L3-edge XANES spectrum are well known to depend on the local electronic structure of the Bi atoms, which could provide information on the Bi valence. The full spectra of Bi L3-edge XANES of undoped BFO and BFAxO samples are also shown in Fig. 5a, while Fig. 5b shows the Bi L3-edge XANES spectrum in the energy region of 13,400–13,480 eV. The analysis of these spectra helps to investigate the local electronic structure of Bi ions in the doped system. From Fig. 5b, it can be seen that the shape of all spectra are the same to each other and there is almost no change of absorption edge in the whole series. The absorption edge energies for our study are found to be 13,429.1 eV, 13,429.4 eV, 13,429.3 eV, 13,429.3 eV, and 13,429.8 eV for x = 0, 0.025, 0.05, and 0.1 and the reference compound Bi2O3, respectively (see Table 4 in Fig. 5). The absorption edges slightly shift toward higher energies with increasing Al concentration. The absorption edge in the Bi L3-edge of the BFAxO samples matches well with that of the reference compound Bi2O3, which indicates that the valence state of Bi ions in all the samples is in + 3 valence state. However, there are two post-edge peaks found in all samples and marked as B1 and B2, respectively. These two post-edge peaks are caused by the electric-forbidden transition from 2p3/2 level to the 6d ones. Compared with undoped BFO, the intensity of peak B2 can be clearly seen to increase for the doped samples (see Fig. 5c), which means the transition from 2p3/2 to 6d state increases, so does the energy of 6d state. Except these, there is no other significant change in the whole spectrum.
Fourier transform of Bi L3-edge EXAFS radial distribution functions is performed, as shown in Fig. 6a. A high-intensity peak located at around 1.618 Å corresponds to the nearest Bi-O coordination shell (surrounded by the dash line), which is a result from scattering from the nearest-neighbor atomic shell of Bi, i.e., oxygen anions. However, the position of Bi-O bond shifts toward larger R values for the doped samples (see Table 5 in Fig. 6). This indicates that the substitution of Al for Fe could affect the nearest-neighbor local structure of the central Bi atom. It also indicates the extension of Bi-O bond length. The peak intensity of the Bi-O distribution exhibited a small increase with increasing Al content, which suggests that the iron-neighboring structure of Bi-O has changed. Figure 6b shows the Bi L3-edge k3 × χ(k) EXAFS spectra with a k space of 0–14 Å−1. From Fig. 6b, it can be seen that all the spectra shape shows similar patterns except some error noises. The error noises are observed in the k space of 12–14 Å−1 (surrounded by the dash line). This result may imply that the k3 × χ(k) EXAFS function of the center Bi atoms has changed with Al doping. This also suggests that the B-site Al substitution influences short-range structural disordering.
The optical properties of the samples are studied by using RT UV-Vis, which is used to characterize the optical properties of the materials. The UV-Vis absorption spectra of undoped BFO and BFAxO samples in the wavelength of 300–800 nm are shown in Fig. 7a. As a result, the UV-Vis spectra of the undoped BFO and BFAxO samples show two absorption edges (marked by dashed arrows). One is a band around 650 nm, which is due to the metal-to-metal transition. The other is a band around 760 nm, which is caused by crystal field transition [52]. In addition, the strong absorption band is observed at about 490 nm (marked by dashed arrow), which is attributed to the electronic transition from O 2p to Fe 3d state in the BFO. These strong bands indicate that the BFO prepared by hydrothermal method could be a promising visible-light photocatalytic material. BFO is of direct transition with a value of n as 2. The absorption edge of the doped samples shifted from 659 to 619 nm, suggesting that the BFAxO powders absorb visible light in the wavelength range of 600–659 nm (see Fig. 7a). A similar blue-shift phenomenon was observed earlier in other element-doped BFO [53,54,55]. This blue shift in the absorption spectra of Al-doped samples in comparison with the undoped BFO shows that doping Al causes a change in the local structure for BFO. From Fig. 7a, one can see that the absorption spectra of the Al-doped samples exhibit a sharp increase around 490 nm and it suggests that all samples can absorb remarkable amounts of visible light. For the sample with x = 0.025, the absorption spectrum shows a sudden increase. It means that it has a wider absorption range than the other samples in this range of visible light. The optical band gap of the samples has been calculated by Tauc’s formula, as follows:
where a is the absorption coefficient, A is the parameter, h is the Planck’s constant, m is the frequency of the incident photon, Eg is the optical band gap, and n (for direct n = 2, for indirect n = 0.5) is a constant associated with different types of electronic transitions, as shown in Fig. 7b. The calculated Eg values are found to be 1.833 eV, 1.888 eV, 1.866 eV, and 1.905 eV for x = 0, x = 0.025, x = 0.05, and x = 0.1 samples, respectively. It is easy to see that the band gap increases with the substitution ratio, as shown in Fig. 7c. The increase in the band gap is attributed to the doping effect. The Eg value for the undoped BFO is about 1.833 eV, which is lower than the previous reports [56, 57].
