Introduction

Collecting solar energy for generating electricity, one of the promising methods of smart and sustainable development, has aroused many research interests. For this end, photocatalytic water splitting generates hydrogen and oxygen from water, which plays an increasingly important role as the clean energy [1]. In this aspect, low-cost and high-efficiency photocatalysts are the typical representatives, e.g., WO3 and TiO2 [2]. Many reports showed that the formation of semiconductor composites can effectively obtain novel active photocatalyst systems because of the improvement of charge carrier separation [3]. Graphene (GR), the thinnest and strongest material, has many extraordinary chemical and physical properties for its unique two-dimensional structure with honeycomb carbon lattice. Graphene complex oxide semiconductor material, e.g., WO3/GR, was reported as one of the best photocatalysts in high-efficiency photoelectrochemical water splitting for its resilience to photocorrosion effect and efficient electron transport behaviors [4, 5]. Thus, graphene complex oxide semiconductor hybrid nanocomposite has aroused great research interest for its huge potential in the past decade for various applications, e.g., NO2 sensor, electrochromic materials, supercapacitor, and photocatalyst [6,7,8,9,10,11,12].

Given the superior photocatalytic performance of the WO3/GR, numerous studies have been conducted to reveal the underlying mechanism that graphene improves WO3 characteristics associated with photo-generated charge transfer, and several well-established explanations have been made. For instance, Wu et al. considered that the graphene can serve as an electron–acceptor material and reduce the recombination of photo-excited electron–hole pairs, thereby increasing photoconversion efficiency [13]. Furthermore, WO3 nanorods can provide another possible electron route between WO3 and coupled rGO nanosheets, thereby exhibiting excellent visible-light catalytic activity for hydrogen production and clarifying the Z-scheme catalytic mechanism [14,15,16,17].

Besides, a few experiments were performed to explain the mechanisms of oxide semiconductor materials and graphene hybrid nanocomposite [18, 19]. Pang et al. used the oxygen-18 isotope labeling technique as a powerful tool to analyze the complicated photocatalytic mechanisms on the TiO2 surface [20]. Recently, several groups reported that light can be used to achieve the charge doping in graphene, which can improve the understanding and the use of graphene Schottky junctions for optoelectronics and electronics [21, 22]. Moreover, photo-induced doping originates from a light-absorbing material on graphene heterostructure interfaces, and it has recently exhibited unique device characteristics and physical effects. Photogenerated charges from light–matter interaction are transferred to graphene, thereby leading to electronic structure tailoring in graphene. It is noteworthy that this non-contact doping approach, easy to control, will ensure no additional defects [23].

In this study, the layered materials WO3/GR were deposited, of which the characteristics were investigated under the Raman spectroscopy, UV–vis spectroscopy and SEM. All the results show that p-graphene emerges and improves the characteristics of the WO3/GR film. The photocatalytic activities of the layered materials were assessed by the photocatalytic degradation of oxytetracycline antibiotics under UV light irradiation. The characteristics of cyclic voltammetry and electrochemical impedance spectra of the as-grown WO3/GR directly fabricated on Cu foils under UV light using electrochemical behavior were obtained here and compared with traditional WO3 catalysts. To explore the charge transfer mechanisms associated with photo-induced doping, the stacks of large area layered materials WO3/GR were designed on the Si substrate using a modified CVD approach, and WO3/GR and WO3 devices were developed by depositing an electrode material of gold foil for comparison. The characteristics of WO3/GR were analyzed and compared with those of WO3 due to photo-induced doping effects using the current–voltage test. Charge transport behaviors of p-graphene can be modified to improve photocatalytic ability. Furthermore, graphene was used as the photogenerated electron acceptor and effectively suppressed the charge recombination in the WO3/GR layered materials.

Experimental Section

Characterization of WO3/GR thin flake transistor: first, large-area graphene films of the order of centimeters were formed on copper substrates by chemical vapor deposition using methane. Graphene films were removed from the Cu foils to SiO2/Si substrate by etching in an aqueous solution of iron nitrate. The WO3 thin film was formed from 50 nm WO3 powder on a clean Si wafer with a 275-nm SiO2, graphene top layer [24]. During the deposition, argon was used as the protective gas. Subsequently, the electrodes (Cr/Au (5/50 nm)) were patterned with standard photolithography, electron beam metal deposition, and lift-off. For comparison, the pure WO3 device without graphene was prepared under the same conditions.

The band-gaps of the fabricated films were obtained by measuring absorbance using an UV–vis instrument (UV-2600, SHIMADZU Inc.). The morphology and microstructure of the nanostructured films were assessed with a JEOL JSM-7600F field emission scanning electron microscopy (FE-SEM). Raman measurements were performed in a Witec system in a backscattering configuration. The excitation was achieved by visible laser light (λ = 532 nm). All spectra were recorded at low power levels to avoid laser-induced modification or ablation of the samples.

Photocatalytic activity tests were performed under UV light. A defined amount of photocatalyst was suspended in 20 mL of antibiotic (oxytetracycline, 15 mg/L) solution in a typical activity test. The suspension was left in the dark for 1 h to reach the adsorption equilibrium, and the photocatalytic reaction was initiated under UV light for 160 min. The light source was a 250-W mercury lamp. By measuring the changes in the UV–vis absorption spectrum as a function of irradiation time, this study monitored antibiotic degradation.

Electrochemical Measurements

All the electrochemical measurements were performed in a three-electrode system for CHI 604E electrochemical workstation (CH Instruments), in which WO3/GR/Cu foil and WO3/Cu foil served as the working electrode, Pt foil as a counter electrode, and a saturated Ag/AgCl as a reference electrode. All the potentials were calibrated by a reversible hydrogen electrode (RHE). Linear sweep voltammetry with a scan rate of ~ 0.1 V s−1, from + 0.20 to − 0.20 V vs. RHE was performed in 0.5 M H2SO4. The Nyquist plots were obtained at the frequencies ranged from 100 kHz to 0.1 Hz at the overpotential of 40 mV. To extract the series and charge-transfer resistance, the impedance data fitted to a simplified Randles circuit.

Optoelectronic Measurement

All the electronic and optoelectronic characterization were performed in a probe station in a vacuum and at ambient temperature. The photocurrent was recorded by the Agilent 1500 A semiconductor analyzer. The light excitation was achieved by the 253 nm lamp used for the UV excitation.

Results and Discuss

The Characteristic of the WO3/GR Film

The deposition process of WO3/GR and WO3 films by CVD is shown in Fig. 1a. Figure 1b and c give SEM photographs of the as-deposited WO3/GR thin films. It is found that the WO3/GR thin film materials are uniform and smooth here. Moreover, from inspection, small crack gaps about 100 nm in size were found on the surface of WO3/GR. Figure 1d, e, and f show the elemental mapping of C, O, and W on the WO3/GR surface. Obviously, both W and O are uniformly distributed over the surface with a higher percentage. Since graphene is grown below WO3, element C can be found at the position of crack gaps with a low percentage [25].

Fig. 1
figure 1

Schematic of the synthesis and the SEM morphologies of the WO3/GR heterostructures. a The 50 nm WO3 powder is positioned in the same ceramic boat at the inlet side of the tube furnace. b × 60,000 and c × 5000 SEM images. d C e O f WEDS elemental mapping of WO3/GR

Figure 2a shows a selected region of the Raman spectra of the WO3/GR, as well as pure WO3. In general, monolayer graphene has two peaks at nearly 1348 cm−1 and 1586 cm−1, suggesting that the intensity ratio of IG/ID peak is about 2 of a Raman spectrum. Similar peaks at D-band (round 1370 cm−1) and G-band (round 1599 cm−1) were observed in the WO3/GR composite. According to the spectra in Fig. 2a, the IG/ID ratio decreased from 2 for the graphene to 1.2 for the WO3/GR composite. Thus, the smaller the IG/ID peak intensity ratio of a Raman spectrum, the higher the defects and disorders of the graphitized structures will be in the WO3/GR composite due to the high temperature of nearly 400 °C. Due to the stretching mode O–W–O in the sample of WO3/GR composite, Raman vibrations centered at 815 cm− 1, the characteristic of pure WO3 was detected, which was constantly narrowed in the sample of WO3/GR composite. It is noteworthy that the G-band of WO3/GR had risen from 1584 to 1599 cm−1 compared with graphene. This G-band up-shift was the general evidence of chemical doping of carbon materials. The trend here is consistent with previous studies with the p-type doping of the graphene, leading to upshift of the G-band. According to the Raman G-band shift, charge transfer between the graphene and the WO3 in the WO3/GR composite was demonstrated [26, 27]. The 2D peak shifted to longer wavelengths, which also verifies that the graphene was effectively p-doped. The 2D band located at 2691 cm−1 for pristine (undoped) graphene and round at 2700 cm−1 for p-doped graphene, respectively [28].