Conclusion
In summary, the BFAxO (x = 0, 0.025, 0.05, and 0.1) multiferroic powder samples were successfully synthesized via hydrothermal route. Effects of Al substitution on the structural, electrical, and optical properties of the samples were studied. The structural study reveals that Al-doped BiFeO3 shows the existence of secondary phases and lattice contraction due to lower ionic radii of Al doped into B-site, which still retains its rhombohedral R3c perovskite structure. Raman scattering measurement infers six Raman active phonon modes, which further confirms the result of XRD. XAFS studies on the Fe K-edge and B L3-edge of the BFAxO samples and of the reference compounds Fe2O3 and Bi2O3 were performed, and the obtained results were compared in order to determine the valance states of Fe and Bi ions in the system. The Fe K-edge XAFS results revealed that BFAxO is a mixed-valent (Fe3+/Fe2+) system. The results of Fe K-edge XAFS also illustrate a competition between the Fe 3d and Al 3d orbitals on hybridization with the O 2p and occurrence of the more 4p orbitals with Al doping. Besides, Al ion doping affects both the nearest-neighbor and next-nearest coordination shells of the Fe atom. The B L3-edge XAFS results indicate that valence states of Bi ions in all the samples are in + 3 and the transition from 2p3/2 to 6d state and the energy of 6d state increases. Substitution Al for Fe could affect the nearest-neighbor local structure of central Bi atom. The BFAxO prepared by hydrothermal method could be an appropriate visible-light photocatalytic material due to a strong absorption band in the visible region.
Abbreviations
- AFM:
-
Antiferromagnetic
- BFAxO:
-
BiFe1-xAlxO3
- BFO:
-
BiFeO3
- EXAFS:
-
X-ray absorption fine structure
- FE:
-
Ferroelectric
- FM:
-
Ferromagnetic
- RT:
-
Room temperature
- UV-Vis:
-
Ultraviolet-visible
- XAFS:
-
X-ray absorption fine structure
- XANES:
-
X-ray absorption near edge structure
- XRD:
-
X-ray diffraction
References
Wang J, Neaton JB, Zheng H, Nagarajan V, Ogale SB, Liu B, Viehland D, Vaithyanathan V, Schlom DG, Waghmare UV (2003) Epitaxial BiFeO3 multiferroic thin film heterostructures. Cheminform 299:1719–1722
Spaldin NA, Fiebig M (2005) The renaissance of magnetoelectric multiferroics. Science 309:391–392
Zhang X, Sui Y, Wang X, Wang Y, Wang Z (2010) Effect of Eu substitution on the crystal structure and multiferroic properties of BiFeO3. J Alloys Compd 507:157–161
Song SH, Zhu QS, Weng LQ, Mudinepalli VR (2015) A comparative study of dielectric, ferroelectric and magnetic properties of BiFeO3 multiferroic ceramics synthesized by conventional and spark plasma sintering techniques. J Eur Ceram Soc 35:131–138
Miah MJ, Khan MNI, Hossain AKMA (2015) Synthesis and enhancement of multiferroic properties of (x)Ba0.95Sr0.05TiO3-(1-x)BiFe0.90Dy0.10O3 ceramics. J Magn Mater 397:39–50
Jia DC, Xu JH, Ke H, Wang W, Zhou Y (2009) Structure and multiferroic properties of BiFeO3 powders. J Eur Ceram Soc 29:3099–3103
Yan F, Lai MO, Lu L, Zhu TJ (2010) Enhanced multiferroic properties and valence effect of Ru-doped BiFeO3 thin films. J Phys Chem C 114:6994–6998