Fig. 2
figure 2

a The Raman spectra of as-prepared samples. b Raman G-peak mapping image of as-prepared samples. c UV–vis absorption spectra of as-prepared samples. d Determination the energy gap of samples

The Raman data of WO3/GR composite were extracted into intensity mapping, and Fig. 2b shows the Raman G peak mapping image of the WO3/GR composites obtained from the G-band of the graphene. The “bright” regions with high intensity illustrate the presence of the graphene, and it can be confirmed that p-doped graphene and defects exist in the layered materials due to the local high bright regions. Also, the “dark” regions are related to the WO3 information, which present the large area distribution of the graphene in the layered materials [29].

UV–vis spectra were treated as a key method to obtain the light absorption properties of photocatalysts. To analyze the interaction of graphene and WO3, UV–vis absorption spectra were recorded as shown in Fig. 2c. The equation αhʋ = A × (hν-Eg)n/2 was used, where α, ν, Eg, and A are the absorption coefficient, the light frequency, the band gap, and a constant, respectively [30]. The (αhν)1/2-hν curves of as-prepared samples are shown in Fig. 2d. According to the results, the light absorption of WO3/GR in the visible light region was more sensitive than that of pure WO3. The mixture of graphene onto the WO3 improved the absorption capacity to the light. Compared with pure WO3, the band gap of WO3/GR was narrowed from 3.88 to 3.68 eV (Fig. 2d). According to the redshift and enhancement of light absorption, WO3/GR exhibits the improved activity to separate electrons and holes.

The Degradation of Antibiotics Oxytetracycline

The detailed roles connected with doped graphene in oxide semiconductor photocatalysts appear to be complicated so that more work in fundamental researches is developed following this direction. The photocatalytic abilities of graphene-based photocatalysts can be improved by strengthening both electronic conductivity and carrier mobility. The conductive graphene can receive the photo-excited electrons as reservoirs when coupling graphene and the semiconductors. Accordingly, the concentration of photo-excited electrons decreased in semiconductor, thereby significantly suppressing their reductive corrosions [31]. Photocatalytic activity and reaction kinetics of WO3/GR, WO3 were observed during the degradation of antibiotics oxytetracycline using UV light (365 nm) as shown in Fig. 3. The photocatalytic activity of composite with photocatalyst and without photocatalyst was determined here in UV light for the comparison. After a specific time interval under UV light, the peak intensity of oxytetracycline associated with the UV–vis absorption characteristics of oxytetracycline molecule at 275 nm gradually decreased after 160 min as shown in Fig. 3a and b. Compared with WO3, WO3/GR led to a high degradation of oxytetracycline. The kinetics of oxytetracycline degradation under UV light can be obtained by pseudo-first-order reaction, where C0 and C are initial and concentration at given degradation time t and k is the rate constant, respectively. The diagram of ln(C/C0) was plotted as a function of t (Fig. 3c).

$$ \mathrm{In}\left(\mathrm{C}/{\mathrm{C}}_0\right)= kt $$
Fig. 3
figure 3

a UV–vis spectra of the degradation of antibiotics in the presence of WO3 composites. b UV–vis spectra of the degradation of antibiotics in the presence of WO3/GR composites. c Kinetics of as prepared WO3 and WO3/GR

The graph for WO3/GR, WO3 fitted linearly, where the correlation coefficient of R2 and the value of rate constant k (kempty =  − 0.0034 min−1, \( {k}_{{\mathrm{WO}}_3}=-0.0045\ {\min}^{-1} \), \( {k}_{{\mathrm{WO}}_3/\mathrm{GR}}=-0.0054\ {\min}^{-1} \)) show the higher catalytic activity of WO3/GR in comparison with WO3. It is because the formation of heterojunctions promotes the separation of electrons and holes. Holes can generate OH, which is considered the major reactive species for the oxidation reactions.

Electrochemical Behavior of the Layered Materials

Cyclic voltammetry is considered the method of analysis of the photoelectrocatalytic characteristics of WO3/GR/Cu and WO3/Cu electrodes for the reduction of hydrogen, as shown in Fig. 4a and b. Under the action of UV light, the current of the Cu electrode under ultraviolet light (8.5 mA) is larger than that in the dark (4 mA). The current of WO3/Cu electrode showed a slight difference between a dark condition and UV light. Moreover, WO3/GR/Cu electrode showed lower overpotential at − 0.08 V than WO3/Cu electrode at − 0.06 V. Reduction of hydrogen from the catalyst generated the response WO3 redox site. According to all the above results, it was clear that WO3/GR/Cu electrode was more efficient and showed the enhanced functional properties compared with that of WO3/Cu. This suggested that the presence of graphene under UV light led to the lower potential value and increased reduction currents under photo-induced doping effects which excited more electrons from WO3 to graphene.

Fig. 4
figure 4

Electrocatalytic application of CVD synthesized layered materials WO3/GR and WO3. a, b CV curves of as-grown WO3/GR, WO3 on Cu foil. c, d electrochemical impedance spectra of WO3/GR, WO3 flakes as well as the Cu foil substrate

The interfacial characteristics of the modified electrode, which were of huge significance to the electrical conductivity, and the electrocatalytic properties of the modified electrode were analyzed here by EIS. The electron-transfer kinetics and diffusion characteristics can be concluded from the shape of the electrochemical impedance spectrum. The semicircular portion, Ret, obtained at higher frequencies represents an electron transfer-limited process, and the linear portion at lower frequencies was attributed to the limited mass transfer of the as-prepared sample ion [32, 33]. Figure 4c and d show the results of EIS for electrodes of WO3/GR/Cu and WO3/Cu. WO3/GR/Cu electrode shows a better depressed semicircle arc compared with the WO3/Cu electrode, representing an excellent diffusion electron-transfer process on the WO3/GR/Cu electrode surface. Under UV light, WO3/Cu electrode still shows the lower depressed semicircle arc (Ret of 50(Z′/Ω)) compared with Ret (75(Z′/Ω)) in the dark. Note that under the UV light, WO3/GR/Cu electrode shows a relatively obvious semicircle arc (Ret = 42(Z′/Ω)), indicating a higher electron transfer resistance behavior than that of Ret (38(Z′/Ω)) in the dark. The increase in the value of electron transfer resistance (Ret) due to photo-induced doping effects improved Fermi energy level of graphene on electrode surface under UV light. These results also demonstrated that the graphene can improve the electron transfer rate between the electrode and WO3, which is consistent with the CV results.

The Charge Transfer Behaviors from WO3/GR Composite Device

Charge transfer behaviors in the WO3/GR layered materials can be surveyed under UV light, as shown in Fig. 5. The typical I–V and I–T characteristics of the device fabricated from WO3/GR composite and the reference device with pure WO3 were measured in the dark and under UV light at 253 nm with the intensity of 0.3 mW/cm2 as shown in Fig. 5a and b [34]. The photocurrent of the WO3/GR composite device was nearly 106 times higher than that of the reference device from pure WO3. Note that the photocurrent was less than the dark current of the WO3/GR composite, which is significantly different from the reference device from pure WO3. The typical I–V characteristics of the device were similar to I–T characteristics (Fig. 5c, d). The WO3/GR resistance R with optical illumination was larger than that in the dark due to photo-induced doping effect. The WO3/GR resistance R showed a constant value about thousands of ohms with optical excitation and dark conditions. However, the reference device, pure WO3 resistance still showed essential semiconductor features [35].

Fig. 5
figure 5

Experimental observation of characteristics in WO3/GR device compared with the pure WO3 device. a Photocurrent of WO3/GR. b Photocurrent of WO3. c Photoresistance of WO3/GR. d Photoresistance of WO3

Figure 6 shows the characteristics of WO3/GR after photo-induced modulation doping. Current route and charge distribution in the WO3/GR device under UV light are shown in Fig. 6a and b. Positive charges accumulated in WO3 under illumination. The higher current of the WO3/GR composite device should be attributed to the improved conductivity of the composite through GR. Graphene can create a Schottky contact at the interface with WO3, thereby forming resistance RWG [36]. The device can be modeled by the circuit as shown in Fig. 6c. Due to WO3 resistance RW>>(RWG + RG), the current of the device was decided by RWG + RG. Therefore, the conductivity properties had been significantly improved in the presence of graphene.

Fig. 6
figure 6

Characteristics of WO3/GR after photo-induced modulation doping. a, b Current route and charge distribution in the WO3/GR device in case of UV light. Positive charges accumulate in WO3 under light illumination. Yellow, Cr/ Au; green, WO3; red, graphene; blue, SiO2; gray, Si. c Equivalent circuit model of the WO3/GR device. d Schematics of the band structure of the WO3/GR heterostructure and illustration of the photodoping mechanism, in which optical excitation first excites electrons from defects in WO3. Red (blue) lines represent the conduction (valence) band. The excited electrons enter the graphene, and the positively charged defects lead to modulation doping in the graphene