Yan F, Zhu TJ, Lai MO, Lu L (2010) Enhanced multiferroic properties and domain structure of La-doped BiFeO3 thin films. Scripta Mater 63:780–783
Catalan G, Scott JF (2009) Physics and applications of bismuth ferrite. Adv Mater 21:2463–2485
Yan X, Tan G, Liu W, Ren H, Xia A (2015) Structural, electric and magnetic properties of Dy and Mn co-doped BiFeO3 thin films. Ceram Int 41:3202–3207
Iorgu AI, Maxim F, Matei C, Ferreira LP, Ferreira P, Cruz MM, Berger D (2015) Fast synthesis of rare-earth (Pr3+ , Sm3+ , Eu3+ and Gd3+) doped bismuth ferrite powders with enhanced magnetic properties. J Alloys Compd 629:62
Cotica LF, Estrada FR, Freitas VF, Dias GS (2012) Ferroic states in La doped BiFeO3-PbTiO3 multiferroic compounds. J Appl Phy 111:114105
Cen Z, Zhou C, Yang H, Zhou Q, Li W, Yuan C (2013) Structural, ferroelectric and piezoelectric properties of Mn-modified BiFeO3-BaTiO3 high-temperature ceramics. J Mater Sci-Mater El 24:3952–3957
Juan PC, Wang JL, Hsieh TY, Lin CL, Yang CM, Shye DC (2015) The physical and electrical characterizations of Cr-doped BiFeO3 ferroelectric thin films for nonvolatile memory applications. Microelectron Eng 138:86–90
Reetu A, Agarwal S, Sanghi A (2011) Rietveld analysis, dielectric and magnetic properties of Sr and Ti codoped BiFeO3 multiferroic. J Appl Phy 110:073909
Suresh P, Babu PD, Srinath S (2016) Role of (La, Gd) co-doping on the enhanced dielectric and magnetic properties of BiFeO3 ceramics. Ceram Int 42:4176–4184
Rojas-George G, Concha-Balderrama A, Esparza-Ponce H, Silva J, Galindo JTE, Cruz MP, Gervacio JJ, Graeve OA, Herrera G, Fuentes L, Reyes-Rojas A (2016) Local polarization switching in Ba-Ni co-doped BiFeO3 thin films with low rhombohedral-symmetry distortion. J Mater Sci 51:2283–2291
Mao WW, Wang XF, Chu L, Zhu YY, Wang Q, Zhang J, Yang JP, Li XA, Huang W (2016) Simultaneous enhancement of magnetic and ferroelectric properties in Dy and Cr co-doped BiFeO3 nanoparticles. Phys Chem Chem Phys 18:6399–6405
Tang P, Kuang DH, Yang SH, Zhang YL (2016) The structural and magnetic properties of Bi1-xYxFe1-yMnyO3 particles synthesized via a sol-gel technique. Ferroelectrics 491:104–111
Sharma S, Shandilya M, Rai R (2015) Effect of Tb, Ti co-doping on the electrical and magnetic properties of (Bi, La)FeO3 multiferroic ceramics. J Mater Sci-Mater El 26:9484–9494
Zhu Y, Quan C, Ma Y, Wang Q, Mao W, Wang X, Zhang J, Min Y, Yang J, Li Xa, Huang W (2017) Effect of Eu, Mn co-doping on structural, optical and magnetic properties of BiFeO3 nanoparticles. Mat Sci Semicon Proc 57:178–184
Bernardo MS, Jardiel T, Peiteado M, Caballero AC (2016) Metastable nature of donor-doped BiFeO3 obtained by mechanochemical synthesis. J Ceram Soc Jpn 124:92–97
Stojadinović B, Dohčević-Mitrović Z, Paunović N, Ilić N, Tasić N, Petronijević I, Popović D, Stojanović B (2016) Comparative study of structural and electrical properties of Pr and Ce doped BiFeO3 ceramics synthesized by auto-combustion method. J Alloys Comp 657:866–872
Ramesh R, Al E et al (2003) Epitaxial BiFeO3 multiferroic thin film heterostructures. Sci 299:1719–1722
Zhang N, Wei Q, Qin L, Chen D, Chen Z, Niu F, Wang J, Huang Y (2017) Crystal structure, magnetic and optical properties of Mn-doped BiFeO3 by hydrothermal synthesis. J Nanosci Nanotechno 17:544–549