Schematics of the band structure of the WO3/GR hybrid composites and diagram of the photo-induced doping mechanism are shown in Fig. 4d. The WO3/GR heterostructure device without light illumination is consistent with the previous result of a stable p-type doped graphene transistor, in which electrons were transferred from the graphene thin film to WO3. Initially, graphene was hole-doped in the dark, and an electric field appeared from graphene to silicon. As shown in Fig. 6d, when the device was under UV light, on the one hand, the electrons in the valence band (VB) of WO3 were excited to the conduction band to create electron–hole pairs [37,38,39]. On the other hand, electrons of donor-liked defects in WO3 were excited by photons to the conduction band. The ionized defects were positively charged and localized in the WO3. These excited electrons in both cases can be mobile, move towards, and then enter the graphene. It was suggested that significant photo-induced electron transfer occurred from WO3 to graphene at the WO3/GR device [40].

The excited electrons entered the graphene, and the positively charged defects led to modulation doping in the graphene. Under this modulation doping in the graphene, WO3/GR heterojunction emerged. Subsequently, the experimental data shows a decrease in conductivity with the increase in Fermi energy, EF of graphene, thereby leading to a slow decrease in the UV photocurrent. This is well consistent with the theoretical model [41]. It is therefore suggested that the transport behavior of the device will be utterly different from pure WO3 when the WO3/GR device is exposed to light. Photo-induced doping effects were also reported by some authors. Tiberj et al. reported that the charge carrier density of graphene can be finely and reversibly tuned between the hole and electron doping due to photo-induced doping, which was significantly affected by the substrate cleaning method [42]. Ju et al. showed photo-induced doping can maintain the high carrier mobility of the graphene/boron nitride heterostructure [43].

Under the light-induced doping effect, the surface of WO3/GR, as the primary photosensitive particles, has more photogenerated holes than the pure WO3 surface under UV light. The more active sites of the WO3/GR surface pores, the more efficient the improvement of photosensitivity [44]. In general, the conductive graphene, as an electron transport mediator, could extend the lifetime of photogenerated charge carriers significantly and strengthen charge extraction and separation. For instance, Weng et al. assembled the graphene−WO3 nanorod nanocomposites, which improved the visible-light photocatalytic performance compared with bare WO3 nanorods [45, 46]. Therefore, how to enhance the photodegradation process of photo-induced doping by doping graphene should be explored. It may be related to the intensity of UV light, dopant concentration, and so on [47, 48]. Chu et al. fabricated GR–WO3 composites mixed with different amounts of graphene (0, 0.1, 0.5, 1, and 3 wt%). Moreover, the sensor based on 0.1 wt% GR–WO3 composite exhibits good selectivity and high response in comparison with those of pure WO3 [49, 50]. It may be based on the reason that the excessive proportion of graphene absorbed on the surface of WO3, decreasing the amount of the active sites. Subsequently, the proper proportion of WO3 and graphene can gain the best experimental effect. Akhavan et al. also analyzed the characteristics of TiO2/GO (graphene oxides) sheets at different irradiation times [51]. They found the GO can be photocatalytically reduced, and the carbon defects increased under irradiation, which was considered to be partly because of photo-induced doping here [52]. Accordingly, this study develops a new route for exploring carrier transfer behaviors and photo-induced doping effects in graphene-based photodegradation materials.

Conclusion

In this study, the photocatalytic activities of the layered materials were assessed by the photocatalytic degradation of oxytetracycline antibiotics under UV light. A higher current of cyclic voltammetry and large resistance of impedance spectra with the as-grown WO3/GR directly synthesized on Cu foils under UV light through electrochemical behavior were obtained, which was also different from traditional WO3 catalysts. The characteristics of WO3/graphene layered materials were investigated under the Raman spectroscopy, UV–vis spectroscopy, and SEM. All results show that p-graphene emerges and enhances the characteristics of the WO3/GR film. The stacks of large-area WO3/GR layered materials were designed on the Si substrate using a modified CVD approach, and WO3/GR and WO3 films were fabricated on an electrode material of gold foil for comparison. Due to photo-induced doping effects, the current–voltage test suggested that the photo-resistance was larger than dark-resistance, and photocurrent was less than dark current based on WO3/GR layered materials, which were different from the characteristics of WO3 layered materials. Besides, charge transport behaviors of p-graphene could be modified to improve photocatalytic ability. Graphene serves as the photogenerated electrons acceptor and effectively suppresses the charge recombination in the WO3/GR layered materials. This study is considered a significant advance towards unraveling photocatalytic dynamics processes based on graphene and oxide semiconductor. Hopefully, these results can motivate scientists to explore high efficient catalysts for related applications.