Zhang H, Kajiyoshi K (2010) Hydrothermal synthesis and size-dependent properties of multiferroic bismuth ferrite crystallites. J Am Ceram Soc 93:3842–3849
Yoshimura M, Byrappa K (2008) Hydrothermal processing of materials: past, present and future. J Mater Sci 43:2085–2103
Azam A, Jawad A, Ahmed AS, Chaman M, Naqvi A (2011) Compounds, structural, optical and transport properties of Al3+ doped BiFeO3 nanopowder synthesized by solution combustion method. J Alloys Comp 509:2909–2913
Chennabasappa M, Bellakki M, Manivannan V (2010) Synthesis and characterization of doped BiFeO3 materials for photocatalytic applications. J Mater Eng 17:131–139
Jawad A, Ahmed AS, Ashraf SSZ, Chaman M, Azam A (2012) Exploring the dielectric behaviour of nano-structured Al3+ doped BiFeO3 ceramics synthesized by auto ignition process. J Alloys Comp 530:63–70
Wang YG, Yang LL, Wang YJ, Wang XF (2012) Hollow crystals of BiFeO3 prepared via a Al3+-assisted hydrothermal method. Appl Mechan Mater 174(177):516–519
Sayers DE, Stern EA, Lytle FW (1971) New technique for investigating noncrystalline structures: fourier analysis of the extended x-ray-absorption fine structure. Phys Rev Lett 27:1204–1207
Ravel B, Newville M (2005) ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J synchrotron radiat 12:537–541
Eerenstein W, Mathur ND, Scott JF (2006) Multiferroic and magnetoelectric materials. Nature 442:759–765
Maître A, François M, Gachon JC (2004) Experimental study of the Bi2O3-Fe2O3 pseudo-binary system. J Phase Equilib Diff 25:59–67
Zheng XH, Ma ZH, Chen PJ, Tang DP, Ma N (2012) Decomposition behavior and dielectric properties of Ti-doped BiFeO3 ceramics derived from molten salt method. J Mater Sci-Mater El 23:1533–1537
Rao TD, Karthik T, Srinivas A, Asthana S (2012) Study of structural, magnetic and electrical properties on Ho-substituted BiFeO3. Solid State Commun 152:2071–2077
Thakur S, Pandey OP, Singh KJCI (2014) Role of Sr2+ substitution on structural, thermal and conducting behavior of Bi1-xSrxFeO3 (0.40≤x≤0.55). Ceram Int 40:16371–16379
Singh MK, Jang HM, Ryu S, Jo MH (2006) Polarized raman scattering of multiferroic BiFeO3 epitaxial films with rhombohedral R3c symmetry. Appl Phys Lett 88:042907
Matson DW, Sharma SK, Philpotts JA (1983) The structure of high-silica alkali-silicate glasses. A Raman spectroscopic investigation. J Non-Cryst Solids 58:323–352
Chang LY, Tu CS, Chen PY, Chen CS, Schmidt VH, Wei HH, Huang DJ, Chan TS (2015) Raman vibrations and photovoltaic conversion in rare earth doped (Bi0.93RE0.07)FeO3 (RE=Dy, Gd, Eu, Sm) ceramics. Ceram Int 42:834–842
Singh MK, Ryu S, Jang HM (2005) Polarized raman scattering of multiferroic bifeo3 thin films with pseudo-tetragonal symmetry. Phys Rev B 72:2101
Goldschmidt VM (1926) Die Gesetze der Krystallochemie. Naturwissenschaften 14:477–485
Liu W, Tan G, Xue X, Dong G, Ren H, Xia A (2014) Phase transition and enhanced multiferroic properties of (Sm, Mn and Cr) co-doped BiFeO3 thin films. Ceram Int 40:12179–12185
Triana CA, Corredor LT, Téllez DAL, Roa-Rojas J (2011) High temperature-induced phase transitions in Sr2GdRuO6 complex perovskite. Mater Res Bull 46:2478–2483
Sato T, Takagi S, Deledda S, Hauback BC, Orimo S (2016) Extending the applicability of the Goldschmidt tolerance factor to arbitrary ionic compounds. Sci Rep 6:23592
Rehr JJ, Albers RC (2000) Theoretical approaches to x-ray absorption fine structure. Rev Mod Phys 72:621–654
Saxena P, Dar MA, Sharma P, Kumar A, Varshney D (2016) Structural, dielectric and ferroelectric properties of La and Ni codoped BiFeO3. J Appl Phys 1728:020307
Lee D, Kim MG, Ryu S, Jang HM, Lee SG (2005) Epitaxially grown La-modified BiFeO3 magnetoferroelectric thin films. Appl Phys Lett 86:222903
Westre TE, Kennepohl P, DeWitt JG, Hedman B, Hodgson KO, Solomon EI (1997) A multiplet analysis of Fe K-edge 1s→3d pre-edge features of iron complexes. J Am Chem Soc 119:6297–6314
Gong L, Zhou Z, Wang S, Wang B (2013) Preparation and characterization of BiFeO3@Ce-doped TiO2 core-shell structured nanocomposites. Mater Sci Semicon Proc 16:288–294
Xiao YG, Zhong WQ, Deng ZY, Yan FS, Jin L (2015) Investigation on structural and functional properties of Nd doped BiFeO3 particles prepared by hydrothermal method. J Mater Sci-Mater El 26:1–7
Jian H, Guo R, Liang F, Wen D, Zheng F, Shen MJMRB (2013) Characterization and visible light photocatalytic mechanism of size-controlled BiFeO3 nanoparticles. Mater Res Bull 48:3017–3024
Quan C, Ma Y, Han Y, Tang X, Lu M, Mao W, Jian Z, Yang J, Li XA, Wei A (2015) Effect of Nd substitution for Ca on crystal structure, optical and magnetic properties of multiferroic Bi0.9Ca0.1FeO3. J Alloys Comp 635:272–277
Sharma S, Singh V, Kotnala RK, Dwivedi RKJJoMSMiE (2014) Comparative studies of pure BiFeO3 prepared by sol-gel versus conventional solid-state-reaction method. J Mater Sci-Mater El 25:1915–1921
Fu C, Sun F, Hao J, Gao R, Cai W, Chen G, Deng X (2016) The growth, enhanced optical and magnetic response of BiFeO3 nanorods synthesized by hydrothermal method. J Mater Sci-Mater El 27:8242–8246
Anshul A, Borkar H, Singh P, Pal P, Kushvaha SS, Kumar A (2014) Photoconductivity and photo-detection response of multiferroic bismuth iron oxide. Appl Phy Lett 104:132910
Acknowledgements
The authors also owe great thanks to the beamline 1W2B-XAFS of Beijing Synchrotron Radiation Facility (BSRF) that provides the beam time.
Funding
This work is supported by the Fundamental Research Funds for Central Universities (Grant Nos. 20720160020 and 20720160013).
Availability of Data and Materials
The datasets are available from the authors on reasonable request.
Author information
Authors and Affiliations
Contributions
The work presented here was performed in collaboration of all the authors. TG carried out most of the measurement and analysis as well as writing the draft of the manuscript. LRZ, JOW, HJQ, and RW contributed to the synchrotron experiments. HQW provided the leading insights and revised the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interest.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Gholam, T., Zheng, L.R., Wang, J.O. et al. Synchrotron X-ray Absorption Spectroscopy Study of Local Structure in Al-Doped BiFeO3 Powders. Nanoscale Res Lett 14, 137 (2019). https://doi.org/10.1186/s11671-019-2965-3